SABIC Innovative Plastics ULTEM D9065 PEI
| Category | Polymer , Thermoplastic , Polyetherimide (PEI) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | ULTEM |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics ULTEM D9065 PEI.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Polyetherimide blend. Meets FAR 25.853 and OSU 65/65 with low toxicity, smoke, and flame evolution. ECO Conforming.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.32 g/cc | 1.32 g/cc | ASTM D792 |
| Linear Mold Shrinkage, Flow | 0.0050 - 0.0070 cm/cm @Thickness 3.20 mm |
0.0050 - 0.0070 in/in @Thickness 0.126 in |
SABIC Method |
| Linear Mold Shrinkage, Transverse | 0.0050 - 0.0070 cm/cm @Thickness 3.20 mm |
0.0050 - 0.0070 in/in @Thickness 0.126 in |
SABIC Method |
| Melt Flow | 15.6 g/10 min @Load 6.60 kg, Temperature 337 °C |
15.6 g/10 min @Load 14.6 lb, Temperature 639 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 88.0 MPa | 12800 psi | Type I, 5 mm/min; ASTM D638 |
| Tensile Strength, Yield | 88.0 MPa | 12800 psi | Type I, 5 mm/min; ASTM D638 |
| Elongation at Break | 100 % | 100 % | Type I, 5 mm/min; ASTM D638 |
| Tensile Modulus | 3.10 GPa | 450 ksi | 5 mm/min; ASTM D638 |
| Flexural Yield Strength | 124 MPa | 18000 psi | 2.6 mm/min, 100 mm span; ASTM D790 |
| Flexural Modulus | 3.10 GPa | 450 ksi | 2.6 mm/min, 100 mm span; ASTM D790 |
| Izod Impact, Notched | 1.49 J/cm | 2.79 ft-lb/in | ASTM D256 |
| 0.960 J/cm @Temperature -30.0 °C |
1.80 ft-lb/in @Temperature -22.0 °F |
ASTM D256 | |
| 20.29 J/cm @Thickness 3.20 mm |
38.01 ft-lb/in @Thickness 0.126 in |
ASTM D256 | |
| Dart Drop, Total Energy | 67.0 J | 49.4 ft-lb | Instrumented Impact Energy @ peak; ASTM D3763 |
| 58.0 J @Temperature -30.0 °C |
42.8 ft-lb @Temperature -22.0 °F |
Instrumented Impact Energy @ peak; ASTM D3763 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| OSU total heat release (2 minute test) | 10kW-min/m^2 | FAR 25.853 |
| OSU peak heat release rate (5 minute test) | 50kW/m^2 | FAR 25.853 |
Users viewing this material also viewed the following:
- Qualchem Danamid FGF-15 Polyamide 6, 15% Glass Fiber
- Polymer Resources NY66-IM2 Impact Modified Nylon 66
- LG Chemical LUMID GP2251AF PA6+GF25%, Flame Retardant
- LG Chemical LUPOL HG3200SK2 PP+MF20%, High Gloss
- Mo-Sci Corporation GL-0176 Barium-Titanate Glass Spheres
- Solvay Specialty Polymers Amodel® A-1133 HS Polyphthalamide (PPA), 33% Glass Fiber (Conditioned)
- Borealis Borcell™ HE1345 High Density Polyethylene Compound for Cellular Insulation of Telephone Singles
- Plenco 2408 Phenolic, Granular, Compression Molded
- Bales Mold Service AMS-2404-C, AMS-2405-B Mold Coating
- Asahi Kasei Tenac®-C LT350 Copolymer Acetal Resin
Copyright © lookpolymers.com All Rights Reserved