Haynes Ultimet® alloy, plate, GMAW weld (short)

Category Metal , Nonferrous Metal , Cobalt Alloy , Superalloy
Manufacturer Haynes International, Inc.
Trade Name Ultimet®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Haynes Ultimet® alloy, plate, GMAW weld (short).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Co content as balance, excellent corrosion resistance, outstanding wear resistance, high tensile strength combined with excellent impact toughness and ductility. Ideal welding material with exceptional ductility and resistance to weld cracking, very easy to apply as an overlay, multiple layers appliable with little to no preheat. Applications include agitators, blenders, bolts, dies, extruders, fan blades, filters, glass plungers, nozzles, pumps, rolls, screw conveyors, and valve parts.Data provided by the manufacturer, Haynes International, Inc.
Physical Properties Metric English Comments
Density 8.47 g/cc
0.306 lb/in³
Mechanical Properties Metric English Comments
Tensile Strength, Ultimate 676 MPa

@Thickness 19.0 mm,
Temperature 538 °C
 98000 psi

@Thickness 0.750 in,
Temperature 1000 °F
786 MPa

@Thickness 12.7 mm,
Temperature 538 °C
 114000 psi

@Thickness 0.500 in,
Temperature 1000 °F
800 MPa

@Thickness 19.0 mm,
Temperature 260 °C
 116000 psi

@Thickness 0.750 in,
Temperature 500 °F
834 MPa

@Thickness 12.7 mm,
Temperature 20.0 °C
 121000 psi

@Thickness 0.500 in,
Temperature 68.0 °F
834 MPa

@Thickness 12.7 mm,
Temperature 260 °C
 121000 psi

@Thickness 0.500 in,
Temperature 500 °F
848 MPa

@Thickness 19.0 mm,
Temperature 20.0 °C
 123000 psi

@Thickness 0.750 in,
Temperature 68.0 °F
Tensile Strength, Yield 310 MPa

@Thickness 19.0 mm,
Temperature 538 °C
 45000 psi

@Thickness 0.750 in,
Temperature 1000 °F
 0.2% offset
365 MPa

@Thickness 12.7 mm,
Temperature 538 °C
 52900 psi

@Thickness 0.500 in,
Temperature 1000 °F
 0.2% offset
427 MPa

@Thickness 19.0 mm,
Temperature 260 °C
 61900 psi

@Thickness 0.750 in,
Temperature 500 °F
 0.2% offset
448 MPa

@Thickness 12.7 mm,
Temperature 260 °C
 65000 psi

@Thickness 0.500 in,
Temperature 500 °F
 0.2% offset
593 MPa

@Thickness 19.0 mm,
Temperature 20.0 °C
 86000 psi

@Thickness 0.750 in,
Temperature 68.0 °F
 0.2% offset
676 MPa

@Thickness 12.7 mm,
Temperature 20.0 °C
 98000 psi

@Thickness 0.500 in,
Temperature 68.0 °F
 0.2% offset
Elongation at Break 6.0 %

@Thickness 12.7 mm
 6.0 %

@Thickness 0.500 in
 in 50.8 mm
10 %

@Thickness 19.0 mm
 10 %

@Thickness 0.750 in
 in 50.8 mm
19 %

@Thickness 12.7 mm,
Temperature 260 °C
 19 %

@Thickness 0.500 in,
Temperature 500 °F
 in 50.8 mm
20 %

@Thickness 19.0 mm,
Temperature 260 °C
 20 %

@Thickness 0.750 in,
Temperature 500 °F
 in 50.8 mm
26 %

@Thickness 19.0 mm,
Temperature 538 °C
 26 %

@Thickness 0.750 in,
Temperature 1000 °F
 in 50.8 mm
28 %

@Thickness 12.7 mm,
Temperature 538 °C
 28 %

@Thickness 0.500 in,
Temperature 1000 °F
 in 50.8 mm
Modulus of Elasticity 180 GPa

@Temperature 649 °C
 26100 ksi

@Temperature 1200 °F
 (heat treated at 1121°C (2050°F), water quenched plate)
189 GPa

@Temperature 538 °C
 27400 ksi

@Temperature 1000 °F
 (heat treated at 1121°C (2050°F), water quenched plate)
197 GPa

@Temperature 427 °C
 28600 ksi

@Temperature 801 °F
 (heat treated at 1121°C (2050°F), water quenched plate)
206 GPa

@Temperature 316 °C
 29900 ksi

@Temperature 601 °F
 (heat treated at 1121°C (2050°F), water quenched plate)
215 GPa

