LyondellBasell Petrothene® GA594189 Linear Low Density Polyethylene, Injection Molding Grade
| Category | Polymer , Thermoplastic , Polyethylene (PE) , LLDPE , Linear Low Density Polyethylene (LLDPE), Injection Molded |
| Manufacturer | LyondellBasell (former Equistar) |
| Trade Name | Petrothene® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | LyondellBasell Petrothene® GA594189 Linear Low Density Polyethylene, Injection Molding Grade.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
PETROTHENE GA594189 is a pelletized LLDPE copolymer resin for injection molding thin-walled items requiring high flow and short cycle times. GA594189 exhibits excellent flow, warp resistance and surface appearance.Specific recommendations for processing GA594189 can only be made when the processing conditions, equipment and end use are known. For further suggestions, please contact your Equistar sales representative.This product is from the former Equistar product line.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.933 g/cc | 0.0337 lb/in³ | ASTM D1505 |
| Melt Flow | 140 g/10 min | 140 g/10 min | ASTM D1238 |
| Spiral Flow | 67.8 cm | 26.7 in | Equistar test |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore D | 61 | 61 | ASTM D2240 |
| Tensile Strength at Break | 17.3 MPa | 2510 psi | ASTM D638 |
| Tensile Strength, Yield | 17.3 MPa | 2510 psi | 2"/min; ASTM D638 |
| Elongation at Yield | 9.8 % | 9.8 % | 2"/min; ASTM D638 |
| 1% Secant Modulus | 669 MPa | 97000 psi | 0.5"/min; ASTM D790 |
| 2% Secant Modulus | 0.572 GPa | 83.0 ksi | 0.5"/min; ASTM D790 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 52.0 °C | 126 °F | ASTM D648 |
| Vicat Softening Point | 91.0 °C | 196 °F | ASTM D1525 |
| Brittleness Temperature | <= -27.0 °C | <= -16.6 °F | F<SUB>50</SUB>; ASTM D746 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 177 °C | 350 °F | |
| Middle Barrel Temperature | 191 °C | 375 °F | |
| Front Barrel Temperature | 204 °C | 400 °F | |
| Nozzle Temperature | 204 °C | 400 °F |
Users viewing this material also viewed the following:
- Potters Industries Q-Cel® 7019 Hollow Engineered Glass Microspheres
- Abatron AboCast 8101-3/AboCure 8101-3 Epoxy (discontinued **)
- Ravago Manufacturing Americas Hylon® N1013L Nylon 6/6 (Cond) (discontinued **)
- Heatbath/Park Durastrip 1500 Cleaning Salt
- Materion Beryllium Copper Alloy 10 Plate & Rolled Bar; A (TB00) Temper; All Thicknesses (UNS C17500)
- Braskem ML2400N LLDPE Injection Molding Polyethylene
- Adell AT-34 Nylon 66, 20% Glass Reinforced; Impact Modified
- Colorite Polymers 7900FR General Purpose Vinyl Compound
- Resinlab® EP1112 Black Electronic Grade Epoxy Encapsulant
Copyright © lookpolymers.com All Rights Reserved