Menzolit Menzolit® SMC 0410 Unsaturated Polyester UP
| Category | Polymer , Thermoset , Polyester, TS , Thermoset Polyester Glass SMC |
| Manufacturer | Menzolit |
| Trade Name | Menzolit® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Menzolit Menzolit® SMC 0410 Unsaturated Polyester UP.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
SMC 0410 is a Premium Class-A SMC for on-line painted exterior body applications on cars developed with CCC technology. These compounds mould to parts with excellent surface quality for on-line painted body panels at high bake temperatures (190- 200 °C). The parts have to be primed with a conductive primer before e-coating.
Moulded parts comply with all regulations of the automotive industry including low C-emissions. Surface defects like waviness, fibre patterns and orange peel are not existent with this product. To achieve the highest surface quality, we recommend that tool surfaces are mirror polished. The parts show very good adhesion to paint or In Mould Coating (IMC).Information Provided by Menzolit
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.90 g/cc | 0.0686 lb/in³ | ISO 1183 |
| Water Absorption | <= 0.50 % | <= 0.50 % | ISO 62 |
| Linear Mold Shrinkage | -0.000500 cm/cm | -0.000500 in/in | ISO 2577 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Ultimate | 90.0 MPa @Temperature 22.0 °C |
13100 psi @Temperature 71.6 °F |
25mm flat samples, compression moulded; ISO 527-4 |
| Tensile Strength, Yield | 90.0 MPa @Temperature 22.0 °C |
13100 psi @Temperature 71.6 °F |
25mm flat samples, compression moulded; ISO 527-4 |
| Elongation at Yield | 1.5 % | 1.5 % | tensile rupture strain; ISO 527-4 |
| Modulus of Elasticity | 12.0 GPa | 1740 ksi | 25mm flat samples, compression moulded; ISO 527-4 |
| Flexural Strength | 190 MPa @Temperature 22.0 °C |
27600 psi @Temperature 71.6 °F |
25 mm wide 100 mm long, flat samples; ISO 14125 |
| Flexural Modulus | 11.0 GPa @Temperature 22.0 °C |
1600 ksi @Temperature 71.6 °F |
25 mm wide 100 mm long, flat samples; ISO 14125 |
| Compressive Yield Strength | 100 MPa | 14500 psi | ISO 14126 |
| Poissons Ratio | 0.30 | 0.30 | |
| Shear Modulus | 4.60 GPa | 667 ksi | in plane |
| Charpy Impact, Notched | 8.60 J/cm² | 40.9 ft-lb/in² | ISO 179 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 10.0 µm/m-°C | 5.56 µin/in-°F | ISO 11359-2 |
| Specific Heat Capacity | 1.10 J/g-°C | 0.263 BTU/lb-°F | |
| Thermal Conductivity | 0.700 W/m-K | 4.86 BTU-in/hr-ft²-°F | |
| Maximum Service Temperature, Air | 165 °C | 329 °F | |
| Deflection Temperature at 1.8 MPa (264 psi) | >= 200 °C | >= 392 °F | ISO 75-2 |
| Minimum Service Temperature, Air | -40.0 °C | -40.0 °F | |
| Glass Transition Temp, Tg | 200 °C | 392 °F | ISO 11357-2 |
| Flammability, UL94 | HB @Thickness 3.00 mm |
HB @Thickness 0.118 in |
|
| Oxygen Index | 22 % | 22 % | ISO 4589-2 |
| Glow Wire Test | 750 °C | 1380 °F | IEC 60695-2-12 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+15 ohm-cm | 1.00e+15 ohm-cm | IEC 60093 |
| Surface Resistance | 1.00e+12 ohm | 1.00e+12 ohm | IEC 60093 |
| Dielectric Constant | 4.0 | 4.0 | IEC 60250 |
| Dielectric Strength | 24.0 kV/mm | 610 kV/in | IEC 60243-1 |
| Dissipation Factor | 0.010 | 0.010 | IEC 60250 |
| Comparative Tracking Index | 600 V | 600 V | IEC 60112 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Processing Temperature | 145 - 155 °C | 293 - 311 °F | Compression moulding, matched metal die |
Users viewing this material also viewed the following:
- Plaskolite Optix® CA - 2000 High Impact Grade Acrylic Resin
- NextGen Adhesives G907-25 Optical Epoxy Adhesive
- PolyOne Geon™ Vinyl Flexible B5D01 Polyvinyl Chloride, Flexible (PVC, Flexible)
- Indium Corp. Indalloy 48 Bismuth Solder Alloy
- Techmer ES HiFill® PA6 GF33 HS BK 33% Glass Filled
- DSM Stanyl® 46HF5041LW Nylon 46-40% Glass Reinforced (European and Asian Grade) (Dry)
- Fainplast Compounds GS 64 Flexible PVC, Injection Molding for Footwear
- Bulk Molding Compounds BMC 3001H Mineral Filled Alkyd
- Cheng Yu Plastic E2315 Flame Retardant PET, 15% Glass Fiber
- TSE Industries Millathane® E34 Millable Polyether Polyurethane Rubber with DOA
Copyright © lookpolymers.com All Rights Reserved