SABIC Innovative Plastics ULTEM 1010K PEI
| Category | Polymer , Thermoplastic , Polyetherimide (PEI) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | ULTEM |
| Port | Ningbo port, China |
| Download PDF |
SABIC Innovative Plastics ULTEM 1010K PEI.pdf
|
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Transparent, high flow Polyetherimide (Tg 217C). ECO Conforming.
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.27 g/cc | 1.27 g/cc | ASTM D792 |
| Density | 1.27 g/cc | 0.0459 lb/in³ | ISO 1183 |
| Moisture Absorption | 0.700 % | 0.700 % | 23°C / 50% RH; ISO 62 |
| Water Absorption at Saturation | 1.25 % | 1.25 % | ISO 62 |
| Linear Mold Shrinkage, Flow | 0.0050 - 0.0070 cm/cm | 0.0050 in/in | on Tensile Bar; SABIC Method |
|
0.0050
- 0.0070
cm/cm <br>@Thickness 3.20 mm
|
0.0050
in/in <br>@Thickness 0.126 in
|
SABIC Method | |
| Linear Mold Shrinkage, Transverse |
0.0050
- 0.0070
cm/cm <br>@Thickness 3.20 mm
|
0.0050
in/in <br>@Thickness 0.126 in
|
SABIC Method |
| Melt Flow |
17.8
g/10 min <br>@Load 6.60 kg,<br> Temperature 337 °C
|
17.8
g/10 min <br>@Load 14.6 lb,<br> Temperature 639 °F
|
ASTM D1238 |
| Melt Index of Compound |
25
g/10 min <br>@Load 5.00 kg,<br> Temperature 360 °C
|
25
g/10 min <br>@Load 11.0 lb,<br> Temperature 680 °F
|
MVR [cm^3/10 min]; ISO 1133 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 85.0 MPa | 12300 psi | 5 mm/min; ISO 527 |
| 105 MPa | 15200 psi | Type I, 5 mm/min; ASTM D638 | |
| Tensile Strength, Yield | 105 MPa | 15200 psi | 5 mm/min; ISO 527 |
| 110 MPa | 16000 psi | Type I, 5 mm/min; ASTM D638 | |
| Elongation at Break | 60 % | 60 % | Type I, 5 mm/min; ASTM D638 |
| 60 % | 60 % | 5 mm/min; ISO 527 | |
| Elongation at Yield | 6.0 % | 6.0 % | 5 mm/min; ISO 527 |
| 7.0 % | 7.0 % | Type I, 5 mm/min; ASTM D638 | |
| Tensile Modulus | 3.20 GPa | 464 ksi | 1 mm/min; ISO 527 |
| 3.59 GPa | 521 ksi | 5 mm/min; ASTM D638 | |
| Flexural Yield Strength | 160 MPa | 23200 psi | 2 mm/min; ISO 178 |
| 165 MPa | 23900 psi | 1.3 mm/min, 50 mm span; ASTM D790 | |
| Flexural Modulus | 3.30 GPa | 479 ksi | 2 mm/min; ISO 178 |
| 3.52 GPa | 511 ksi | 1.3 mm/min, 50 mm span; ASTM D790 | |
| Izod Impact, Notched | 0.320 J/cm | 0.599 ft-lb/in | ASTM D256 |
|
0.350
J/cm <br>@Temperature -30.0 °C
|
0.656
ft-lb/in <br>@Temperature -22.0 °F
|
ASTM D256 | |
|
11.75
J/cm <br>@Thickness 3.20 mm
|
22.01
ft-lb/in <br>@Thickness 0.126 in
|
ASTM D256 | |
| Izod Impact, Unnotched | 13.35 J/cm | 25.01 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 5.00 kJ/m² | 2.38 ft-lb/in² | 80*10*4; ISO 180/1A |
|
5.00
kJ/m² <br>@Temperature -30.0 °C
|
2.38
ft-lb/in² <br>@Temperature -22.0 °F
|
80*10*4; ISO 180/1A | |
| Izod Impact, Unnotched (ISO) | NB | NB | 80*10*4; ISO 180/1U |
