SABIC Innovative Plastics ULTEM CRS5201 PEI (Asia Pacific)
| Category | Polymer , Thermoplastic , Polyetherimide (PEI) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | ULTEM |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics ULTEM CRS5201 PEI (Asia Pacific).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
20% Glass fiber filled, standard flow Polyetherimide copolymer (Tg 225C) with enhanced chemical resistance to strong acids, bases, aromatics, and ketones. ECO Conforming, UL94 V0 and 5VA listing.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.42 g/cc | 1.42 g/cc | ASTM D792 |
| Melt Flow | 2.3 g/10 min @Load 6.60 kg, Temperature 337 °C |
2.3 g/10 min @Load 14.6 lb, Temperature 639 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 131 MPa | 19000 psi | Type I, 5 mm/min; ASTM D638 |
| Elongation at Break | 5.0 % | 5.0 % | Type I, 5 mm/min; ASTM D638 |
| Tensile Modulus | 6.89 GPa | 999 ksi | 5 mm/min; ASTM D638 |
| Flexural Yield Strength | 213 MPa | 30900 psi | 2.6 mm/min, 100 mm span; ASTM D790 |
| Flexural Modulus | 6.89 GPa | 999 ksi | 2.6 mm/min, 100 mm span; ASTM D790 |
| Izod Impact, Notched | 0.740 J/cm | 1.39 ft-lb/in | ASTM D256 |
| 4.80 J/cm @Thickness 3.20 mm |
8.99 ft-lb/in @Thickness 0.126 in |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 218 °C @Thickness 6.40 mm |
424 °F @Thickness 0.252 in |
unannealed; ASTM D648 |
| Glass Transition Temp, Tg | 225 °C | 437 °F | |
| UL RTI, Electrical | 105 °C | 221 °F | UL 746B |
| UL RTI, Mechanical with Impact | 105 °C | 221 °F | UL 746B |
| UL RTI, Mechanical without Impact | 105 °C | 221 °F | UL 746B |
| Flammability, UL94 | V-0 @Thickness 1.47 mm |
V-0 @Thickness 0.0579 in |
UL 94 |
| 5VA @Thickness 1.47 mm |
5VA @Thickness 0.0579 in |
UL 94 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Arc Resistance | 120 - 180 sec | 120 - 180 sec | Tungsten; ASTM D495 |
| Comparative Tracking Index | 100 - 175 V | 100 - 175 V | UL 746A |
| Hot Wire Ignition, HWI | 30 - 60 sec | 30 - 60 sec | UL 746A |
| High Amp Arc Ignition, HAI | 0.00 - 15 arcs | 0.00 - 15 arcs | UL 746A |
| High Voltage Arc-Tracking Rate, HVTR | >= 150 mm/min | >= 5.91 in/min | UL 746A |
Users viewing this material also viewed the following:
- Plaskolite Optix® CA - 75 UVT General Purpose Acrylic Resin
- SABIC Innovative Plastics LNP STAT-KON DE0069F PC
- Techmer ES HiFill® PA6/6 GF60 IM HS L 60% Glass Filled (Conditioned)
- SK Chemicals SKYTHANE® 175A S series Polyurethane
- A. Schulman POLYBATCH™ Brown 1281 Concentrate Based In Polyethylene
- Elgiloy® Co-Cr-Ni Alloy, Wire, 20% Cold Reduction
- AK Steel SAE J1392 040XLK or 040YLK, Grade 40 Cold Rolled Carbon Steel, High Strength Low Alloy Steel (HSLAS)
- A. Schulman ComAlloy E-16831B Polycarbonate, Electrically Conductive - Carbon Fiber Filled
Copyright © lookpolymers.com All Rights Reserved