- Polyram PlusTek RA303G3 Nylon 66 for Injection Molding, 15% Glass Fiber Reinforced, Heat Stabilized, Hydrolysis Resistant
Polyram PlusTek RA303G3 Nylon 66 for Injection Molding, 15% Glass Fiber Reinforced, Heat Stabilized, Hydrolysis Resistant
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, 20% Glass Fiber Filled |
| Manufacturer | Polyram |
| Trade Name | PlusTek |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Polyram PlusTek RA303G3 Nylon 66 for Injection Molding, 15% Glass Fiber Reinforced, Heat Stabilized, Hydrolysis Resistant.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
15% Glass fiber reinforced, heat stabilized and hydrolysis resistant Nylon 66 for injection molding applications.Information provided by Polyram.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.23 g/cc | 0.0444 lb/in³ | ISO 1183 |
| Water Absorption at Saturation | 0.0090 % | 0.0090 % | ISO 62 |
| Linear Mold Shrinkage | 0.0040 - 0.0050 cm/cm | 0.0040 - 0.0050 in/in | ISO 2577 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | >= 100 MPa | >= 14500 psi | ISO 527 |
| Elongation at Break | >= 3.0 % | >= 3.0 % | ISO 527 |
| Flexural Strength | >= 155 MPa | >= 22500 psi | ISO 178 |
| Flexural Modulus | >= 4.00 GPa | >= 580 ksi | ISO 178 |
| Izod Impact, Notched (ISO) | >= 4.50 kJ/m² | >= 2.14 ft-lb/in² | ISO 180 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 256 °C | 493 °F | ISO 11357 |
| Deflection Temperature at 0.46 MPa (66 psi) | >= 200 °C | >= 392 °F | ISO 75 |
| Deflection Temperature at 1.8 MPa (264 psi) | >= 180 °C | >= 356 °F | ISO 75 |
| Flammability, UL94 | HB @Thickness 3.00 mm |
HB @Thickness 0.118 in |
Users viewing this material also viewed the following:
- Polymax® Maxelast® A9850 TPE, ABS/PC Overmold
- Inno-Comp INNOPOL® CS 1-3130 30% Talc-Filled Polypropylene Homopolymer
- Solvay Specialty Polymers AvaSpire® AV-651 Polyaryletherketone (PAEK)
- Saint-Gobain Rulon® 125 Bearing/Seal PTFE
- SABIC Innovative Plastics LNP THERMOCOMP MF008S PP
- Dow DOWLEX™ 2045A Linear Low Density Polyethylene, Blown Film Grade
- Techmer Lehvoss Compounds Luvotech™ J-4/35 NAT PA6/12 (discontinued **)
- Rogers Corporation Bisco® A2 R 1.0 Engineered Solid Silicone Mass Layer, Fiberglass Reinforced Sound Barrier
- DuPont Performance Polymers Crastin® S600F10 NC010 PBT (Unverified Data**)
Copyright © lookpolymers.com All Rights Reserved