SABIC Innovative Plastics LNP Colorcomp DX98735 PC

Category Polymer , Thermoplastic , Polycarbonate (PC)
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name LNP Colorcomp
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics LNP Colorcomp DX98735 PC.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
LNP COLORCOMP* DX98735 is a compound based on Polycarbonate resin containing Proprietary Fillers.This data was supplied by SABIC-IP for the Americas region.
Physical Properties Metric English Comments
Specific Gravity 1.21 g/cc
1.21 g/cc
ASTM D 792
Density 1.21 g/cc
0.0437 lb/in³
ASTM D 792
Moisture Absorption at Equilibrium 0.21 %
0.21 %
23°C / 50% RH; ISO 62
0.14 %

@Time 86400 sec
 0.14 %

@Time 24.0 hour
 50% RH; ASTM D 570
Linear Mold Shrinkage, Flow 0.0060 - 0.0080 cm/cm

@Time 86400 sec
 0.0060 - 0.0080 in/in

@Time 24.0 hour
 ASTM D 955
Linear Mold Shrinkage, Transverse 0.0080 - 0.010 cm/cm

@Time 86400 sec
 0.0080 - 0.010 in/in

@Time 24.0 hour
 ASTM D 955
Mechanical Properties Metric English Comments
Tensile Strength at Break 54.0 MPa
7830 psi
Type I, 5 mm/min; ASTM D 638
58.0 MPa
8410 psi
5 mm/min; ISO 527
Tensile Strength, Yield 62.0 MPa
8990 psi
5 mm/min; ISO 527
64.0 MPa
9280 psi
Type I, 5 mm/min; ASTM D 638
Elongation at Break 66 %
66 %
Type I, 5 mm/min; ASTM D 638
167 %
167 %
5 mm/min; ISO 527
Elongation at Yield 6.2 %
6.2 %
5 mm/min; ISO 527
6.3 %
6.3 %
Type I, 5 mm/min; ASTM D 638
Tensile Modulus 2.24 GPa
325 ksi
1 mm/min; ISO 527
2.33 GPa
338 ksi
50 mm/min; ASTM D 638
Flexural Strength 80.0 MPa
11600 psi
ISO 178
Flexural Modulus 2.28 GPa
331 ksi
2 mm/min; ISO 178
2.46 GPa
357 ksi
1.3 mm/min, 50 mm span; ASTM D 790
Izod Impact, Notched 1.01 J/cm

@Temperature 23.0 °C
 1.89 ft-lb/in

@Temperature 73.4 °F
 ASTM D 256
Izod Impact, Unnotched 25.2 J/cm

@Temperature 23.0 °C
 47.2 ft-lb/in

@Temperature 73.4 °F
 ASTM D 4812
Izod Impact, Notched (ISO) 9.00 kJ/m²

@Temperature 23.0 °C
 4.28 ft-lb/in²

@Temperature 73.4 °F
 80*10*4; ISO 180/1A
Izod Impact, Unnotched (ISO) 212 kJ/m²

@Temperature 23.0 °C
 101 ft-lb/in²

@Temperature 73.4 °F
 80*10*4; ISO 180/1U
Impact Test 77.0 J
56.8 ft-lb
Multiaxial Impact; ISO 6603
61.0 J

@Temperature 23.0 °C
 45.0 ft-lb

@Temperature 73.4 °F
 Instrumented Impact Total Energy; ASTM D 3763
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 67.0 µm/m-°C

@Temperature -30.0 - 30.0 °C
 37.2 µin/in-°F

@Temperature -22.0 - 86.0 °F
 ASTM D 696
CTE, linear, Transverse to Flow 69.0 µm/m-°C

@Temperature -30.0 - 30.0 °C
 38.3 µin/in-°F

@Temperature -22.0 - 86.0 °F
 ASTM D 696
Deflection Temperature at 0.46 MPa (66 psi) 138 °C
280 °F
Flatw 80*10*4 sp=64mm; ISO 75/Bf
139 °C

@Thickness 3.20 mm
 282 °F

@Thickness 0.126 in
 unannealed; ASTM D 648
Deflection Temperature at 1.8 MPa (264 psi) 126 °C
259 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af
132 °C

@Thickness 3.20 mm
 270 °F

@Thickness 0.126 in
 unannealed; ASTM D 648