SABIC Innovative Plastics Xenoy® X5630 PC+PET (Asia Pacific)
| Category | Polymer , Thermoplastic , ABS Polymer , Polycarbonate/ABS Alloy, Unreinforced , Polycarbonate (PC) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | Xenoy® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics Xenoy® X5630 PC+PET (Asia Pacific).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Mineral filled PC/PET blend with high heat dimensional stability, low shrinkage and low CTE, especially for painted applications
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.35 g/cc | 1.35 g/cc | ASTM D792 |
| Density | 1.35 g/cc | 0.0488 lb/in³ | ISO 1183 |
| Moisture Absorption | 0.140 % | 0.140 % | 23°C / 50% RH; ISO 62 |
| Water Absorption at Saturation | 0.42 % | 0.42 % | ISO 62 |
| Linear Mold Shrinkage, Flow | 0.0050 - 0.0060 cm/cm @Thickness 3.20 mm |
0.0050 - 0.0060 in/in @Thickness 0.126 in |
SABIC Method |
| Melt Flow | 11 g/10 min @Load 5.00 kg, Temperature 266 °C |
11 g/10 min @Load 11.0 lb, Temperature 511 °F |
ASTM D1238 |
| Melt Index of Compound | 10 g/10 min @Load 5.00 kg, Temperature 265 °C |
10 g/10 min @Load 11.0 lb, Temperature 509 °F |
MVR [cm^3/10 min]; ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 50.0 MPa | 7250 psi | Type I, 5 mm/min; ASTM D638 |
| 50.0 MPa | 7250 psi | 5 mm/min; ISO 527 | |
| Tensile Strength, Yield | 55.0 MPa | 7980 psi | Type I, 5 mm/min; ASTM D638 |
| 56.0 MPa | 8120 psi | 5 mm/min; ISO 527 | |
| Elongation at Break | 8.0 % | 8.0 % | 5 mm/min; ISO 527 |
| 10 % | 10 % | Type I, 5 mm/min; ASTM D638 | |
| Elongation at Yield | 3.2 % | 3.2 % | Type I, 5 mm/min; ASTM D638 |
| 3.2 % | 3.2 % | 5 mm/min; ISO 527 | |
| Tensile Modulus | 4.30 GPa | 624 ksi | 1 mm/min; ISO 527 |
| 4.40 GPa | 638 ksi | 5 mm/min; ASTM D638 | |
| Flexural Yield Strength | 90.0 MPa | 13100 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| 90.0 MPa | 13100 psi | 2 mm/min; ISO 178 | |
| Flexural Modulus | 4.20 GPa | 609 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
| 4.20 GPa | 609 ksi | 2 mm/min; ISO 178 | |
| Izod Impact, Notched | 0.800 J/cm | 1.50 ft-lb/in | ASTM D256 |
| 0.600 J/cm @Temperature -30.0 °C |
1.12 ft-lb/in @Temperature -22.0 °F |
ASTM D256 | |
| Izod Impact, Notched (ISO) | 8.00 kJ/m² | 3.81 ft-lb/in² | 80*10*4; ISO 180/1A |
| 6.00 kJ/m² @Temperature -30.0 °C |
2.86 ft-lb/in² @Temperature -22.0 °F |
80*10*4; ISO 180/1A | |
| Izod Impact, Unnotched (ISO) | 100 kJ/m² | 47.6 ft-lb/in² | 80*10*4; ISO 180/1U |
| 80.0 kJ/m² @Temperature -30.0 °C |
38.1 ft-lb/in² @Temperature -22.0 °F |
80*10*4; ISO 180/1U | |
| Charpy Impact, Notched | 0.600 J/cm² | 2.86 ft-lb/in² | Edgew 80*10*4 sp=62mm; ISO 179/1eA |
| Dart Drop, Total Energy | 45.0 J @Temperature 23.0 °C |
33.2 ft-lb @Temperature 73.4 °F |
ASTM D3763 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 43.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
23.9 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| 48.0 µm/m-°C @Temperature -30.0 - 80.0 °C |
26.7 µin/in-°F @Temperature -22.0 - 176 °F |
ISO 11359-2 | |
| 48.0 µm/m-°C @Temperature 23.0 - 80.0 °C |
26.7 µin/in-°F @Temperature 73.4 - 176 °F |
ISO 11359-2 | |
| CTE, linear, Transverse to Flow | 64.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
35.6 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| 68.0 µm/m-°C @Temperature -30.0 - 80.0 °C |
37.8 µin/in-°F @Temperature -22.0 - 176 °F |
ISO 11359-2 | |
| 68.0 µm/m-°C @Temperature 23.0 - 80.0 °C |
37.8 µin/in-°F @Temperature 73.4 - 176 °F |
ISO 11359-2 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 112 °C | 234 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 112 °C @Thickness 3.20 mm |
234 °F @Thickness 0.126 in |
unannealed; ASTM D648 | |
| Vicat Softening Point | 138 °C | 280 °F | Rate B/50; ASTM D1525 |
| 138 °C | 280 °F | Rate B/50; ISO 306 | |
| 140 °C | 284 °F | Rate B/120; ISO 306 |
Users viewing this material also viewed the following:
- Omya PULPROWHITE® 8 - SA Calcium Carbonate
- Radici Raditer® BRV300 Polybutylene Terephthalate
- LTL Color Compounds ColorFast® PCT2018 PC/PBT Alloy
- Solvay TECHNYL® A 218 V35 Black 21NHFE PA66, 35% glass fiber, Conditioned
- Saint-Gobain Chemfab® 2 Porous PTFE-Coated Glass
- SK Chemicals SKYTHANE® X585A Polyester Based Thermoplastic Polyurethane Elastomer
- Wico Plast Wicotal 500 Acetal
- CIMBAR Suspengel™ 16 High Purity Bentonite, Industrial Grade
- Ravago Manufacturing Americas Hylex® P1010G15 HB Polycarbonate, 15% Fiberglass Reinforced
- Saint-Gobain CHR® M54 Polyester Film Backing Natural Rubber Adhesive Pressure Sensitive Tape
Copyright © lookpolymers.com All Rights Reserved