Polymer Resources PPX-GP4 Modified PPO, General Purpose with HDT of 210 F (Unverified Data**)

Category	Polymer , Thermoplastic , Polyphenylene Ether/PPO , Polyphenylene Ether, Molded
Manufacturer
Trade Name
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Polymer Resources PPX-GP4 Modified PPO, General Purpose with HDT of 210 F (Unverified Data**).pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Process: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples. Information provided by Polymer Resources Corporation.

Physical Properties	Metric	English	Comments
Density	1.06 g/cc	0.0383 lb/in³	ASTM D792
Linear Mold Shrinkage	0.0050 - 0.0070 cm/cm	0.0050 - 0.0070 in/in	ASTM D955
Melt Flow	20 - 30 g/10 min	20 - 30 g/10 min	ASTM D1238

Mechanical Properties	Metric	English	Comments
Tensile Strength at Break	34.5 MPa	5000 psi	ASTM D638
Tensile Strength, Yield	34.5 MPa	5000 psi	ASTM D638
Flexural Strength	48.3 MPa	7000 psi	ASTM D790
Flexural Modulus	1.76 GPa	255 ksi	ASTM D790
Izod Impact, Notched	2.67 J/cm	5.00 ft-lb/in	ASTM D256
Gardner Impact	>= 14.1 J	>= 10.4 ft-lb	ASTM D3029

Thermal Properties	Metric	English	Comments
Deflection Temperature at 0.46 MPa (66 psi)	98.9 °C	210 °F	ASTM D648
Deflection Temperature at 1.8 MPa (264 psi)	93.3 °C	200 °F	ASTM D648
Flammability, UL94	HB	HB	1/16 in
	HB	HB	1/8 in

Processing Properties	Metric	English
Rear Barrel Temperature	249 - 299 °C	480 - 570 °F
Middle Barrel Temperature	260 - 304 °C	500 - 580 °F
Front Barrel Temperature	271 - 310 °C	520 - 590 °F
Melt Temperature	288 - 316 °C	550 - 600 °F
Mold Temperature	71.1 - 98.9 °C	160 - 210 °F
Drying Temperature	104 - 110 °C	220 - 230 °F
Dry Time	3 - 4 hour	3 - 4 hour