ExxonMobil OPTEMA™ TC 115 Molding, extrusion and compounding resin (discontinued **)

Category	Polymer , Thermoplastic , Ethylene Methyl Acrylate , Ethylene-Methyl Acrylate Copolymer, Molding Grade
Manufacturer
Trade Name
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	ExxonMobil OPTEMA™ TC 115 Molding, extrusion and compounding resin (discontinued **).pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

OPTEMA TC 115 is an ethylene methyl acrylate copolymer, which can be used as a compatibilizer and impact modifier for engineering thermoplastics. It has been processed at temperatures up to 625°F without thermal degradation.Information provided by ExxonMobil Chemical

Physical Properties	Metric	English	Comments
Density	0.937 g/cc	0.0339 lb/in³	ExxonMobil Method
Methyl Acrylate Content	16.5 %	16.5 %
Melt Flow	0.70 g/10 min	0.70 g/10 min	ASTM D1238

Mechanical Properties	Metric	English	Comments
Hardness, Shore A	84	84	15s; ASTM D2240
Hardness, Shore D	34	34	15s; ASTM D2240
Tensile Strength at Break	12.1 MPa	1750 psi	ASTM D638
Elongation at Break	>= 800 %	>= 800 %	ASTM D638
Flexural Modulus	0.0572 GPa	8.30 ksi	1% secant; ASTM D790
Impact Test	20.3 J @Temperature 23.0 °C	15.0 ft-lb @Temperature 73.4 °F	Instrument Impact, Total Energy; ASTM D3763
	31.2 J @Temperature -40.0 °C	23.0 ft-lb @Temperature -40.0 °F	Instrumented Impact, Total Energy; ASTM D3763

Thermal Properties	Metric	English	Comments
Melting Point	87.2 °C	189 °F	Peak Melting Temperature; ExxonMobil Method
Vicat Softening Point	43.3 °C	110 °F	ASTM D1525

Descriptive Properties	Value	Comments
Features	Thermal Stabilizer

Users viewing this material also viewed the following: