SABIC Innovative Plastics ULTEM ATX200F PEI+PCE (Asia Pacific)
| Category | Polymer , Thermoplastic , Polyetherimide (PEI) , Polyetherimide (PEI) + PCE |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | ULTEM |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics ULTEM ATX200F PEI+PCE (Asia Pacific).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
High flow Polyetherimide blend. ECO Conforming, UL94 V0 Listing. US FDA Food Contact compliant.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.26 g/cc | 1.26 g/cc | ASTM D792 |
| Linear Mold Shrinkage, Flow | 0.0050 - 0.0070 cm/cm @Thickness 3.20 mm |
0.0050 - 0.0070 in/in @Thickness 0.126 in |
SABIC Method |
| Melt Flow | 24 g/10 min @Load 6.60 kg, Temperature 337 °C |
24 g/10 min @Load 14.6 lb, Temperature 639 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 96.0 MPa | 13900 psi | Type I, 5 mm/min; ASTM D638 |
| Elongation at Break | 70 % | 70 % | Type I, 5 mm/min; ASTM D638 |
| Flexural Yield Strength | 144 MPa | 20900 psi | 2.6 mm/min, 100 mm span; ASTM D790 |
| Flexural Modulus | 3.17 GPa | 460 ksi | 2.6 mm/min, 100 mm span; ASTM D790 |
| Izod Impact, Notched | 0.530 J/cm | 0.993 ft-lb/in | ASTM D256 |
| 26.7 J/cm @Thickness 3.20 mm |
50.0 ft-lb/in @Thickness 0.126 in |
ASTM D256 | |
| Izod Impact, Unnotched | 20.82 J/cm | 39.00 ft-lb/in | ASTM D4812 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 190 °C @Thickness 6.40 mm |
374 °F @Thickness 0.252 in |
unannealed; ASTM D648 |
| UL RTI, Electrical | 115 °C | 239 °F | UL 746B |
| UL RTI, Mechanical with Impact | 115 °C | 239 °F | UL 746B |
| UL RTI, Mechanical without Impact | 115 °C | 239 °F | UL 746B |
| Flammability, UL94 | V-2 @Thickness 0.760 mm |
V-2 @Thickness 0.0299 in |
UL 94 |
| V-0 @Thickness 1.49 mm |
V-0 @Thickness 0.0587 in |
UL 94 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Comparative Tracking Index | 100 - 175 V | 100 - 175 V | UL 746A |
| Hot Wire Ignition, HWI | >= 120 sec | >= 120 sec | UL 746A |
| High Amp Arc Ignition, HAI | 0.00 - 15 arcs | 0.00 - 15 arcs | UL 746A |
Users viewing this material also viewed the following:
- NatureWorks® Ingeo™ 6252D Meltblown Fiber Grade Biopolymer
- GrafTech GRAFOIL® GHH Standard Internal Combustion Laminate, Metal Reinforced
- SABIC Innovative Plastics LNP LUBRICOMP IL004 PA 6/12 (Asia Pacific)
- Sibur 153-02K Superior Quality Polyethylene for Cable Production
- Williams Advanced Alloys Wambraze™ WB1025 Solder
- Zig Sheng Industrial ZISAMIDE® TP6603 Nylon 6
- DuPont Performance Polymers Hytrel® 7246HS NC010 Polyester Elastomer TPC-ET (Unverified Data**)
- BASF Polystyrol® 158 K Polystyrene (Global)
- SABIC Innovative Plastics LNP LUBRICOMP DFL369XF PC (Asia Pacific)
Copyright © lookpolymers.com All Rights Reserved