- SABIC Innovative Plastics NORYL PX2944 PPE+HIPS (Asia Pacific)
SABIC Innovative Plastics NORYL PX2944 PPE+HIPS (Asia Pacific)
| Category | Polymer , Thermoplastic , Polyphenylene Ether/PPO , Polystyrene (PS) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | Noryl |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics NORYL PX2944 PPE+HIPS (Asia Pacific).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
PPE/PS, GF20%, high heat, non-FR
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.22 g/cc | 1.22 g/cc | ASTM D792 |
| Water Absorption | 0.060 % @Time 86400 sec |
0.060 % @Time 24.0 hour |
ASTM D570 |
| Linear Mold Shrinkage, Flow | 0.0020 - 0.0030 cm/cm @Thickness 3.20 mm |
0.0020 - 0.0030 in/in @Thickness 0.126 in |
SABIC Method |
| Melt Flow | 6.1 g/10 min @Load 5.00 kg, Temperature 300 °C |
6.1 g/10 min @Load 11.0 lb, Temperature 572 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 88.0 MPa | 12800 psi | SABIC - Japan Method |
| Elongation at Break | 4.0 - 6.0 % | 4.0 - 6.0 % | SABIC - Japan Method |
| Flexural Strength | 142 MPa | 20600 psi | ASTM D790 |
| Flexural Modulus | 5.27 GPa | 764 ksi | ASTM D790 |
| Izod Impact, Notched | 0.760 J/cm | 1.42 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 30.0 - 40.0 µm/m-°C @Temperature -30.0 - 30.0 °C |
16.7 - 22.2 µin/in-°F @Temperature -22.0 - 86.0 °F |
TMA |
| Deflection Temperature at 1.8 MPa (264 psi) | 154 °C @Thickness 6.40 mm |
309 °F @Thickness 0.252 in |
unannealed; ASTM D648 |
Users viewing this material also viewed the following:
- S&E Specialty Polymers GPP™ 1005M-EXLT PP
- Polykemi AB POLYshine PBT D201 PBT
- PolyOne Edgetek® NY-20GF/10GB/000 Polyamide 6 (Nylon 6)
- Lanxess Pocan® KU 1-7313 000000 PBT + PET, 15% Glass Fiber
- Karina 800-10/177-Y-ERYB-PO White PVC Compound
- SGL Carbon Group PANOX® SM C076 SSC Oxidized Textile Fiber, Crimped staple fiber, For felts and non-wovens
- Solvay IGEPAL® CA 210 Surfactant
- A. Schulman INVISION™ VX-5060UI INVISIONTMSoft Touch Polyolefin Thermoplastic
- Tra-Con Tra-Bond 868-3N1 Room Temperature Cure Adhesive
Copyright © lookpolymers.com All Rights Reserved