SABIC Innovative Plastics Valox® DR48 PBT (Europe-Africa-Middle East)

Category Polymer , Thermoplastic , Polyester, TP , Polybutylene Terephthalate (PBT)
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name Valox®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics Valox® DR48 PBT (Europe-Africa-Middle East).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
VALOX DR48 is a 17% glass reinforced, flame retardant injection moulding PBT resin. Applications: lamp sockets, connectors, switches, electrical housings and bases, bobbins, trimmers and electromotor housings.
Physical Properties Metric English Comments
Specific Gravity 1.51 g/cc
1.51 g/cc
ASTM D792
Density 1.51 g/cc
0.0546 lb/in³
ISO 1183
Filler Content 17 %
17 %
ASTM D229
Moisture Absorption 0.0700 %
0.0700 %
23°C / 50% RH; ISO 62
Water Absorption at Saturation 0.17 %
0.17 %
ISO 62
Viscosity 105000 cP
105000 cP
Melt Viscosity, 260°C, 1500 sec-1; ISO 11443
Linear Mold Shrinkage, Flow 0.0050 - 0.0080 cm/cm
0.0050 - 0.0080 in/in
on Tensile Bar; SABIC Method
Linear Mold Shrinkage, Transverse 0.0060 - 0.0090 cm/cm
0.0060 - 0.0090 in/in
on Tensile Bar; SABIC Method
Melt Flow 90 g/10 min

@Load 5.00 kg,
Temperature 266 °C
90 g/10 min

@Load 11.0 lb,
Temperature 511 °F
ASTM D1238
Melt Index of Compound 14 g/10 min

@Load 2.16 kg,
Temperature 250 °C
14 g/10 min

@Load 4.76 lb,
Temperature 482 °F
MVR [cm^3/10 min]; ISO 1133
40 g/10 min

@Load 5.00 kg,
Temperature 250 °C
40 g/10 min

@Load 11.0 lb,
Temperature 482 °F
MVR [cm^3/10 min]; ISO 1133
70 g/10 min

@Load 5.00 kg,
Temperature 265 °C
70 g/10 min

@Load 11.0 lb,
Temperature 509 °F
MVR [cm^3/10 min]; ISO 1133
Mechanical Properties Metric English Comments
Hardness, Rockwell R 120
120
ISO 2039-2
Hardness, H358/30 218 MPa
31600 psi
ISO 2039-1
Tensile Strength at Break 100 MPa
14500 psi
Type I, 5 mm/min; ASTM D638
104 MPa
15100 psi
5 mm/min; ISO 527
Tensile Strength, Yield 100 MPa
14500 psi
Type I, 5 mm/min; ASTM D638
104 MPa
15100 psi
5 mm/min; ISO 527
Elongation at Break 2.0 %
2.0 %
Type I, 5 mm/min; ASTM D638
2.0 %
2.0 %
5 mm/min; ISO 527
3.0 %
3.0 %
Flexural Strain, break, 2 mm/min; ISO 178
Elongation at Yield 2.0 %
2.0 %
Type I, 5 mm/min; ASTM D638
2.0 %
2.0 %
5 mm/min; ISO 527
Tensile Modulus 7.00 GPa
1020 ksi
1 mm/min; ISO 527
7.10 GPa
1030 ksi
5 mm/min; ASTM D638
Flexural Strength 130 MPa
18900 psi
1.3 mm/min, 50 mm span; ASTM D790
155 MPa
22500 psi
2 mm/min; ISO 178
Flexural Yield Strength 130 MPa
18900 psi
1.3 mm/min, 50 mm span; ASTM D790
155 MPa
22500 psi
2 mm/min; ISO 178
Flexural Modulus 5.40 GPa
783 ksi
1.3 mm/min, 50 mm span; ASTM D790
6.10 GPa
885 ksi
2 mm/min; ISO 178
Izod Impact, Notched 0.450 J/cm
0.843 ft-lb/in
ASTM D256
0.450 J/cm

@Temperature 0.000 °C
0.843 ft-lb/in

@Temperature 32.0 °F
ASTM D256
0.450 J/cm

@Temperature -30.0 °C
0.843 ft-lb/in

@Temperature -22.0 °F
ASTM D256
Izod Impact, Unnotched 2.80 J/cm
5.25 ft-lb/in
ASTM D4812
2.75 J/cm

