SABIC Innovative Plastics Noryl LS175 PPE+HIPS

Category Polymer , Thermoplastic , Polyphenylene Ether/PPO , Polystyrene (PS)
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name Noryl
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics Noryl LS175 PPE+HIPS.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Noryl* LS175 modified polyphenylene ether resin is an unfilled grade suitable for both extrusion and injection molding conversion routes. It uses non-chlorinated, non-brominated FR additives to deliver low smoke performance and a UL94 V0 rating. Noryl LS175 resin is currently available in limited colors and may be an excellent material candidate for applications in transportation and building/construction markets.This data was supplied by SABIC-IP for the Americas region.
Physical Properties Metric English Comments
Specific Gravity 1.11 g/cc
1.11 g/cc
ASTM D 792
Density 1.11 g/cc
0.0401 lb/in³
ISO 1183
Moisture Absorption at Equilibrium 0.42 %
0.42 %
23°C / 50% RH; ISO 62
Water Absorption at Saturation 0.45 %

@Temperature 23.0 °C
 0.45 %

@Temperature 73.4 °F
 ISO 62
Linear Mold Shrinkage, Flow 0.0050 - 0.0080 cm/cm

@Thickness 3.20 mm
 0.0050 - 0.0080 in/in

@Thickness 0.126 in
 SABIC Method
Melt Flow 4.0 g/10 min

@Load 5.00 kg,
Temperature 280 °C
 4.0 g/10 min

@Load 11.0 lb,
Temperature 536 °F
 [cm^3/10 min] Melt Volume Rate; ISO 1133
4.4 g/10 min

@Load 5.00 kg,
Temperature 280 °C
 4.4 g/10 min

@Load 11.0 lb,
Temperature 536 °F
 ASTM D 1238
Mechanical Properties Metric English Comments
Tensile Strength at Break 56.0 MPa
8120 psi
Type I, 50 mm/min; ASTM D 638
68.0 MPa
9860 psi
50 mm/min; ISO 527
Tensile Strength, Yield 72.0 MPa
10400 psi
50 mm/min; ISO 527
74.0 MPa
10700 psi
Type I, 50 mm/min; ASTM D 638
Elongation at Break 6.0 %
6.0 %
50 mm/min; ISO 527
16 %
16 %
Type I, 50 mm/min; ASTM D 638
Elongation at Yield 4.5 %
4.5 %
50 mm/min; ISO 527
5.2 %
5.2 %
Type I, 50 mm/min; ASTM D 638
Tensile Modulus 2.70 GPa
392 ksi
1 mm/min; ISO 527
2.89 GPa
419 ksi
50 mm/min; ASTM D 638
Flexural Yield Strength 110 MPa
16000 psi
2 mm/min; ISO 178
119 MPa
17300 psi
1.3 mm/min, 50 mm span; ASTM D 790
Flexural Modulus 2.56 GPa
371 ksi
2 mm/min; ISO 178
2.57 GPa
373 ksi
1.3 mm/min, 50 mm span; ASTM D 790
Izod Impact, Notched 0.730 J/cm

@Temperature -30.0 °C
 1.37 ft-lb/in

@Temperature -22.0 °F
 ASTM D 256
1.69 J/cm

@Temperature 23.0 °C
 3.17 ft-lb/in

@Temperature 73.4 °F
 ASTM D 256
Izod Impact, Notched (ISO) 9.00 kJ/m²

@Temperature -30.0 °C
 4.28 ft-lb/in²

@Temperature -22.0 °F
 80*10*4; ISO 180/1A
21.0 kJ/m²

@Temperature 23.0 °C
 9.99 ft-lb/in²

@Temperature 73.4 °F
 80*10*4; ISO 180/1A
Charpy Impact, Notched 2.60 J/cm²

@Temperature 23.0 °C
 12.4 ft-lb/in²

@Temperature 73.4 °F
 V-notch Edgew 80*10*4 sp=62mm; ISO 179/1eA
Impact Test 49.0 J

@Temperature 23.0 °C
 36.1 ft-lb

@Temperature 73.4 °F
 Instrumented Impact Total Energy; ASTM D 3763
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 86.5 µm/m-°C

@Temperature 23.0 - 80.0 °C
 48.1 µin/in-°F

@Temperature 73.4 - 176 °F
 ISO 11359-2
92.4 µm/m-°C

@Temperature -40.0 - 40.0 °C
 51.3 µin/in-°F

@Temperature -40.0 - 104 °F
 ASTM E 831
CTE, linear, Transverse to Flow 95.9 µm/m-°C

