SABIC Innovative Plastics Valox® 865 PBT (Europe-Africa-Middle East)
| Category | Polymer , Thermoplastic , Polyester, TP , Polybutylene Terephthalate (PBT) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | Valox® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics Valox® 865 PBT (Europe-Africa-Middle East).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
VALOX 865 is a 30% glass fibre reinforced, non blooming flame retardant PBT+PET blend with an excellent surface appearance. Applications: External housings, steam irons, appliance housings and lighting parts.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.65 g/cc | 1.65 g/cc | ASTM D792 |
| Density | 1.65 g/cc | 0.0596 lb/in³ | ISO 1183 |
| Filler Content | 30 % | 30 % | ASTM D229 |
| Moisture Absorption | 0.0300 % | 0.0300 % | 23°C / 50% RH; ISO 62 |
| Water Absorption at Saturation | 0.32 % | 0.32 % | ISO 62 |
| Viscosity | 145000 cP | 145000 cP | Melt Viscosity, 260°C, 1500 sec-1; ISO 11443 |
| Linear Mold Shrinkage, Flow | 0.0040 - 0.0080 cm/cm | 0.0040 - 0.0080 in/in | on Tensile Bar; SABIC Method |
| Linear Mold Shrinkage, Transverse | 0.0060 - 0.010 cm/cm | 0.0060 - 0.010 in/in | on Tensile Bar; SABIC Method |
| Melt Flow | 70 g/10 min @Load 5.00 kg, Temperature 266 °C |
70 g/10 min @Load 11.0 lb, Temperature 511 °F |
ASTM D1238 |
| Melt Index of Compound | 7.0 g/10 min @Load 1.20 kg, Temperature 265 °C |
7.0 g/10 min @Load 2.65 lb, Temperature 509 °F |
MVR [cm^3/10 min]; ISO 1133 |
| 15 g/10 min @Load 2.16 kg, Temperature 265 °C |
15 g/10 min @Load 4.76 lb, Temperature 509 °F |
MVR [cm^3/10 min]; ISO 1133 | |
| 23 g/10 min @Load 5.00 kg, Temperature 250 °C |
23 g/10 min @Load 11.0 lb, Temperature 482 °F |
MVR [cm^3/10 min]; ISO 1133 | |
| 50 g/10 min @Load 5.00 kg, Temperature 265 °C |
50 g/10 min @Load 11.0 lb, Temperature 509 °F |
MVR [cm^3/10 min]; ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 120 | 120 | ISO 2039-2 |
| Hardness, H358/30 | 115 MPa | 16700 psi | ISO 2039-1 |
| Tensile Strength at Break | 130 MPa | 18900 psi | 5 mm/min; ISO 527 |
| 135 MPa | 19600 psi | Type I, 5 mm/min; ASTM D638 | |
| Tensile Strength, Yield | 130 MPa | 18900 psi | 5 mm/min; ISO 527 |
| 135 MPa | 19600 psi | Type I, 5 mm/min; ASTM D638 | |
| Elongation at Break | 2.0 % | 2.0 % | Type I, 5 mm/min; ASTM D638 |
| 2.0 % | 2.0 % | 5 mm/min; ISO 527 | |
| 3.0 % | 3.0 % | Flexural Strain, break, 2 mm/min; ISO 178 | |
| Elongation at Yield | 2.0 % | 2.0 % | Type I, 5 mm/min; ASTM D638 |
| 2.0 % | 2.0 % | 5 mm/min; ISO 527 | |
| Tensile Modulus | 11.0 GPa | 1600 ksi | 5 mm/min; ASTM D638 |
| 11.0 GPa | 1600 ksi | 1 mm/min; ISO 527 | |
| Flexural Strength | 185 MPa | 26800 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| 195 MPa | 28300 psi | 2 mm/min; ISO 178 | |
| Flexural Yield Strength | 185 MPa | 26800 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| 195 MPa | 28300 psi | 2 mm/min; ISO 178 | |
| Flexural Modulus | 9.00 GPa | 1310 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
| 9.20 GPa | 1330 ksi | 2 mm/min; ISO 178 | |
| Izod Impact, Notched | 0.750 J/cm | 1.41 ft-lb/in | ASTM D256 |
| 0.750 J/cm @Temperature 0.000 °C |
1.41 ft-lb/in @Temperature 32.0 °F |
ASTM D256 | |
| 0.750 J/cm @Temperature -30.0 °C |
1.41 ft-lb/in @Temperature -22.0 °F |
ASTM D256 | |
