SABIC Innovative Plastics Valox® ENH4560 PBT (Asia Pacific)

Category Polymer , Thermoplastic , Polyester, TP , Polybutylene Terephthalate (PBT)
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name Valox®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics Valox® ENH4560 PBT (Asia Pacific).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Valox* ENH4560 resin is a non-brominated/non-chlorinated flame retardant product based on Valox* iQ PBT resin.
Physical Properties Metric English Comments
Specific Gravity 1.56 g/cc
1.56 g/cc
ASTM D792
Density 1.56 g/cc
0.0564 lb/in³
ISO 1183
Moisture Absorption 0.0900 %
0.0900 %
23°C / 50% RH; ISO 62
Water Absorption at Saturation 0.23 %
0.23 %
ISO 62
Linear Mold Shrinkage, Flow 0.0028 cm/cm

@Thickness 3.20 mm
 0.0028 in/in

@Thickness 0.126 in
 SABIC Method
Melt Index of Compound 16 g/10 min

@Load 5.00 kg,
Temperature 250 °C
 16 g/10 min

@Load 11.0 lb,
Temperature 482 °F
 MVR [cm^3/10 min]; ISO 1133
Mechanical Properties Metric English Comments
Tensile Strength at Break 105 MPa
15200 psi
Type I, 5 mm/min; ASTM D638
108 MPa
15700 psi
5 mm/min; ISO 527
Tensile Strength, Yield 105 MPa
15200 psi
Type I, 5 mm/min; ASTM D638
108 MPa
15700 psi
5 mm/min; ISO 527
Elongation at Break 2.0 %
2.0 %
Type I, 5 mm/min; ASTM D638
2.0 %
2.0 %
5 mm/min; ISO 527
Elongation at Yield 2.0 %
2.0 %
Type I, 5 mm/min; ASTM D638
2.0 %
2.0 %
5 mm/min; ISO 527
Tensile Modulus 11.0 GPa
1600 ksi
5 mm/min; ASTM D638
11.0 GPa
1600 ksi
1 mm/min; ISO 527
Flexural Strength 165 MPa
23900 psi
1.3 mm/min, 50 mm span; ASTM D790
175 MPa
25400 psi
2 mm/min; ISO 178
Flexural Yield Strength 165 MPa
23900 psi
1.3 mm/min, 50 mm span; ASTM D790
175 MPa
25400 psi
2 mm/min; ISO 178
Flexural Modulus 9.60 GPa
1390 ksi
1.3 mm/min, 50 mm span; ASTM D790
10.0 GPa
1450 ksi
2 mm/min; ISO 178
Izod Impact, Notched 0.720 J/cm
1.35 ft-lb/in
ASTM D256
0.550 J/cm

@Temperature -30.0 °C
 1.03 ft-lb/in

@Temperature -22.0 °F
 ASTM D256
Izod Impact, Unnotched 5.70 J/cm
10.7 ft-lb/in
ASTM D4812
Izod Impact, Notched (ISO) 7.00 kJ/m²
3.33 ft-lb/in²
80*10*4; ISO 180/1A
6.00 kJ/m²

@Temperature -30.0 °C
 2.86 ft-lb/in²

@Temperature -22.0 °F
 80*10*4; ISO 180/1A
Izod Impact, Unnotched (ISO) 37.0 kJ/m²
17.6 ft-lb/in²
80*10*4; ISO 180/1U
Dart Drop, Total Energy 6.00 J

@Temperature 23.0 °C
 4.43 ft-lb

@Temperature 73.4 °F
 ASTM D3763
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 24.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
 13.3 µin/in-°F

@Temperature -40.0 - 104 °F
 ASTM E 831
CTE, linear, Transverse to Flow 80.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
 44.4 µin/in-°F

@Temperature -40.0 - 104 °F
 ASTM E 831
Deflection Temperature at 1.8 MPa (264 psi) 205 °C
401 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af
200 °C

@Thickness 3.20 mm
 392 °F

@Thickness 0.126 in
 unannealed; ASTM D648
210 °C

@Thickness 6.40 mm
 410 °F

@Thickness 0.252 in
 unannealed; ASTM D648
Vicat Softening Point 195 °C
383 °F
Rate B/50; ASTM D1525
195 °C
383 °F
Rate B/50; ISO 306
205 °C
401 °F
Rate B/120; ISO 306
Flammability, UL94 V-0

@Thickness 0.800 mm
 V-0

@Thickness 0.0315 in
 UL 94
5VB

@Thickness 3.00 mm
 5VB

@Thickness 0.118 in
 UL 94
Glow Wire Test 800 °C
1470 °F
IEC 60695-2-13
960 °C

@Thickness 1.00 mm
 1760 °F

@Thickness 0.0394 in
 IEC 60695-2-12
Electrical Properties Metric English Comments
Comparative Tracking Index >= 600 V
>= 600 V
UL 746A
600 V
600 V
IEC 60112
Hot Wire Ignition, HWI >= 120 sec
>= 120 sec
UL 746A
High Amp Arc Ignition, HAI >= 120 arcs
>= 120 arcs
UL 746A
Descriptive Properties Value Comments
Ball Pressure Test, 125°C +/- 2°C PASSES
IEC 60695-10-2
Users viewing this material also viewed the following: