SABIC Innovative Plastics ULTEM EXUM0169 PEI Blend
| Category | Polymer , Thermoplastic , Polyetherimide (PEI) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | ULTEM |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics ULTEM EXUM0169 PEI Blend.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Improved ductility, transparent, enhanced flow Polyetherimide blend (Tg 200C) with internal mold release and enhanced ductility. ECO Conforming.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.28 g/cc | 1.28 g/cc | ASTM D792 |
| Density | 1.28 g/cc | 0.0462 lb/in³ | ISO 1183 |
| Moisture Absorption | 0.0800 % | 0.0800 % | 23°C / 50% RH; ISO 62 |
| Water Absorption at Saturation | 0.36 % | 0.36 % | ISO 62 |
| Linear Mold Shrinkage, Flow | 0.0050 - 0.0070 cm/cm @Thickness 3.20 mm |
0.0050 - 0.0070 in/in @Thickness 0.126 in |
SABIC Method |
| Melt Flow | 43 g/10 min @Load 6.60 kg, Temperature 337 °C |
43 g/10 min @Load 14.6 lb, Temperature 639 °F |
ASTM D1238 |
| Melt Index of Compound | 56 g/10 min @Load 5.00 kg, Temperature 360 °C |
56 g/10 min @Load 11.0 lb, Temperature 680 °F |
MVR [cm^3/10 min]; ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell M | 108 | 108 | ASTM D785 |
| Tensile Strength at Break | 80.0 MPa | 11600 psi | 5 mm/min; ISO 527 |
| 85.0 MPa | 12300 psi | Type I, 5 mm/min; ASTM D638 | |
| Tensile Strength, Yield | 98.0 MPa | 14200 psi | 5 mm/min; ISO 527 |
| 103 MPa | 14900 psi | Type I, 5 mm/min; ASTM D638 | |
| Elongation at Break | 80 % | 80 % | Type I, 5 mm/min; ASTM D638 |
| 80 % | 80 % | 5 mm/min; ISO 527 | |
| Elongation at Yield | 7.0 % | 7.0 % | Type I, 5 mm/min; ASTM D638 |
| 7.0 % | 7.0 % | 5 mm/min; ISO 527 | |
| Tensile Modulus | 2.50 GPa | 363 ksi | 1 mm/min; ISO 527 |
| 3.21 GPa | 466 ksi | 5 mm/min; ASTM D638 | |
| Flexural Yield Strength | 135 MPa | 19600 psi | 2 mm/min; ISO 178 |
| 145 MPa | 21000 psi | 1.3 mm/min, 50 mm span; ASTM D790 | |
| Flexural Modulus | 3.10 GPa | 450 ksi | 2 mm/min; ISO 178 |
| 3.32 GPa | 482 ksi | 1.3 mm/min, 50 mm span; ASTM D790 | |
| Izod Impact, Notched | 0.320 J/cm | 0.599 ft-lb/in | ASTM D256 |
| 0.350 J/cm @Temperature -30.0 °C |
0.656 ft-lb/in @Temperature -22.0 °F |
ASTM D256 | |
| 20.85 J/cm @Thickness 3.20 mm |
39.06 ft-lb/in @Thickness 0.126 in |
ASTM D256 | |
| Izod Impact, Unnotched | NB | NB | ASTM D4812 |
| NB @Temperature -30.0 °C |
NB @Temperature -22.0 °F |
ASTM D4812 | |
| Izod Impact, Notched (ISO) | 2.00 kJ/m² | 0.952 ft-lb/in² | 80*10*4; ISO 180/1A |
| 2.00 kJ/m² @Temperature -30.0 °C |
0.952 ft-lb/in² @Temperature -22.0 °F |
80*10*4; ISO 180/1A | |
| Charpy Impact, Notched | 0.200 J/cm² | 0.952 ft-lb/in² | Edgew 80*10*4 sp=62mm; ISO 179/1eA |
| Dart Drop, Total Energy | 8.00 J @Temperature -20.0 °C |
5.90 ft-lb @Temperature -4.00 °F |
ASTM D3763 |
| 48.0 J @Temperature 23.0 °C |
35.4 ft-lb @Temperature 73.4 °F |
ASTM D3763 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 55.0 µm/m-°C @Temperature 23.0 - 150 °C |
30.6 µin/in-°F @Temperature 73.4 - 302 °F |
ISO 11359-2 |
| 60.0 µm/m-°C @Temperature -40.0 - 150 °C |
33.3 µin/in-°F @Temperature -40.0 - 302 °F |
ASTM E 831 | |
| CTE, linear, Transverse to Flow | 55.0 µm/m-°C @Temperature 23.0 - 150 °C |
30.6 µin/in-°F @Temperature 73.4 - 302 °F |
ISO 11359-2 |
| 60.0 µm/m-°C @Temperature -40.0 - 150 °C |
33.3 µin/in-°F @Temperature -40.0 - 302 °F |
ASTM E 831 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 168 °C | 334 °F | Edgew 120*10*4 sp=100mm; ISO 75/Ae |
| 173 °C @Thickness 3.20 mm |
343 °F @Thickness 0.126 in |
unannealed; ASTM D648 | |
| 178 °C @Thickness 6.40 mm |
352 °F @Thickness 0.252 in |
unannealed; ASTM D648 | |
| Vicat Softening Point | 192 °C | 378 °F | Rate B/50; ASTM D1525 |
| 192 °C | 378 °F | Rate B/50; ISO 306 | |
| 195 °C | 383 °F | Rate B/120; ISO 306 | |
| Glass Transition Temp, Tg | 200 °C | 392 °F |
| Optical Properties | Metric | English | Comments |
|---|---|---|---|
| Transmission, Visible | 90 % | 90 % | transparent; thickness not quantified |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+17 ohm-cm | 1.00e+17 ohm-cm | ASTM D257 |
| Surface Resistance | 1.60e+17 ohm | 1.60e+17 ohm | ASTM D257 |
| Dissipation Factor | 0.0061 @Frequency 1.00e+6 Hz |
0.0061 @Frequency 1.00e+6 Hz |
ASTM D150 |
Users viewing this material also viewed the following:
- Polykemi AB POLYelast TPE HJ753 Thermoplastic Elastomer, PP/Elastomer, Mineral Reinforced
- SABIC Innovative Plastics LNP LUBRICOMP CGI11XP PS (Europe-Africa-Middle East)
- Kraton® D1102 + PP blend (10/90)
- Momentive Performance Materials RTV5242 Neutral Cure, One Component RTV Adhesive Sealant
- Shandong Rike Chemical HELIâ„¢ HG-200 PVC Processing Aid Series (PA)
- SABIC Innovative Plastics LNP THERMOCOMP WC003 PBT (Europe-Africa-Middle East)
- DuPont™ Fusabond® P353 Polymer Modifier
- Epoxy Technology EPO-TEK® OE188 High Temperature Silica-Filled Epoxy
- ATI Allegheny Ludlum Stainless Steel Type 301, 1/2 Hard (UNS S30100)
- Polymer Resources AC-GP1 Acetal Copolymer, Low Flow, High Melt Strength (Unverified Data**)
Copyright © lookpolymers.com All Rights Reserved