| Izod Impact, Unnotched | 7.30 J/cm | 13.7 ft-lb/in | ASTM D4812 |
| 7.20 J/cm @Temperature -30.0 °C |
13.5 ft-lb/in @Temperature -22.0 °F |
ASTM D4812 | |
| Izod Impact, Notched (ISO) | 8.00 kJ/m² | 3.81 ft-lb/in² | 80*10*4; ISO 180/1A |
| 7.00 kJ/m² @Temperature -30.0 °C |
3.33 ft-lb/in² @Temperature -22.0 °F |
80*10*4; ISO 180/1A | |
| 8.00 kJ/m² @Temperature 0.000 °C |
3.81 ft-lb/in² @Temperature 32.0 °F |
80*10*4; ISO 180/1A | |
| Izod Impact, Unnotched (ISO) | 50.0 kJ/m² | 23.8 ft-lb/in² | 80*10*4; ISO 180/1U |
| 45.0 kJ/m² @Temperature -30.0 °C |
21.4 ft-lb/in² @Temperature -22.0 °F |
80*10*4; ISO 180/1U | |
| Charpy Impact Unnotched | 5.00 J/cm² | 23.8 ft-lb/in² | Edgew 80*10*4 sp=62mm; ISO 179/1eU |
| 5.50 J/cm² | 26.2 ft-lb/in² | ISO 179/2C | |
| 5.00 J/cm² @Temperature -30.0 °C |
23.8 ft-lb/in² @Temperature -22.0 °F |
ISO 179/2C | |
| NB @Temperature -30.0 °C |
NB @Temperature -22.0 °F |
Edgew 80*10*4 sp=62mm; ISO 179/1eU | |
| Charpy Impact, Notched | 0.800 J/cm² | 3.81 ft-lb/in² | Edgew 80*10*4 sp=62mm; ISO 179/1eA |
| 0.800 J/cm² | 3.81 ft-lb/in² | ISO 179/2C | |
| 0.800 J/cm² @Temperature -30.0 °C |
3.81 ft-lb/in² @Temperature -22.0 °F |
Edgew 80*10*4 sp=62mm; ISO 179/1eA | |
| 0.800 J/cm² @Temperature -30.0 °C |
3.81 ft-lb/in² @Temperature -22.0 °F |
ISO 179/2C |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+15 ohm-cm | 1.00e+15 ohm-cm | ASTM D257 |
| 1.00e+15 ohm-cm | 1.00e+15 ohm-cm | IEC 60093 | |
| Surface Resistance | >= 1.00e+15 ohm | >= 1.00e+15 ohm | ROA; IEC 60093 |
| Dielectric Constant | 3.3 @Frequency 1.00e+6 Hz |
3.3 @Frequency 1.00e+6 Hz |
IEC 60250 |
| 3.4 @Frequency 50.0 - 60.0 Hz |
3.4 @Frequency 50.0 - 60.0 Hz |
IEC 60250 | |
| Dielectric Strength | 15.0 kV/mm @Thickness 3.20 mm |
381 kV/in @Thickness 0.126 in |
in oil; ASTM D149 |
| 15.0 kV/mm @Thickness 3.20 mm |
381 kV/in @Thickness 0.126 in |
in oil; IEC 60243-1 | |
| 19.0 kV/mm @Thickness 1.60 mm |
483 kV/in @Thickness 0.0630 in |
in oil; ASTM D149 | |
| 19.0 kV/mm @Thickness 1.60 mm |
483 kV/in @Thickness 0.0630 in |
in oil; IEC 60243-1 | |
| 25.0 kV/mm @Thickness 0.800 mm |
635 kV/in @Thickness 0.0315 in |
in oil; IEC 60243-1 | |
| 25.0 kV/mm @Thickness 0.800 mm |
635 kV/in @Thickness 0.0315 in |
in oil; ASTM D149 | |
| Dissipation Factor | 0.0010 @Frequency 50.0 - 60.0 Hz |
0.0010 @Frequency 50.0 - 60.0 Hz |
IEC 60250 |
| 0.012 @Frequency 1.00e+6 Hz |
0.012 @Frequency 1.00e+6 Hz |
IEC 60250 | |
| Arc Resistance | 60 - 120 sec | 60 - 120 sec | Tungsten; ASTM D495 |
| Comparative Tracking Index | >= 150 V | >= 150 V | IEC 60112 |
| 175 - 250 V | 175 - 250 V | UL 746A | |
| 225 V | 225 V | IEC 60112 | |
| Hot Wire Ignition, HWI | 60 - 120 sec | 60 - 120 sec | UL 746A |
| High Amp Arc Ignition, HAI | 15 - 30 arcs | 15 - 30 arcs | UL 746A |
Users viewing this material also viewed the following:
- Plansee MoRe41 Molybdenum-Rhenium
- Nye Lubricants 737B (RL) Synthetic Oil
- MetalTek MTEK 25-35LC Heat Resistant Stainless Steel
- SABIC Innovative Plastics SABIC PPCOMPOUND 8620A PP
- Shandong Rike Chemical HELIâ„¢ HG-200 PVC Processing Aid Series (PA)
- Teknor Apex APEX® 84459 Polyvinyl Chloride, Flexible
- Dynasol Calprene® 710 Thermoplastic Rubber SBS Dry
- Shakespeare LMX-3 Easy Casting Nylon Copolymer Fishing Line, 4 lb
Copyright © lookpolymers.com All Rights Reserved