SABIC Innovative Plastics ULTEM D9065 PEI (Asia Pacific)
| Category | Polymer , Thermoplastic , Polyetherimide (PEI) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | ULTEM |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics ULTEM D9065 PEI (Asia Pacific).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Polyetherimide blend. Meets FAR 25.853 and OSU 65/65 with low toxicity, smoke, and flame evolution. ECO Conforming.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.32 g/cc | 1.32 g/cc | ASTM D792 |
| Linear Mold Shrinkage, Flow | 0.0050 - 0.0070 cm/cm @Thickness 3.20 mm |
0.0050 - 0.0070 in/in @Thickness 0.126 in |
SABIC Method |
| Linear Mold Shrinkage, Transverse | 0.0050 - 0.0070 cm/cm @Thickness 3.20 mm |
0.0050 - 0.0070 in/in @Thickness 0.126 in |
SABIC Method |
| Melt Flow | 15.6 g/10 min @Load 6.60 kg, Temperature 337 °C |
15.6 g/10 min @Load 14.6 lb, Temperature 639 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 88.0 MPa | 12800 psi | Type I, 5 mm/min; ASTM D638 |
| Tensile Strength, Yield | 88.0 MPa | 12800 psi | Type I, 5 mm/min; ASTM D638 |
| Elongation at Break | 100 % | 100 % | Type I, 5 mm/min; ASTM D638 |
| Tensile Modulus | 3.10 GPa | 450 ksi | 5 mm/min; ASTM D638 |
| Flexural Yield Strength | 124 MPa | 18000 psi | 2.6 mm/min, 100 mm span; ASTM D790 |
| Flexural Modulus | 3.10 GPa | 450 ksi | 2.6 mm/min, 100 mm span; ASTM D790 |
| Izod Impact, Notched | 1.49 J/cm | 2.79 ft-lb/in | ASTM D256 |
| 0.960 J/cm @Temperature -30.0 °C |
1.80 ft-lb/in @Temperature -22.0 °F |
ASTM D256 | |
| 20.29 J/cm @Thickness 3.20 mm |
38.01 ft-lb/in @Thickness 0.126 in |
ASTM D256 | |
| Dart Drop, Total Energy | 67.0 J | 49.4 ft-lb | Instrumented Impact Energy @ peak; ASTM D3763 |
| 58.0 J @Temperature -30.0 °C |
42.8 ft-lb @Temperature -22.0 °F |
Instrumented Impact Energy @ peak; ASTM D3763 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| OSU total heat release (2 minute test) | 10kW-min/m^2 | FAR 25.853 |
| OSU peak heat release rate (5 minute test) | 50kW/m^2 | FAR 25.853 |
Users viewing this material also viewed the following:
- Osprey Metals 410L Stainless Steel Powder (Grade 80% - 22)
- Ineos K44-15-186 Polyethylene Copolymer
- SABIC Innovative Plastics LNP THERMOCOMP DF006 PC (Europe-Africa-Middle East)
- SABIC Innovative Plastics LNP THERMOCOMP PF006S PA 6 (Europe-Africa-Middle East)
- A. Schulman SCHULAMID® 6 GF33RN 33% Glass Bead Reinforced, Industrial Grade Nylon 6
- Eastman Cadence™ GS1 Copolyester for film calendering
- DuPont™ Nomex® N102 Texturized Filament Yarn
- ExxonMobil 25 Mobil DTE 20 Series
- Bhansali Engineering Abstron IM-21 ABS Very High Rigidity Injection Molding Grade
- Bhansali Engineering Abstron SE-45 ABS Sheet Extrusion Grade
Copyright © lookpolymers.com All Rights Reserved