@Temperature -40.0 - 40.0 °C
 53.3 µin/in-°F

@Temperature -40.0 - 104 °F
 ASTM E 831
95.9 µm/m-°C

@Temperature -40.0 - 40.0 °C
 53.3 µin/in-°F

@Temperature -40.0 - 104 °F
 ISO 11359-2
Deflection Temperature at 1.8 MPa (264 psi) 117 °C
243 °F
Edgew 120*10*4 sp=100mm; ISO 75/Ae
115 °C

@Thickness 3.20 mm
 239 °F

@Thickness 0.126 in
 unannealed; ASTM D 648
Vicat Softening Point 140 °C
284 °F
Rate B/50; ASTM D 1525
142 °C
288 °F
Rate B/50; ISO 306
144 °C
291 °F
Rate B/120; ISO 306
UL RTI, Electrical 65.0 °C
149 °F
UL 746B
UL RTI, Mechanical with Impact 65.0 °C
149 °F
UL 746B
UL RTI, Mechanical without Impact 65.0 °C
149 °F
UL 746B
Flammability, UL94 V-1

@Thickness 1.00 mm
 V-1

@Thickness 0.0394 in
 UL 94
V-0

@Thickness 1.50 mm
 V-0

@Thickness 0.0591 in
 UL 94
Oxygen Index 31 %
31 %
LOI; ISO 4589
Glow Wire Test 825 °C

@Thickness 1.00 mm
 1520 °F

@Thickness 0.0394 in
 Glow Wire Ignitability Temperature; IEC 60695-2-13
825 °C

@Thickness 2.00 mm
 1520 °F

@Thickness 0.0787 in
 Glow Wire Ignitability Temperature; IEC 60695-2-13
825 °C

@Thickness 2.50 mm
 1520 °F

@Thickness 0.0984 in
 Glow Wire Ignitability Temperature; IEC 60695-2-13
825 °C

@Thickness 3.00 mm
 1520 °F

@Thickness 0.118 in
 Glow Wire Ignitability Temperature; IEC 60695-2-13
960 °C

@Thickness 3.20 mm
 1760 °F

@Thickness 0.126 in
 Glow Wire Flammability Index; IEC 60695-2-12
Electrical Properties Metric English Comments
Volume Resistivity 1.00e+15 ohm-cm
1.00e+15 ohm-cm
IEC 60093
1.00e+17 ohm-cm
1.00e+17 ohm-cm
ASTM D 257
Surface Resistance >= 1.00e+15 ohm
>= 1.00e+15 ohm
ROA; IEC 60093
>= 1.00e+17 ohm
>= 1.00e+17 ohm
ASTM D 257
Dielectric Constant 2.7

@Frequency 1.00e+6 Hz
 2.7

@Frequency 1.00e+6 Hz
 IEC 60250
2.8

@Frequency 50.0 - 60.0 Hz
 2.8

@Frequency 50.0 - 60.0 Hz
 IEC 60250
Dielectric Strength 16.0 kV/mm

@Thickness 3.20 mm
 406 kV/in

@Thickness 0.126 in
 in oil; IEC 60243-1
26.0 kV/mm

@Thickness 1.60 mm
 660 kV/in

@Thickness 0.0630 in
 in oil; IEC 60243-1
33.0 kV/mm

@Thickness 0.800 mm
 838 kV/in

@Thickness 0.0315 in
 in oil; IEC 60243-1
Dissipation Factor 0.0020

@Frequency 1.00e+6 Hz
 0.0020

@Frequency 1.00e+6 Hz
 IEC 60250
0.0040

@Frequency 50.0 - 60.0 Hz
 0.0040

@Frequency 50.0 - 60.0 Hz
 IEC 60250
Arc Resistance 60 - 120 sec
60 - 120 sec
Tungsten, PLC code 6; ASTM D 495
Comparative Tracking Index 200 V
200 V
IEC 60112
175 - 250 V
175 - 250 V
PLC code 3; UL 746A
Hot Wire Ignition, HWI 60 - 120 sec
60 - 120 sec
PLC code 1; UL 746A
High Amp Arc Ignition, HAI >= 120 arcs
>= 120 arcs
surface, PLC code 0; UL 746A
High Voltage Arc-Tracking Rate, HVTR 80.0 - 150 mm/min
3.15 - 5.91 in/min
PLC code 3; UL 746A