- Sax Polymers SAXAMID 136F4Q32 Nylon 6, 20% Glass Fiber
Sax Polymers SAXAMID 136F4Q32 Nylon 6, 20% Glass Fiber
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, 20% Glass Fiber Filled , Nylon 6, Glass Filled, Impact Grade |
| Manufacturer | Sax Polymers |
| Trade Name | SAXAMID |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Sax Polymers SAXAMID 136F4Q32 Nylon 6, 20% Glass Fiber.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
SAXAMID 136F4Q32 is a high impact-modified polyamide 6 injection-molding-grade reinforced with 20% glass fibers.Information provided by SAX Polymers
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.19 g/cc | 0.0430 lb/in³ | ISO 1183 |
| Viscosity Test | 150 cm³/g | 150 cm³/g | H<sub>2</sub>SO<sub>4</sub>; ISO 307 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength | 80.0 MPa | 11600 psi | 5 mm/min; ISO 527-1 |
| Elongation at Break | 3.3 % | 3.3 % | 5 mm/min; ISO 527-1 |
| Tensile Modulus | 4.80 GPa | 696 ksi | 1 mm/min; ISO 527-1 |
| Flexural Strength | 132 MPa | 19100 psi | 2 mm/min; ISO 178 |
| Flexural Modulus | 3.70 GPa | 537 ksi | 2 mm/min; ISO 178 |
| Izod Impact, Notched (ISO) | 13.0 kJ/m² @Temperature -30.0 °C |
6.19 ft-lb/in² @Temperature -22.0 °F |
ISO 180/1A |
| 17.0 kJ/m² @Temperature 23.0 °C |
8.09 ft-lb/in² @Temperature 73.4 °F |
ISO 180/1A | |
| Izod Impact, Unnotched (ISO) | 78.0 kJ/m² @Temperature 23.0 °C |
37.1 ft-lb/in² @Temperature 73.4 °F |
ISO 180/1U |
| 79.0 kJ/m² @Temperature -30.0 °C |
37.6 ft-lb/in² @Temperature -22.0 °F |
ISO 180/1U | |
| Charpy Impact Unnotched | 7.50 J/cm² @Temperature 23.0 °C |
35.7 ft-lb/in² @Temperature 73.4 °F |
ISO 179/1eU |
| 7.60 J/cm² @Temperature -30.0 °C |
36.2 ft-lb/in² @Temperature -22.0 °F |
ISO 179/1eU | |
| Charpy Impact, Notched | 1.40 J/cm² @Temperature -30.0 °C |
6.66 ft-lb/in² @Temperature -22.0 °F |
ISO 179/1eA |
| 1.80 J/cm² @Temperature 23.0 °C |
8.57 ft-lb/in² @Temperature 73.4 °F |
ISO 179/1eA |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 178 °C | 352 °F | 80*10*4 s=60mm; ISO 75-1 a |
| Vicat Softening Point | 185 °C | 365 °F | B/120; ISO 306 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 260 - 290 °C | 500 - 554 °F | |
| Mold Temperature | 70.0 - 90.0 °C | 158 - 194 °F | |
| Drying Temperature | 80.0 °C @Time 7200 - 21600 sec |
176 °F @Time 2.00 - 6.00 hour |
|
| Moisture Content | <= 0.20 % | <= 0.20 % |
Users viewing this material also viewed the following:
- Polycasa Acryl® KR 2014/1 Acrylic, Impact Grade
- Parker Chomerics Tecknit Consil®-E 811 Extruded Silver-Filled Silicone Elastomer
- Michelman® Hydrosize® U2-01 Nonionic polyurethane emulsion
- Haynes 242® alloy, cold reduced sheet, annealed and 40% cold work
- Samyang Trirex® 3020IR Polycarbonate with Heat Stabilizer
- Plenco 6990 Phenolic, Briquette, Transfer Molded
- A. Schulman POLYFORT™ FPP 3716 Talc Filled Copolymer Polypropylene
- Ensinger Tecapeek® XP-181 Compression Molded PPEK Compound, EWS Filled and Carbon Fiber Reinforced
- CLAL-MSX DECLAFOR® 1015 TDX Wire quenched/Cold Rolled Copper Alloy
- Ascend Performance Materials VYDYNE® R400G Nylon, Mineral and Glass Reinforced
Copyright © lookpolymers.com All Rights Reserved