Asahi Kasei Leona® 13G25 25% Glass Filled Nylon 66
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, 30% Glass Fiber Filled |
| Manufacturer | Asahi Kasei |
| Trade Name | Leona® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Asahi Kasei Leona® 13G25 25% Glass Filled Nylon 66.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Enhanced strength, stiffness and durability; with 25% GF.Applications:Automotive parts Information provided by Asahi Kasei
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.32 g/cc | 1.32 g/cc | Dry; ASTM D792 |
| Water Absorption | 1.9 % | 1.9 % | Wet |
| Linear Mold Shrinkage | 0.0050 cm/cm | 0.0050 in/in | Dry; ASTM D2863 |
| Linear Mold Shrinkage, Transverse | 0.0090 cm/cm | 0.0090 in/in | Dry; ASTM D2863 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell M | 74 | 74 | Wet; ASTM D785 |
| 96 | 96 | Dry; ASTM D785 | |
| Hardness, Rockwell R | 120 | 120 | Dry; ASTM D785 |
| Tensile Strength, Yield | 110 MPa | 16000 psi | Wet; ASTM D638 |
| 180 MPa | 26100 psi | Dry; ASTM D638 | |
| Elongation at Break | 3.0 % | 3.0 % | Dry; ASTM D638 |
| 6.0 % | 6.0 % | Wet; ASTM D638 | |
| Flexural Strength | 175 MPa | 25400 psi | Wet; ASTM D790 |
| 290 MPa | 42100 psi | Dry; ASTM D790 | |
| Flexural Modulus | 4.70 GPa | 682 ksi | Wet; ASTM D790 |
| 8.10 GPa | 1170 ksi | Dry; ASTM D790 | |
| Izod Impact, Notched | 1.05 J/cm | 1.97 ft-lb/in | Dry; ASTM D256 |
| 1.60 J/cm | 3.00 ft-lb/in | Wet; ASTM D256 | |
| Taber Abrasion, mg/1000 Cycles | 12 | 12 | Wet; ASTM D1044 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 30.0 µm/m-°C @Temperature 20.0 °C |
16.7 µin/in-°F @Temperature 68.0 °F |
Dry; ASTM D696 |
| Thermal Conductivity | 0.300 W/m-K | 2.08 BTU-in/hr-ft²-°F | Dry |
| Deflection Temperature at 0.46 MPa (66 psi) | 260 °C | 500 °F | Dry; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 250 °C | 482 °F | Dry; ASTM D648 |
| Flammability, UL94 | HB | HB | Dry |
Users viewing this material also viewed the following:
- PolyOne Geon™ Vinyl Wire & Cable WJAC36L Polyvinyl Chloride, Flexible (PVC, Flexible)
- S&E Specialty Polymers TufTech™ GA-92-129 Clear PVC Compound
- Kennametal Stellite Denertiaâ„¢ C13 Cobalt Chromium Dental Alloy
- Solvay Specialty Polymers Amodel® HFZ A-1133 L Polyphthalamide (PPA), 33% Glass Fiber
- Cytec (Conap) FR-1047 / EA-87 Conapoxy® Resin / Conacure® Hardener
- DuPont Teijin Films Teijin® Tetoron® HSL Polyester Film, 300 Gauge
- 3M Dyneon™ FEP 6307Z Fluorinated Ethylene Propylene Fluorothermoplastic Granules
- Sinotek Materials Packing Expanded Graphite Braided
Copyright © lookpolymers.com All Rights Reserved