PolyOne Geon™ Vinyl Rigid Extrusion L9620 Polyvinyl Chloride, Rigid (PVC, Rigid)
| Category | Polymer , Thermoplastic , Vinyl (PVC) , PVC, Rigid Grade |
| Manufacturer | PolyOne Corporation |
| Trade Name | Geon™ |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | PolyOne Geon™ Vinyl Rigid Extrusion L9620 Polyvinyl Chloride, Rigid (PVC, Rigid).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
The Cell Classification was determined using the notched Izod test with injection molded samples.Information provided by PolyOne
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.34 g/cc | 1.34 g/cc | ASTM D792 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore D | 80 | 80 | 15 sec; ASTM D2240 |
| Tensile Strength, Yield | 44.6 MPa | 6470 psi | Type I, 5.1 mm/min; ASTM D638 |
| Tensile Modulus | 2.56 GPa | 371 ksi | Type I, 5.1 mm/min; ASTM D638 |
| Flexural Strength | 74.6 MPa | 10800 psi | ASTM D790 |
| Flexural Modulus | 2.52 GPa | 365 ksi | ASTM D790 |
| Izod Impact, Notched | 8.10 J/cm @Thickness 3.18 mm, Temperature 23.0 °C |
15.2 ft-lb/in @Thickness 0.125 in, Temperature 73.4 °F |
Compression Molded, Across Flow; ASTM D256A |
| 9.80 J/cm @Thickness 3.18 mm, Temperature 23.0 °C |
18.4 ft-lb/in @Thickness 0.125 in, Temperature 73.4 °F |
Compression Molded, Flow; ASTM D256A | |
| 14.0 J/cm @Thickness 3.18 mm, Temperature 23.0 °C |
26.2 ft-lb/in @Thickness 0.125 in, Temperature 73.4 °F |
Injection Molded; ASTM D256A | |
| Dart Drop Total Energy | 60.1 J/cm @Temperature 23.0 °C |
0.113 ft-lb/mil @Temperature 73.4 °F |
Procedure A, C.125; ASTM D4226 |
| 173 J/cm @Temperature 23.0 °C |
0.324 ft-lb/mil @Temperature 73.4 °F |
Procedure B, C.125; ASTM D4226 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 74.0 µm/m-°C | 41.1 µin/in-°F | ASTM D696 |
| Deflection Temperature at 1.8 MPa (264 psi) | 72.8 °C @Thickness 3.18 mm |
163 °F @Thickness 0.125 in |
Unannealed; ASTM D648 |
| Flammability, UL94 | V-0 @Thickness 1.50 mm |
V-0 @Thickness 0.0591 in |
ALL; UL 94 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 182 - 193 °C | 360 - 379 °F |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Ease of Sizing | Acceptable | |
| Features | Good Surface Finish | |
| High Gloss | ||
| Forms | Pellets | |
| Generic Material | PVC, Rigid | |
| Generic Name | Polyvinyl Chloride, Rigid (PVC, Rigid) | |
| Processing Method | Extrusion | |
| PVC Cell Classification | 16344 | ASTM D1784 |
| Regional Availability | Africa & Middle East | |
| Asia Pacific | ||
| Europe | ||
| North America | ||
| South America | ||
| Uses | Edge Banding | |
| Profiles |
Users viewing this material also viewed the following:
- Total Finaprene® 411x Styrene-Butadiene TPE Copolymer Compounded to 58 Shore A (discontinued **)
- Lehmann & Voss LUVOCOM® 100-7126 VP Thermoplastic polyurethane, with PTFE
- Techmer ES HiFill® TPX-PBT-01022 25% Mineral Filled
- SABIC Innovative Plastics LNP Thermocomp PH0600A PA 6 (Asia Pacific)
- Styron CALIBREâ„¢ MEGARAD 2080 10 Polycarbonate, Gamma Radiation Resistant
- ELASTO UK Dryflex® 422501S SBS Based Material, 50D Hardness, Black
- Carpenter Custom 450® Stainless Steel, 25 mm Bar, Condition H1050 (Age Hardened 566°C)
- Alliance N-42 Neodymium Iron Boron Magnetic Material
- ACC MM913 Condensation Cure 2-Part Molding Rubber
Copyright © lookpolymers.com All Rights Reserved