SABIC Innovative Plastics XYLEX X7300 PC+POLYESTER (Asia Pacific)

Category Polymer , Thermoplastic , Polycarbonate (PC) , Polycarbonate/PET Polyester Blend , Polyester, TP , Polyethylene Terephthalate (PET)
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name Xylex
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics XYLEX X7300 PC+POLYESTER (Asia Pacific).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
PC+POLYESTER unreinforced alloy. High flow, chemically resistant with excellent optical quality. UV-stabilized.
Physical Properties Metric English Comments
Specific Gravity 1.20 g/cc
1.20 g/cc
ASTM D792
Density 1.18 g/cc
0.0426 lb/in³
ISO 1183
Linear Mold Shrinkage, Flow 0.0040 - 0.0080 cm/cm

@Thickness 3.20 mm
 0.0040 - 0.0080 in/in

@Thickness 0.126 in
 SABIC Method
Linear Mold Shrinkage, Transverse 0.0050 - 0.0070 cm/cm

@Thickness 3.20 mm
 0.0050 - 0.0070 in/in

@Thickness 0.126 in
 SABIC Method
Melt Flow 21 g/10 min

@Load 2.16 kg,
Temperature 265 °C
 21 g/10 min

@Load 4.76 lb,
Temperature 509 °F
 ASTM D1238
Melt Index of Compound 21 g/10 min

@Load 2.16 kg,
Temperature 265 °C
 21 g/10 min

@Load 4.76 lb,
Temperature 509 °F
 MVR [cm^3/10 min]; ISO 1133
Mechanical Properties Metric English Comments
Tensile Strength at Break 52.0 MPa
7540 psi
Type I, 50 mm/min; ASTM D638
55.0 MPa
7980 psi
50 mm/min; ISO 527
Tensile Strength, Yield 49.0 MPa
7110 psi
Type I, 50 mm/min; ASTM D638
55.0 MPa
7980 psi
50 mm/min; ISO 527
Elongation at Break 150 %
150 %
Type I, 50 mm/min; ASTM D638
>= 150 %
>= 150 %
50 mm/min; ISO 527
Elongation at Yield 5.0 %
5.0 %
Type I, 50 mm/min; ASTM D638
5.0 %
5.0 %
50 mm/min; ISO 527
Tensile Modulus 1.84 GPa
267 ksi
50 mm/min; ASTM D638
1.90 GPa
276 ksi
1 mm/min; ISO 527
Flexural Strength 71.0 MPa
10300 psi
2 mm/min; ISO 178
Flexural Yield Strength 83.0 MPa
12000 psi
1.3 mm/min, 50 mm span; ASTM D790
Flexural Modulus 1.94 GPa
281 ksi
1.3 mm/min, 50 mm span; ASTM D790
2.00 GPa
290 ksi
2 mm/min; ISO 178
Izod Impact, Notched 6.60 J/cm
12.4 ft-lb/in
ASTM D256
Izod Impact, Notched (ISO) 9.00 kJ/m²
4.28 ft-lb/in²
80*10*4; ISO 180/1A
Dart Drop, Total Energy 95.0 J

@Temperature 23.0 °C
 70.1 ft-lb

@Temperature 73.4 °F
 ASTM D3763
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 85.0 µm/m-°C

@Temperature 23.0 - 60.0 °C
 47.2 µin/in-°F

@Temperature 73.4 - 140 °F
 ISO 11359-2
115 µm/m-°C

@Temperature -40.0 - 40.0 °C
 63.9 µin/in-°F

@Temperature -40.0 - 104 °F
 ASTM E 831
CTE, linear, Transverse to Flow 85.0 µm/m-°C

@Temperature 23.0 - 60.0 °C
 47.2 µin/in-°F

@Temperature 73.4 - 140 °F
 ISO 11359-2
105 µm/m-°C

@Temperature -40.0 - 40.0 °C
 58.3 µin/in-°F

@Temperature -40.0 - 104 °F
 ASTM E 831
Deflection Temperature at 0.46 MPa (66 psi) 102 °C

@Thickness 3.20 mm
 216 °F

@Thickness 0.126 in
 unannealed; ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 90.0 °C
194 °F
Edgew 120*10*4 sp=100mm; ISO 75/Ae
88.0 °C

@Thickness 3.20 mm
 190 °F

@Thickness 0.126 in
 unannealed; ASTM D648
Vicat Softening Point 106 °C
223 °F
Rate B/120; ISO 306
108 °C
226 °F
Rate B/50; ASTM D1525
Optical Properties Metric English Comments
Haze 2.0 %

@Thickness 2.54 mm
 2.0 %

@Thickness 0.100 in
 ASTM D1003
Transmission, Visible 88 %
88 %
2.54 mm; ASTM D1003