- HOME
- POLYMER SEARCH
- Thermoplastic
- Nylon
- Nylon 612
- PolyOne Lubri-Tech™ NL-40GB/15T Nylon 6/12 - 40% Glass Bead Reinforced - 15% PTFE Lubricated (discontinued **
PolyOne Lubri-Tech™ NL-40GB/15T Nylon 6/12 - 40% Glass Bead Reinforced - 15% PTFE Lubricated (discontinued **
| Category | Polymer , Thermoplastic , Nylon , Nylon 612 |
| Manufacturer | |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | PolyOne Lubri-Tech™ NL-40GB/15T Nylon 6/12 - 40% Glass Bead Reinforced - 15% PTFE Lubricated
(discontinued **.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Data provided by PolyOne.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.54 g/cc | 0.0556 lb/in³ | ASTM D792 |
| Water Absorption | 0.20 % | 0.20 % | 24 hrs. ASTM D570 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Ultimate | 45.0 MPa | 6530 psi | ASTM D638 |
| Elongation at Break | 3.0 - 4.0 % | 3.0 - 4.0 % | ASTM D638 |
| Izod Impact, Notched | 0.450 J/cm @Thickness 6.35 mm |
0.843 ft-lb/in @Thickness 0.250 in |
ASTM D256 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 249 - 271 °C | 480 - 520 °F | Stock |
| Mold Temperature | 49.0 - 82.0 °C | 120 - 180 °F | |
| Drying Temperature | 77.0 °C | 171 °F |
Users viewing this material also viewed the following:
- MV Labs PT260 Na2PtBr6 Sodium hexabromoplatinate(IV)
- TIMET TIMETAL® 6-4 ELI Titanium Alloy (Ti-6Al-4V ELI; ASTM Grade 23) (Annealed; 2.50 - 4.00 in Rod or Thickness; Per ASTM F136)
- Westlake Elevate™ EF563 6.5% Ethylene Vinyl Acetate Copolymer
- DuPont Performance Polymers VESPEL TP-8311 Polyimide
- ExxonMobil 60 Mobilube XFD
- DuPont Teijin Films Mylar® OL2 Polyester Film, 100 Gauge
- Axiall 7765 Rigid PVC, Extrusion
- Arlon 51576R031 0.031" (0.787 mm) Uncured/Cured Silicone Rubber with Fiberglass Substrate
- BASF Pluracol® TP 440 Specialty Polyol
Copyright © lookpolymers.com All Rights Reserved