Zotefoams Plastazote® LD29 Low Density Polyethylene Foam

Category Polymer , Thermoplastic , Polyethylene (PE) , LDPE
Manufacturer Zotefoams
Trade Name Plastazote®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Zotefoams Plastazote® LD29 Low Density Polyethylene Foam.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Plastazote® is a closed cell, cross-linked polyethylene foam manufactured using nitrogen expansion technology to produce foams with exceptional cell size uniformity, low odor / high purity and outstanding physical attributes.Compliant with EC food contact and US FDA regulations.Information provided by Zotefoams
Physical Properties Metric English Comments
Density 0.0250 - 0.0330 g/cc
0.000903 - 0.00119 lb/in³
sheet density
0.0290 g/cc
0.00105 lb/in³
Nominal skin/skin; BS ISO 7214 1998
Cell Length 0.400 - 0.900 mm
0.0157 - 0.0354 in
0.650 mm
0.0256 in
Typical Diameter
Mechanical Properties Metric English Comments
Hardness, Shore OO 53
53
10 mm cell/cell thickness; ISO 868 1985
Tensile Strength 0.375 MPa
54.4 psi
ISO 7214 1998
Elongation at Break 140 %
140 %
Compressive Yield Strength 0.0470 MPa

@Strain 10.0 %
6.82 psi

@Strain 10.0 %
BS ISO 7214 1998
0.0640 MPa

@Strain 25.0 %
9.28 psi

@Strain 25.0 %
BS ISO 7214 1998
0.0970 MPa

@Strain 40.0 %
14.1 psi

@Strain 40.0 %
BS ISO 7214 1998
0.131 MPa

@Strain 50.0 %
19.0 psi

@Strain 50.0 %
BS ISO 7214 1998
Tear Strength 0.740 kN/m
4.22 pli
BS EN ISO 8067 1995
Compression Set 3.0 %

@Time 79200 sec,
Strain 25.0 %
3.0 %

@Time 22.0 hour,
Strain 25.0 %
24 hr recovery; BS ISO 7214 1998
10.5 %

@Time 79200 sec,
Strain 25.0 %
10.5 %

@Time 22.0 hour,
Strain 25.0 %
0.5 hr recovery; BS ISO 7214 1998
14 %

@Time 79200 sec,
Strain 50.0 %
14 %

@Time 22.0 hour,
Strain 50.0 %
24 hr recovery; BS ISO 7214 1998
23.5 %

@Time 79200 sec,
Strain 50.0 %
23.5 %

@Time 22.0 hour,
Strain 50.0 %
0.5 hr recovery; BS ISO 7214 1998
Thermal Properties Metric English Comments
Thermal Conductivity 0.0390 W/m-K
0.271 BTU-in/hr-ft²-°F
mean temp of 10°C; ISO 8302 1991
Maximum Service Temperature, Air 100 °C
212 °F
Minimum Service Temperature, Air -70.0 °C
-94.0 °F
Flammability Test 1.2

@Thickness 13.0 mm
1.2

@Thickness 0.512 in
Horizontal Burn Rate, mm/sec; ISO 7214 1998
1.7

@Thickness 5.00 mm
1.7

@Thickness 0.197 in
Horizontal Burn Rate, mm/sec; ISO 7214 1998