SABIC Innovative Plastics Noryl N750T PPE+HIPS
| Category | Polymer , Thermoplastic , Polyphenylene Ether/PPO , Polystyrene (PS) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | Noryl |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics Noryl N750T PPE+HIPS.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
ECO-FLO(tm). ECO conforming, nonhalogenated flame retardant PPE+PS. High flow. Electrical, TV and Business equipment applications.This data was supplied by SABIC-IP for the Americas region.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.12 g/cc | 1.12 g/cc | ASTM D 792 |
| Linear Mold Shrinkage, Flow | 0.0050 - 0.0070 cm/cm @Thickness 3.20 mm |
0.0050 - 0.0070 in/in @Thickness 0.126 in |
SABIC Method |
| Melt Flow | 30 g/10 min @Load 3.80 kg, Temperature 260 °C |
30 g/10 min @Load 8.38 lb, Temperature 500 °F |
ASTM D 1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 44.0 MPa | 6380 psi | Type I, 50 mm/min; ASTM D 638 |
| Tensile Strength, Yield | 55.0 MPa | 7980 psi | Type I, 50 mm/min; ASTM D 638 |
| Elongation at Break | 25 % | 25 % | Type I, 50 mm/min; ASTM D 638 |
| Elongation at Yield | 3.0 % | 3.0 % | Type I, 50 mm/min; ASTM D 638 |
| Tensile Modulus | 2.41 GPa | 350 ksi | 50 mm/min; ASTM D 638 |
| Flexural Yield Strength | 82.0 MPa | 11900 psi | 1.3 mm/min, 50 mm span; ASTM D 790 |
| Flexural Modulus | 2.41 GPa | 350 ksi | 1.3 mm/min, 50 mm span; ASTM D 790 |
| Izod Impact, Notched | 1.33 J/cm @Temperature 23.0 °C |
2.49 ft-lb/in @Temperature 73.4 °F |
ASTM D 256 |
| Impact Test | 33.0 J @Temperature 23.0 °C |
24.3 ft-lb @Temperature 73.4 °F |
Instrumented Impact Total Energy; ASTM D 3763 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 77.4 µm/m-°C @Temperature -40.0 - 40.0 °C |
43.0 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| CTE, linear, Transverse to Flow | 81.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
45.0 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| Deflection Temperature at 0.46 MPa (66 psi) | 81.0 °C @Thickness 3.20 mm |
178 °F @Thickness 0.126 in |
unannealed; ASTM D 648 |
| 85.0 °C @Thickness 6.40 mm |
185 °F @Thickness 0.252 in |
unannealed; ASTM D 648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 73.0 °C @Thickness 3.20 mm |
163 °F @Thickness 0.126 in |
unannealed; ASTM D 648 |
| 76.0 °C @Thickness 6.40 mm |
169 °F @Thickness 0.252 in |
unannealed; ASTM D 648 | |
| Vicat Softening Point | 90.0 °C | 194 °F | Rate B/50; ASTM D 1525 |
| UL RTI, Electrical | 65.0 °C | 149 °F | UL 746B |
| UL RTI, Mechanical with Impact | 65.0 °C | 149 °F | UL 746B |
| UL RTI, Mechanical without Impact | 65.0 °C | 149 °F | UL 746B |
| Flammability, UL94 | V-0 @Thickness 2.54 mm |
V-0 @Thickness 0.100 in |
UL 94 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Comparative Tracking Index | 250 - 400 V | 250 - 400 V | PLC code 2; UL 746A |
| Hot Wire Ignition, HWI | 30 - 60 sec | 30 - 60 sec | PLC code 2; UL 746A |
| High Amp Arc Ignition, HAI | >= 120 arcs | >= 120 arcs | surface, PLC code 0; UL 746A |
Users viewing this material also viewed the following:
- Idemitsu Kosan Xarec® WA 552 SPS, 30% Glass Filled
- Lucent Polymers PBT-310 Polybutylene Terephthalate, 30% Glass Fiber/Mineral Reinforced, Low Warp
- H.C. Starck Amperit® 554.071 Tungsten Carbide-Cobalt-Chromium 86-10-4 (WC-Co-Cr)
- LATI Latilub 57-30GRTS G/20 PPA, 20% Glass Fiber Reinforced
- A. Schulman POLYFORT™ FPP 3443U UV Resistant Homopolymer Polypropylene
- CRG Industries Advantic™ 40 Syntactic Foam
- ConocoPhillips Hydroclear® El Mar® Ashless Heavy Duty SAE 30
- Mateck Sodium Chloride (NaCl)
Copyright © lookpolymers.com All Rights Reserved