@Temperature -30.0 °C
5.15 ft-lb/in

@Temperature -22.0 °F
ASTM D4812
Izod Impact, Notched (ISO) 5.00 kJ/m²
2.38 ft-lb/in²
80*10*4; ISO 180/1A
5.00 kJ/m²

@Temperature 0.000 °C
2.38 ft-lb/in²

@Temperature 32.0 °F
80*10*4; ISO 180/1A
5.00 kJ/m²

@Temperature -30.0 °C
2.38 ft-lb/in²

@Temperature -22.0 °F
80*10*4; ISO 180/1A
Izod Impact, Unnotched (ISO) 20.0 kJ/m²
9.52 ft-lb/in²
80*10*4; ISO 180/1U
20.0 kJ/m²

@Temperature -30.0 °C
9.52 ft-lb/in²

@Temperature -22.0 °F
80*10*4; ISO 180/1U
Charpy Impact Unnotched 2.40 J/cm²
11.4 ft-lb/in²
ISO 179/2C
2.50 J/cm²
11.9 ft-lb/in²
Edgew 80*10*4 sp=62mm; ISO 179/1eU
2.00 J/cm²

@Temperature -30.0 °C
9.52 ft-lb/in²

@Temperature -22.0 °F
Edgew 80*10*4 sp=62mm; ISO 179/1eU
2.40 J/cm²

@Temperature -30.0 °C
11.4 ft-lb/in²

@Temperature -22.0 °F
ISO 179/2C
Charpy Impact, Notched 0.500 J/cm²
2.38 ft-lb/in²
Edgew 80*10*4 sp=62mm; ISO 179/1eA
0.500 J/cm²
2.38 ft-lb/in²
ISO 179/2C
0.400 J/cm²

@Temperature -30.0 °C
1.90 ft-lb/in²

@Temperature -22.0 °F
Edgew 80*10*4 sp=62mm; ISO 179/1eA
0.500 J/cm²

@Temperature -30.0 °C
2.38 ft-lb/in²

@Temperature -22.0 °F
ISO 179/2C
Taber Abrasion, mg/1000 Cycles 16
16
CS-17, 1 kg; SABIC Method
Electrical Properties Metric English Comments
Volume Resistivity 1.00e+15 ohm-cm
1.00e+15 ohm-cm
ASTM D257
1.00e+15 ohm-cm
1.00e+15 ohm-cm
IEC 60093
Surface Resistance >= 1.00e+15 ohm
>= 1.00e+15 ohm
ROA; IEC 60093
Dielectric Constant 3.1

@Frequency 1.00e+6 Hz
3.1

@Frequency 1.00e+6 Hz
ASTM D150
3.1

@Frequency 1.00e+6 Hz
3.1

@Frequency 1.00e+6 Hz
IEC 60250
3.2

@Frequency 50.0 - 60.0 Hz
3.2

@Frequency 50.0 - 60.0 Hz
IEC 60250
Dielectric Strength 16.0 kV/mm

@Thickness 3.20 mm
406 kV/in

@Thickness 0.126 in
in oil; ASTM D149
16.0 kV/mm

@Thickness 3.20 mm
406 kV/in

@Thickness 0.126 in
in oil; IEC 60243-1
19.0 kV/mm

@Thickness 1.00 mm
483 kV/in

@Thickness 0.0394 in
short time; IEC 60243-1
23.0 kV/mm

@Thickness 1.60 mm
584 kV/in

@Thickness 0.0630 in
in oil; ASTM D149
23.0 kV/mm

@Thickness 1.60 mm
584 kV/in

@Thickness 0.0630 in
in oil; IEC 60243-1
29.0 kV/mm

@Thickness 0.800 mm
737 kV/in

@Thickness 0.0315 in
in oil; IEC 60243-1
29.0 kV/mm

@Thickness 0.800 mm
737 kV/in

@Thickness 0.0315 in
in oil; ASTM D149
Dissipation Factor 0.0010

@Frequency 50.0 - 60.0 Hz
0.0010

@Frequency 50.0 - 60.0 Hz
IEC 60250
0.012

@Frequency 1.00e+6 Hz
0.012

@Frequency 1.00e+6 Hz
IEC 60250
0.012

@Frequency 1.00e+6 Hz
0.012

@Frequency 1.00e+6 Hz
ASTM D150
Arc Resistance 60 - 120 sec
60 - 120 sec
Tungsten; ASTM D495
Comparative Tracking Index >= 150 V
>= 150 V
IEC 60112
175 V
175 V
IEC 60112
175 - 250 V
175 - 250 V
UL 746A