POLYMER SEARCH

Styron CALIBREâ„¢ 5101-15 Polycarbonate Resin

Category	Polymer , Thermoplastic , Polycarbonate (PC)
Manufacturer	Styron
Trade Name	CALIBRE™
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Styron CALIBREâ„¢ 5101-15 Polycarbonate Resin.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Overview: CALIBREâ„¢ 5101 Polycarbonate resin is 10% glass-reinforced and provides increased modulus and improved heat distortion resistance with minimal shrinkage. This resin offers outstanding UL 94 flammability ratings and contains mold release. CALIBRE 5101 is available in 8 and 15 melt flow rates. CALIBRE 5101 resin has undergone biocompatibility testing based on ISO 10993 (Biological Evaluation of Medical Devices) and is suitable for use in approved medical applications.Main Characteristics: Glass reinforcedIgnition resistantISO 10993 Applications:Information Technology EquipmentTelecommunicationsMedical applicationsInformation provided by Styron

Physical Properties	Metric	English	Comments
Density	1.27 g/cc	0.0459 lb/inÂ³	ISO 1183/A; ASTM D792
Water Absorption	0.25 % @Temperature 23.0 Â°C	0.25 % @Temperature 73.4 Â°F	Equilibrium, 50% RH; ISO 62; ASTM D570
	0.15 % @Temperature 23.0 Â°C, Time 86400 sec	0.15 % @Temperature 73.4 Â°F, Time 24.0 hour	ISO 62; ASTM D570
Linear Mold Shrinkage, Flow	0.0020 - 0.0050 cm/cm	0.0020 - 0.0050 in/in	ISO 294-4; ASTM D955
Melt Flow	15 g/10 min @Load 1.20 kg, Temperature 300 Â°C	15 g/10 min @Load 2.65 lb, Temperature 572 Â°F	ASTM D1238; ISO 1133

Mechanical Properties	Metric	English	Comments
Hardness, Rockwell M	62	62	ASTM D785
Hardness, Rockwell R	122	122	ASTM D785
Tensile Strength at Break	60.7 MPa	8800 psi	50 mm/min; ASTM D638
	61.0 MPa	8850 psi	ISO 527-2/50
Tensile Strength, Yield	62.0 MPa	8990 psi	ISO 527-2/50
	62.1 MPa	9010 psi	50 mm/min; ASTM D638
Elongation at Break	6.0 %	6.0 %	50 mm/min; ISO 527-2/50; ASTM D638
Tensile Modulus	3.38 GPa	490 ksi	50 mm/min; ISO 527-2/50; ASTM D638
Flexural Strength	93.8 MPa	13600 psi	Method I (3 point load), 2.0 mm/min; ISO 178; ASTM D790
Flexural Modulus	3.17 GPa	460 ksi	Method I (3 point load), 2.0 mm/min; ISO 178; ASTM D790
Izod Impact, Notched	0.800 J/cm @Temperature 23.0 Â°C	1.50 ft-lb/in @Temperature 73.4 Â°F	ASTM D256
Tensile Impact Strength	147 kJ/mÂ²	69.9 ft-lb/inÂ²	ASTM D1822
Dart Drop, Total Energy	40.1 J	29.6 ft-lb	3.39 m/sec; ASTM D3763

Thermal Properties	Metric	English	Comments
CTE, linear, Parallel to Flow	38.0 Âµm/m-Â°C @Temperature -40.0 - 82.0 Â°C	21.1 Âµin/in-Â°F @Temperature -40.0 - 180 Â°F	ASTM D696
Deflection Temperature at 0.46 MPa (66 psi)	144 Â°C	291 Â°F	Annealed; ISO 75-2/B; ASTM D648
Deflection Temperature at 1.8 MPa (264 psi)	134 Â°C	273 Â°F	Unannealed; ISO 75-2/B; ASTM D648
Vicat Softening Point	160 Â°C @Load 5.10 kg	320 Â°F @Load 11.2 lb	Rate A (50Â°C/h); ISO 306/B50; ASTM D1525
Flammability, UL94	V-2 @Thickness 1.59 mm	V-2 @Thickness 0.0626 in
	V-0 @Thickness 3.20 mm	V-0 @Thickness 0.126 in
Oxygen Index	32 %	32 %	ISO 4289-2

Descriptive Properties	Value	Comments
Average Extent of Burring	1 cm	ASTM D635

Users viewing this material also viewed the following: