SABIC Innovative Plastics Noryl GTX GTX9200 PPE+PS+PA66

Category Polymer , Thermoplastic , Polyphenylene Ether/PPO , Polystyrene (PS)
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name NORYL GTX
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics Noryl GTX GTX9200 PPE+PS+PA66.pdf
Price EMAIL US    sales@lookpolymers.com
Material Notes:
High Flow GTX for Automotive applicationsThis data was supplied by SABIC-IP for the Americas region.
Physical Properties Metric English Comments
Specific Gravity 1.09 g/cc
1.09 g/cc
ASTM D 792
Density 1.09 g/cc
0.0394 lb/in³
ISO 1183
Moisture Absorption at Equilibrium 0.30 %
0.30 %
23°C / 50% RH; ISO 62
Water Absorption at Saturation 0.55 %

@Temperature 23.0 °C
 0.55 %

@Temperature 73.4 °F
 ISO 62
Linear Mold Shrinkage, Flow 0.0113 - 0.0126 cm/cm

@Thickness 3.20 mm
 0.0113 - 0.0126 in/in

@Thickness 0.126 in
 SABIC Method
Melt Flow 22 g/10 min

@Load 5.00 kg,
Temperature 220 °C
 22 g/10 min

@Load 11.0 lb,
Temperature 428 °F
 [cm^3/10 min] Melt Volume Rate; ISO 1133
24 g/10 min

@Load 3.80 kg,
Temperature 200 °C
 24 g/10 min

@Load 8.38 lb,
Temperature 392 °F
 ASTM D 1238
Mechanical Properties Metric English Comments
Tensile Strength at Break 51.0 MPa
7400 psi
50 mm/min; ISO 527
54.0 MPa
7830 psi
Type I, 50 mm/min; ASTM D 638
Tensile Strength, Yield 53.0 MPa
7690 psi
Type I, 50 mm/min; ASTM D 638
56.0 MPa
8120 psi
50 mm/min; ISO 527
Elongation at Break 42.9 %
42.9 %
50 mm/min; ISO 527
49.5 %
49.5 %
Type I, 50 mm/min; ASTM D 638
Elongation at Yield 7.5 %
7.5 %
50 mm/min; ISO 527
10.6 %
10.6 %
Type I, 50 mm/min; ASTM D 638
Tensile Modulus 2.13 GPa
309 ksi
5 mm/min; ASTM D 638
2.38 GPa
345 ksi
1 mm/min; ISO 527
Flexural Yield Strength 77.0 MPa
11200 psi
1.3 mm/min, 50 mm span; ASTM D 790
87.0 MPa
12600 psi
2 mm/min; ISO 178
Flexural Modulus 2.21 GPa
321 ksi
2 mm/min; ISO 178
2.31 GPa
335 ksi
1.3 mm/min, 50 mm span; ASTM D 790
Izod Impact, Notched 1.36 J/cm

@Temperature -30.0 °C
 2.55 ft-lb/in

@Temperature -22.0 °F
 ASTM D 256
2.51 J/cm

@Temperature 23.0 °C
 4.70 ft-lb/in

@Temperature 73.4 °F
 ASTM D 256
Izod Impact, Notched (ISO) 17.0 kJ/m²

@Temperature -30.0 °C
 8.09 ft-lb/in²

@Temperature -22.0 °F
 80*10*4; ISO 180/1A
25.0 kJ/m²

@Temperature 23.0 °C
 11.9 ft-lb/in²

@Temperature 73.4 °F
 80*10*4; ISO 180/1A
Charpy Impact, Notched 2.80 J/cm²

@Temperature 23.0 °C
 13.3 ft-lb/in²

@Temperature 73.4 °F
 V-notch Edgew 80*10*4 sp=62mm; ISO 179/1eA
Impact Test 56.0 J

@Temperature 23.0 °C
 41.3 ft-lb

@Temperature 73.4 °F
 Instrumented Impact Total Energy; ASTM D 3763
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 90.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
 50.0 µin/in-°F

@Temperature -40.0 - 104 °F
 ASTM E 831
100 µm/m-°C

@Temperature -40.0 - 40.0 °C
 55.6 µin/in-°F

@Temperature -40.0 - 104 °F
 ISO 11359-2
CTE, linear, Transverse to Flow 50.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
 27.8 µin/in-°F

@Temperature -40.0 - 104 °F
 ISO 11359-2
70.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
 38.9 µin/in-°F

@Temperature -40.0 - 104 °F
 ASTM E 831
Deflection Temperature at 0.46 MPa (66 psi) 156 °C
313 °F
Flatw 80*10*4 sp=64mm; ISO 75/Bf
156 °C

@Thickness 3.20 mm
 313 °F

@Thickness 0.126 in
 unannealed; ASTM D 648
Vicat Softening Point 168 °C
334 °F
Rate B/50; ASTM D 1525
168 °C
334 °F
Rate B/50; ISO 306
169 °C
336 °F
Rate B/120; ISO 306