|
NB
<br>@Temperature -30.0 °C
|
NB <br>@Temperature -22.0 °F
|
80*10*4; ISO 180/1U | |
| Charpy Impact, Notched | 0.300 J/cm² | 1.43 ft-lb/in² | Edgew 80*10*4 sp=62mm; ISO 179/1eA |
| Dart Drop, Total Energy |
33.0
J <br>@Temperature 23.0 °C
|
24.3
ft-lb <br>@Temperature 73.4 °F
|
ASTM D3763 |
| Optical Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow |
50.0
µm/m-°C <br>@Temperature 23.0 - 150 °C
|
27.8
µin/in-°F <br>@Temperature 73.4 - 302 °F
|
ISO 11359-2 |
|
55.0
µm/m-°C <br>@Temperature -40.0 - 150 °C
|
30.6
µin/in-°F <br>@Temperature -40.0 - 302 °F
|
ASTM E 831 | |
| CTE, linear, Transverse to Flow |
50.0
µm/m-°C <br>@Temperature 23.0 - 150 °C
|
27.8
µin/in-°F <br>@Temperature 73.4 - 302 °F
|
ISO 11359-2 |
|
55.0
µm/m-°C <br>@Temperature -40.0 - 150 °C
|
30.6
µin/in-°F <br>@Temperature -40.0 - 302 °F
|
ASTM E 831 | |
| Deflection Temperature at 0.46 MPa (66 psi) | 200 °C | 392 °F | Edgew 120*10*4 sp=100mm; ISO 75/Be |
|
205
°C <br>@Thickness 3.20 mm
|
401
°F <br>@Thickness 0.126 in
|
unannealed; ASTM D648 | |
|
207
°C <br>@Thickness 6.40 mm
|
405
°F <br>@Thickness 0.252 in
|
unannealed; ASTM D648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 190 °C | 374 °F | Edgew 120*10*4 sp=100mm; ISO 75/Ae |
| 193 °C | 379 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af | |
|
197
°C <br>@Thickness 3.20 mm
|
387
°F <br>@Thickness 0.126 in
|
unannealed; ASTM D648 | |
|
199
°C <br>@Thickness 6.40 mm
|
390
°F <br>@Thickness 0.252 in
|
unannealed; ASTM D648 | |
| Vicat Softening Point | 211 °C | 412 °F | Rate B/50; ISO 306 |
| 212 °C | 414 °F | Rate B/120; ISO 306 | |
| 215 °C | 419 °F | Rate A/50; ISO 306 | |
| 219 °C | 426 °F | Rate B/50; ASTM D1525 | |
| Glass Transition Temp, Tg | 217 °C | 423 °F |
| Component Elements Properties | Metric | English | Comments |
|---|---|---|---|
| Transmission, Visible | 90 % | 90 % | transparent; thickness not quantified |
| Compliance Properties | Metric | English | Comments |
|---|---|---|---|
| Ball Pressure Test, 125°C +/- 2°C | Passes | IEC 60695-10-2 |
Users viewing this material also viewed:
- Nye Lubricants UniFlor 8170U (UF) Synthetic Oil
- Ravago Manufacturing Americas Hylon® N2033HL Nylon 6 (DAM)
- Ineos Nova Zylar® 220 High Performance Styrenic, Acrylic Copolymer (discontinued **)
- Cookson Group Plaskon® 3100 Novolac Epoxy Molding Compound (discontinued **)
- Wellman Wellamid® MRGF25/15 42H-BKJA6A Nylon 6, 25% Mineral and 15% Glass Reinforced
- A. Schulman PAPERMATCH® T-4228-8 Specialty Masterbatch
- DuPont Performance Polymers VESPEL TP-8792 Polyimide
- Albis Plastics Tedur® L 9511 PPS, 45% Glass Fiber
- Axiall 3240 Rigid PVC, Extrusion
Copyright © lookpolymers.com All Rights Reserved