BASF Procom® D 1189 Polypropylene
| Category | Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene, Molded |
| Manufacturer | BASF |
| Trade Name | Procom® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | BASF Procom® D 1189 Polypropylene.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Data was collected by ISO methods and provided by BASF.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.04 g/cc | 0.0376 lb/in³ | |
| Linear Mold Shrinkage, Flow | 0.015 cm/cm | 0.015 in/in |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 29.0 MPa | 4210 psi | |
| Elongation at Break | 20 % | 20 % | |
| Tensile Modulus | 2.00 GPa | 290 ksi | |
| Charpy Impact Unnotched | 3.50 J/cm² | 16.7 ft-lb/in² | |
| 1.00 J/cm² @Temperature -30.0 °C |
4.76 ft-lb/in² @Temperature -22.0 °F |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 50.0 µm/m-°C @Temperature 20.0 °C |
27.8 µin/in-°F @Temperature 68.0 °F |
|
| Deflection Temperature at 0.46 MPa (66 psi) | 115 °C | 239 °F | |
| Deflection Temperature at 1.8 MPa (264 psi) | 70.0 °C | 158 °F | |
| Vicat Softening Point | 100 °C | 212 °F |
Users viewing this material also viewed the following:
- Meehanite K-325 Austempered Ductile Iron
- Mitsubishi Xantar® C CM 206 U Polycarbonate/ABS Blend
- Grupo Repol Dinalon® A1S25 B30 PA66 30% Glass Beads
- HP Alloys Alloy C-276, 10% Cold Worked
- SABIC Innovative Plastics Xenoy® X6800BM PBT (Asia Pacific)
- Loctite® 3301 Light Cure Acrylic Adhesive
- TSE Industries Millathane® 5004 Millable Polyurethane Elastomer with 10 PHR Tricresyl Phosphate
- Akro-Plastic Akromid® A3 GM 10/20 S1 PA, 10% Glass Filled, 20% Mineral Filled, Cold-Impact Resistant (discont
Copyright © lookpolymers.com All Rights Reserved