@Temperature 204 °C
 31200 ksi

@Temperature 399 °F
 (heat treated at 1121°C (2050°F), water quenched plate)
Charpy Impact 127 J
93.7 ft-lb
V Notch
Thermal Properties Metric English Comments
CTE, linear 14.0 µm/m-°C

@Temperature 26.0 - 316 °C
 7.78 µin/in-°F

@Temperature 78.8 - 601 °F
14.5 µm/m-°C

@Temperature 26.0 - 427 °C
 8.06 µin/in-°F

@Temperature 78.8 - 801 °F
14.8 µm/m-°C

@Temperature 26.0 - 538 °C
 8.22 µin/in-°F

@Temperature 78.8 - 1000 °F
15.1 µm/m-°C

@Temperature 26.0 - 649 °C
 8.39 µin/in-°F

@Temperature 78.8 - 1200 °F
15.9 µm/m-°C

@Temperature 26.0 - 760 °C
 8.83 µin/in-°F

@Temperature 78.8 - 1400 °F
16.4 µm/m-°C

@Temperature 26.0 - 871 °C
 9.11 µin/in-°F

@Temperature 78.8 - 1600 °F
16.9 µm/m-°C

@Temperature 26.0 - 982 °C
 9.39 µin/in-°F

@Temperature 78.8 - 1800 °F
Specific Heat Capacity 0.456 J/g-°C

@Temperature 23.0 °C
 0.109 BTU/lb-°F

@Temperature 73.4 °F
0.470 J/g-°C

@Temperature 100 °C
 0.112 BTU/lb-°F

@Temperature 212 °F
0.482 J/g-°C

@Temperature 200 °C
 0.115 BTU/lb-°F

@Temperature 392 °F
0.504 J/g-°C

@Temperature 300 °C
 0.120 BTU/lb-°F

@Temperature 572 °F
0.525 J/g-°C

@Temperature 400 °C
 0.125 BTU/lb-°F

@Temperature 752 °F
0.545 J/g-°C

@Temperature 500 °C
 0.130 BTU/lb-°F

@Temperature 932 °F
0.573 J/g-°C

@Temperature 600 °C
 0.137 BTU/lb-°F

@Temperature 1110 °F
Thermal Conductivity 12.3 W/m-K

@Temperature 23.0 °C
 85.4 BTU-in/hr-ft²-°F

@Temperature 73.4 °F
13.8 W/m-K

@Temperature 100 °C
 95.8 BTU-in/hr-ft²-°F

@Temperature 212 °F
15.6 W/m-K

@Temperature 200 °C
 108 BTU-in/hr-ft²-°F

@Temperature 392 °F
17.5 W/m-K

@Temperature 300 °C
 121 BTU-in/hr-ft²-°F

@Temperature 572 °F
19.4 W/m-K

@Temperature 400 °C
 135 BTU-in/hr-ft²-°F

@Temperature 752 °F
21.5 W/m-K

@Temperature 500 °C
 149 BTU-in/hr-ft²-°F

@Temperature 932 °F
23.9 W/m-K

@Temperature 600 °C
 166 BTU-in/hr-ft²-°F

@Temperature 1110 °F
Melting Point 1332 - 1354 °C
2430 - 2469 °F
Solidus 1332 °C
2430 °F
Liquidus 1354 °C
2469 °F
Component Elements Properties Metric English Comments
Carbon, C 0.060 %
0.060 %
Chromium, Cr 26 %
26 %
Cobalt, Co 54 %
54 %
Iron, Fe 3.0 %
3.0 %
Manganese, Mn 0.80 %
0.80 %
Molybdenum, Mo 5.0 %
5.0 %
Nickel, Ni 9.0 %
9.0 %
Nitrogen, N 0.080 %
0.080 %
Silicon, Si 0.30 %
0.30 %
Tungsten, W 2.0 %
2.0 %
Electrical Properties Metric English Comments
Electrical Resistivity 0.0000870 ohm-cm

@Temperature 23.0 °C
 0.0000870 ohm-cm

@Temperature 73.4 °F
0.0000890 ohm-cm

@Temperature 100 °C
 0.0000890 ohm-cm

@Temperature 212 °F
0.0000930 ohm-cm

@Temperature 200 °C
 0.0000930 ohm-cm

@Temperature 392 °F
0.0000960 ohm-cm

@Temperature 300 °C
 0.0000960 ohm-cm

@Temperature 572 °F
0.000100 ohm-cm

@Temperature 400 °C
 0.000100 ohm-cm

@Temperature 752 °F
0.000103 ohm-cm

@Temperature 500 °C
 0.000103 ohm-cm

@Temperature 932 °F
0.000105 ohm-cm

@Temperature 600 °C
 0.000105 ohm-cm

@Temperature 1110 °F