Chevron Phillips MarFlex® 5619 LDPE Shrink and Heavy Duty Packaging Film Resin

Category	Polymer , Film , Thermoplastic , Polyethylene (PE) , LDPE , Low Density Polyethylene (LDPE), Film Grade
Manufacturer	Chevron Phillips Chemical Company LP
Trade Name	MarFlex®
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Chevron Phillips MarFlex® 5619 LDPE Shrink and Heavy Duty Packaging Film Resin.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Resin Type: HomopolymerCharacteristics: Excellent Tensile and Impact Strength, Good Abrasion and Tear Resistance, Good Resistance to Blocking, Wide Range of Shrinkage Characteristics, Low Slip, Low Antiblock, Good ESCRApplications:Pallet Shrink, Heavy Duty PackagingProcessing Conditions: Extruder 6.35 cm. Screw L/D Ratio 24:1. Die Opening 0.0762 cm. Blow-Up Ratio 3:1.Film properties below based on film thickness of 76 µm.Data provided by Chevron Chemical.

Physical Properties	Metric	English	Comments
Density	0.923 g/cc	0.0333 lb/in³	ASTM D1505
Melt Flow	0.40 g/10 min	0.40 g/10 min	Condition E; ASTM D 1238

Mechanical Properties	Metric	English	Comments
Secant Modulus, MD	0.170 GPa	24.7 ksi	ASTM D882
Secant Modulus, TD	0.180 GPa	26.1 ksi	ASTM D882
Coefficient of Friction	0.10	0.10	ASTM D1894
Dart Drop	2.80 g/micron	71.1 g/mil	F<sub>50</sub>; 1.5 in. dart/26 in. drop height; ASTM D 1709

Optical Properties	Metric	English	Comments
Haze	10 %	10 %	ASTM D2457
Gloss	57 %	57 %	at 45°. ASTM D 2457
	90 %	90 %	at 60°. ASTM D 2457

Processing Properties	Metric	English	Comments
Melt Temperature	210 °C	410 °F