SABIC Innovative Plastics Valox® 175 PBT

Category Polymer , Thermoplastic , Polyester, TP , Polybutylene Terephthalate (PBT)
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name Valox®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics Valox® 175 PBT.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Unreinforced, neat PBT resin for compounding only. Natural Color Only, Not intended for injection molding.This data was supplied by SABIC-IP for the Americas region.
Physical Properties Metric English Comments
Specific Gravity 1.32 g/cc
1.32 g/cc
ASTM D 792
Density 1.31 g/cc
0.0473 lb/in³
ISO 1183
Moisture Absorption at Equilibrium 0.070 %
0.070 %
23°C / 50% RH; ISO 62
Water Absorption at Saturation 0.080 %

@Temperature 23.0 °C
 0.080 %

@Temperature 73.4 °F
 ISO 62
Linear Mold Shrinkage, Flow 0.015 - 0.018 cm/cm

@Thickness 3.20 mm
 0.015 - 0.018 in/in

@Thickness 0.126 in
 SABIC Method
Linear Mold Shrinkage, Transverse 0.016 - 0.020 cm/cm

@Thickness 3.20 mm
 0.016 - 0.020 in/in

@Thickness 0.126 in
 SABIC Method
Melt Flow 127 g/10 min

@Load 1.20 kg,
Temperature 250 °C
 127 g/10 min

@Load 2.65 lb,
Temperature 482 °F
 ASTM D 1238
127 g/10 min

@Load 1.20 kg,
Temperature 250 °C
 127 g/10 min

@Load 2.65 lb,
Temperature 482 °F
 [cm^3/10 min] Melt Volume Rate; ISO 1133
231 g/10 min

@Load 2.16 kg,
Temperature 250 °C
 231 g/10 min

@Load 4.76 lb,
Temperature 482 °F
 [cm^3/10 min] Melt Volume Rate; ISO 1133
Mechanical Properties Metric English Comments
Tensile Strength at Break 45.0 MPa
6530 psi
50 mm/min; ISO 527
50.0 MPa
7250 psi
Type I, 50 mm/min; ASTM D 638
Tensile Strength, Yield 45.0 MPa
6530 psi
50 mm/min; ISO 527
50.0 MPa
7250 psi
Type I, 50 mm/min; ASTM D 638
Elongation at Break 1.8 %
1.8 %
50 mm/min; ISO 527
2.0 %
2.0 %
Type I, 50 mm/min; ASTM D 638
Elongation at Yield 1.8 %
1.8 %
50 mm/min; ISO 527
2.0 %
2.0 %
Type I, 50 mm/min; ASTM D 638
Tensile Modulus 2.50 GPa
363 ksi
5 mm/min; ASTM D 638
2.60 GPa
377 ksi
1 mm/min; ISO 527
Flexural Yield Strength 81.0 MPa
11700 psi
2 mm/min; ISO 178
84.0 MPa
12200 psi
1.3 mm/min, 50 mm span; ASTM D 790
Flexural Modulus 2.29 GPa
332 ksi
2 mm/min; ISO 178
2.39 GPa
347 ksi
1.3 mm/min, 50 mm span; ASTM D 790
Izod Impact, Notched 0.280 J/cm

@Temperature 23.0 °C
 0.525 ft-lb/in

@Temperature 73.4 °F
 ASTM D 256
Izod Impact, Unnotched 8.90 J/cm

@Temperature 23.0 °C
 16.7 ft-lb/in

@Temperature 73.4 °F
 ASTM D 4812
Izod Impact, Notched (ISO) 2.00 kJ/m²

@Temperature 23.0 °C
 0.952 ft-lb/in²

@Temperature 73.4 °F
 80*10*4; ISO 180/1A
Izod Impact, Unnotched (ISO) 35.0 kJ/m²

@Temperature 23.0 °C
 16.7 ft-lb/in²

@Temperature 73.4 °F
 80*10*4; ISO 180/1U
Charpy Impact, Notched 0.700 J/cm²

@Temperature 23.0 °C
 3.33 ft-lb/in²

@Temperature 73.4 °F
 V-notch Edgew 80*10*4 sp=62mm; ISO 179/1eA
Impact Test 5.00 J

@Temperature 23.0 °C
 3.69 ft-lb

@Temperature 73.4 °F
 Instrumented Impact Total Energy; ASTM D 3763
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 85.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
 47.2 µin/in-°F

@Temperature -40.0 - 104 °F
 ISO 11359-2
CTE, linear, Transverse to Flow 85.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
 47.2 µin/in-°F

@Temperature -40.0 - 104 °F
 ISO 11359-2
Deflection Temperature at 0.46 MPa (66 psi) 113 °C
235 °F
Flatw 80*10*4 sp=64mm; ISO 75/Bf
104 °C

@Thickness 3.20 mm
 219 °F

@Thickness 0.126 in
 unannealed; ASTM D 648
Deflection Temperature at 1.8 MPa (264 psi) 51.0 °C
124 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af
48.0 °C

@Thickness 3.20 mm
 118 °F

@Thickness 0.126 in
 unannealed; ASTM D 648
Vicat Softening Point 177 °C
351 °F
Rate B/120; ISO 306
178 °C
352 °F
Rate B/50; ISO 306