SABIC Innovative Plastics Noryl PX5622 PPE+PS

Category Polymer , Thermoplastic , Polyphenylene Ether/PPO , Polystyrene (PS)
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name Noryl
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics Noryl PX5622 PPE+PS.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
PPE+PS blend. Unfilled. Non-brominated, non-chlorinated FR system. Good flow and surface aesthetics. UL94 V0/5VA/5VB. RTI Elec/Imp/Str 65. Suitable for E/E market indoor/outdoor applications.This data was supplied by SABIC-IP for the Americas region.
Physical Properties Metric English Comments
Specific Gravity 1.12 g/cc
1.12 g/cc
ASTM D 792
Linear Mold Shrinkage, Flow 0.0050 - 0.0070 cm/cm

@Thickness 3.20 mm
 0.0050 - 0.0070 in/in

@Thickness 0.126 in
 SABIC Method
Melt Flow 4.2 g/10 min

@Load 2.16 kg,
Temperature 230 °C
 4.2 g/10 min

@Load 4.76 lb,
Temperature 446 °F
 ASTM D 1238
10 g/10 min

@Load 3.80 kg,
Temperature 230 °C
 10 g/10 min

@Load 8.38 lb,
Temperature 446 °F
 ASTM D 1238
32.1 g/10 min

@Load 10.0 kg,
Temperature 220 °C
 32.1 g/10 min

@Load 22.0 lb,
Temperature 428 °F
 ASTM D 1238
Mechanical Properties Metric English Comments
Tensile Strength at Break 40.0 MPa
5800 psi
Type I, 50 mm/min; ASTM D 638
Tensile Strength, Yield 50.0 MPa
7250 psi
Type I, 50 mm/min; ASTM D 638
Elongation at Break 30 %
30 %
Type I, 50 mm/min; ASTM D 638
Elongation at Yield 3.0 %
3.0 %
Type I, 50 mm/min; ASTM D 638
Tensile Modulus 1.65 GPa
239 ksi
50 mm/min; ASTM D 638
Flexural Yield Strength 74.0 MPa
10700 psi
2.6 mm/min, 100 mm span; ASTM D 790
Flexural Modulus 2.20 GPa
319 ksi
2.6 mm/min, 100 mm span; ASTM D 790
Izod Impact, Notched 1.33 J/cm

@Temperature 23.0 °C
 2.49 ft-lb/in

@Temperature 73.4 °F
 ASTM D 256
Impact Test 37.0 J

@Temperature 23.0 °C
 27.3 ft-lb

@Temperature 73.4 °F
 Instrumented Impact Total Energy; ASTM D 3763
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 86.4 µm/m-°C

@Temperature -40.0 - 40.0 °C
 48.0 µin/in-°F

@Temperature -40.0 - 104 °F
 ASTM E 831
CTE, linear, Transverse to Flow 93.6 µm/m-°C

@Temperature -40.0 - 40.0 °C
 52.0 µin/in-°F

@Temperature -40.0 - 104 °F
 ASTM E 831
Deflection Temperature at 0.46 MPa (66 psi) 82.0 °C

@Thickness 6.40 mm
 180 °F

@Thickness 0.252 in
 unannealed; ASTM D 648
Deflection Temperature at 1.8 MPa (264 psi) 72.0 °C

@Thickness 6.40 mm
 162 °F

@Thickness 0.252 in
 unannealed; ASTM D 648
Vicat Softening Point 85.0 °C
185 °F
Rate B/50; ASTM D 1525
UL RTI, Electrical 50.0 °C
122 °F
UL 746B
UL RTI, Mechanical with Impact 50.0 °C
122 °F
UL 746B
UL RTI, Mechanical without Impact 50.0 °C
122 °F
UL 746B
Flammability, UL94 V-0

@Thickness 1.49 mm
 V-0

@Thickness 0.0587 in
 UL 94
5VB

@Thickness 2.41 mm
 5VB

@Thickness 0.0949 in
 UL 94
5VA

@Thickness 3.22 mm
 5VA

@Thickness 0.127 in
 UL 94
Oxygen Index 36.5 %
36.5 %
LOI; ASTM D 2863
Electrical Properties Metric English Comments
Comparative Tracking Index 250 - 400 V
250 - 400 V
PLC code 2; UL 746A
Hot Wire Ignition, HWI >= 120 sec
>= 120 sec
PLC code 0; UL 746A
High Amp Arc Ignition, HAI 30 - 60 arcs
30 - 60 arcs
surface, PLC code 2; UL 746A