SABIC Innovative Plastics SABIC PPCOMPOUND 55T1040 PP
| Category | Polymer , Thermoplastic , Polypropylene (PP) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | SABIC PPCOMPOUND |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics SABIC PPCOMPOUND 55T1040 PP.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
SABIC® PPcompound 55T1040 is a general purpose, talc filled, heat stabilized copolymer polypropylene compound. This compound exhibits very high impact and high rigidity, and is suitable for injection molding applications. The IMDS ID is 278629571
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.27 g/cc | 1.27 g/cc | ASTM D792 |
| Density | 1.27 g/cc | 0.0459 lb/in³ | ISO 1183 |
| Melt Flow | 3.0 g/10 min @Load 2.16 kg, Temperature 230 °C |
3.0 g/10 min @Load 4.76 lb, Temperature 446 °F |
ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 14.0 MPa | 2030 psi | 50 mm/min, 1A; ISO 527 |
| Tensile Strength, Yield | 20.0 MPa | 2900 psi | 50 mm/min; ISO 527 |
| Elongation at Break | 10.8 % | 10.8 % | 50 mm/min; ISO 527 |
| Elongation at Yield | 3.0 % | 3.0 % | 50 mm/min; ISO 527 |
| Tensile Modulus | 2.45 GPa | 355 ksi | 1 mm/min; ISO 527 |
| Flexural Modulus | 3.27 GPa | 474 ksi | 2 mm/min, 64mm span; ISO 178 |
| Izod Impact, Notched (ISO) | 7.00 kJ/m² | 3.33 ft-lb/in² | 80*10*4mm, Cut; ISO 180/1A |
| 2.00 kJ/m² @Temperature -30.0 °C |
0.952 ft-lb/in² @Temperature -22.0 °F |
80*10*4mm, Cut; ISO 180/1A | |
| Charpy Impact, Notched | 0.800 J/cm² | 3.81 ft-lb/in² | 80*10*4mm, Cut; ISO 179/1eA |
| 0.200 J/cm² @Temperature -30.0 °C |
0.952 ft-lb/in² @Temperature -22.0 °F |
80*10*4mm, Cut; ISO 179/1eA | |
| Dart Drop, Total Energy | 10.0 J @Temperature 23.0 °C |
7.38 ft-lb @Temperature 73.4 °F |
Instrumented Impact Energy @ peak, 6.6 m/s; ASTM D3763 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 70.0 °C | 158 °F | 80*10*4mm, Cut; ISO 75-1&2 |
| Deflection Temperature at 1.8 MPa (264 psi) | 124 °C | 255 °F | 80*10*4mm, Cut; ISO 75-1&2 |
| Vicat Softening Point | 142 °C | 288 °F | 10N, 50°C/hr; ISO 306 |
Users viewing this material also viewed the following:
- NYCOA 2263 Copolymer Nylon Alloy
- SABIC Innovative Plastics Cycoloy® C4220K PC+ABS (Asia Pacific)
- Polymer Resources PC/ABS-FR1 Flame Retardant PC/ABS Alloy
- PolyOne Geon™ Vinyl Flexible B5500 Polyvinyl Chloride, Flexible (PVC, Flexible)
- Huntsman HY 5200 Aromatic Amine
- Sylvin Technologies 9915-70 Natural PVC Molding Compound
- Teknor Apex Flexalloy® 3500-75NT Polyvinyl Chloride Elastomer
- Teknor Apex Monprene® MP-1775D Thermoplastic Elastomer
- Eastman Tenite Propionate 350E0096912 Natural, Trsp Cellulose Acetate Propionate
- Arlon 55359R062 62 mil Uncured/Cured Silicone Rubber with Fiberglass Substrate
Copyright © lookpolymers.com All Rights Reserved