SABIC Innovative Plastics LNP THERMOCOMP UC008H PPA
| Category | Polymer , Thermoplastic , Polyphthalamide (PPA) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP THERMOCOMP |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP THERMOCOMP UC008H PPA.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP THERMOCOMP* UC008H is a compound based on Polyphthalamide resin containing 40% Carbon Fiber. Added features of this material include: Electrically Conductive, Healthcare.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.38 g/cc | 0.0499 lb/in³ | ASTM D792 |
| Moisture Absorption | 0.400 % | 0.400 % | 50% RH, 24 hrs; ASTM D570 |
| 0.460 - 1.38 % | 0.460 - 1.38 % | 23°C / 50% RH; ISO 62 | |
| Linear Mold Shrinkage, Flow | 0.0070 - 0.0090 cm/cm @Time 86400 sec |
0.0070 - 0.0090 in/in @Time 24.0 hour |
ASTM D955 |
| 0.0070 - 0.0090 cm/cm @Time 86400 sec |
0.0070 - 0.0090 in/in @Time 24.0 hour |
ISO 294 | |
| Linear Mold Shrinkage, Transverse | 0.0070 - 0.0090 cm/cm @Time 86400 sec |
0.0070 - 0.0090 in/in @Time 24.0 hour |
ASTM D955 |
| 0.0070 - 0.0090 cm/cm @Time 86400 sec |
0.0070 - 0.0090 in/in @Time 24.0 hour |
ISO 294 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 232 MPa | 33600 psi | ISO 527 |
| 261 MPa | 37900 psi | ASTM D638 | |
| Elongation at Break | 1.0 % | 1.0 % | ASTM D638 |
| 1.3 % | 1.3 % | ISO 527 | |
| Tensile Modulus | 33.78 GPa | 4899 ksi | 50 mm/min; ASTM D638 |
| 35.53 GPa | 5153 ksi | 1 mm/min; ISO 527 | |
| Flexural Strength | 425 MPa | 61600 psi | ISO 178 |
| 441 MPa | 64000 psi | ASTM D790 | |
| Flexural Modulus | 26.59 GPa | 3857 ksi | ISO 178 |
| 26.82 GPa | 3890 ksi | ASTM D790 | |
| Izod Impact, Notched | 0.580 J/cm | 1.09 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 3.28 J/cm | 6.14 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 7.00 kJ/m² | 3.33 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 45.0 kJ/m² | 21.4 ft-lb/in² | 80*10*4; ISO 180/1U |
| Dart Drop, Total Energy | 7.00 J | 5.16 ft-lb | Instrumented Impact Energy @ peak; ASTM D3763 |
| Impact Test | 5.00 J | 3.69 ft-lb | Multiaxial Impact; ISO 6603 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | >= 250 °C | >= 482 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| >= 248 °C @Thickness 3.20 mm |
>= 478 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 100 - 10000 ohm-cm | 100 - 10000 ohm-cm | ASTM D257 |
| Surface Resistance | 100 - 10000 ohm | 100 - 10000 ohm | ASTM D257 |
Users viewing this material also viewed the following:
- Nye Lubricants 868 (FG) Synthetic Oil
- Osprey Metals 434L Stainless Steel Powder (Grade 90% - 16)
- Resin Technology Group UV-412 Medium Viscosity, High Clarity, UV Curable Adhesive
- Westlake EF606 Low Density Polyethylene
- Hexcel® HexWeb® CR III 5/32-5052-.0015 Corrosion Resistant Specification Grade Aluminum Honeycomb
- Polyram PlusTek PB200 Nylon 6 for Extrusion
- Cytec Thornel® VCK Carbon Cloth Laminate with Mil R-9299 Resin
- Covestro Makrofol® DE 7-2 Polycarbonate
- Lanxess Pocan® TP 740-201 000000 PBT + ASA, 20% Glass Fiber (discontinued **)
Copyright © lookpolymers.com All Rights Reserved