SABIC Innovative Plastics NORYL NH8006 PPE+HIPS (Europe-Africa-Middle East)
| Category | Polymer , Thermoplastic , Polyphenylene Ether/PPO , Polystyrene (PS) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | Noryl |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics NORYL NH8006 PPE+HIPS (Europe-Africa-Middle East).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Noryl* NH8006 resin is a 30% glass reinforced, modified PPE-PS blend. The material uses non-halogenated flame retardants to achieve a UL94 V0 flame rating (color specific) while offering an exceptional balance of strength and dimensional stability. This grade can be processed via extrusion or injection molding. Noryl NH8006 is available in custom colors and may be an excellent material candidate for use in electrical and electronics markets.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.33 g/cc | 1.33 g/cc | ASTM D792 |
| Density | 1.34 g/cc | 0.0484 lb/in³ | ISO 1183 |
| Moisture Absorption | 0.0700 % | 0.0700 % | 23°C / 50% RH; ISO 62 |
| Water Absorption at Saturation | 0.23 % | 0.23 % | ISO 62 |
| Linear Mold Shrinkage, Flow | 0.0020 - 0.0025 cm/cm @Thickness 3.20 mm |
0.0020 - 0.0025 in/in @Thickness 0.126 in |
SABIC Method |
| Melt Flow | 2.1 g/10 min @Load 5.00 kg, Temperature 280 °C |
2.1 g/10 min @Load 11.0 lb, Temperature 536 °F |
ASTM D1238 |
| Melt Index of Compound | 6.0 g/10 min @Load 10.0 kg, Temperature 280 °C |
6.0 g/10 min @Load 22.0 lb, Temperature 536 °F |
MVR [cm^3/10 min]; ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 125 MPa | 18100 psi | Type I, 5 mm/min; ASTM D638 |
| 125 MPa | 18100 psi | 5 mm/min; ISO 527 | |
| Tensile Strength, Yield | 125 MPa | 18100 psi | Type I, 5 mm/min; ASTM D638 |
| 125 MPa | 18100 psi | 5 mm/min; ISO 527 | |
| Elongation at Break | 1.8 % | 1.8 % | 5 mm/min; ISO 527 |
| 2.0 % | 2.0 % | Type I, 5 mm/min; ASTM D638 | |
| Elongation at Yield | 1.8 % | 1.8 % | 5 mm/min; ISO 527 |
| 2.0 % | 2.0 % | Type I, 5 mm/min; ASTM D638 | |
| Tensile Modulus | 9.00 GPa | 1310 ksi | 1 mm/min; ISO 527 |
| 9.50 GPa | 1380 ksi | 5 mm/min; ASTM D638 | |
| Flexural Yield Strength | 160 MPa | 23200 psi | 2 mm/min; ISO 178 |
| 185 MPa | 26800 psi | 1.3 mm/min, 50 mm span; ASTM D790 | |
| Flexural Modulus | 8.00 GPa | 1160 ksi | 2 mm/min; ISO 178 |
| 8.60 GPa | 1250 ksi | 1.3 mm/min, 50 mm span; ASTM D790 | |
| Izod Impact, Notched | 0.850 J/cm | 1.59 ft-lb/in | ASTM D256 |
| 0.750 J/cm @Temperature -30.0 °C |
1.41 ft-lb/in @Temperature -22.0 °F |
ASTM D256 | |
| Izod Impact, Unnotched | 5.00 J/cm | 9.37 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 8.00 kJ/m² | 3.81 ft-lb/in² | 80*10*4; ISO 180/1A |
| 8.00 kJ/m² @Temperature -30.0 °C |
3.81 ft-lb/in² @Temperature -22.0 °F |
80*10*4; ISO 180/1A | |
| Izod Impact, Unnotched (ISO) | 26.0 kJ/m² | 12.4 ft-lb/in² | 80*10*4; ISO 180/1U |
| Charpy Impact, Notched | 0.900 J/cm² | 4.28 ft-lb/in² | Edgew 80*10*4 sp=62mm; ISO 179/1eA |
| Dart Drop, Total Energy | 14.0 J @Temperature 23.0 °C |
10.3 ft-lb @Temperature 73.4 °F |
ASTM D3763 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 37.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
20.6 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| 37.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
20.6 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 | |
| CTE, linear, Transverse to Flow | 55.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
30.6 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| 55.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
30.6 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 149 °C | 300 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 149 °C @Thickness 3.20 mm |
300 °F @Thickness 0.126 in |
unannealed; ASTM D648 | |
| Vicat Softening Point | 156 °C | 313 °F | Rate B/50; ASTM D1525 |
| 156 °C | 313 °F | Rate B/50; ISO 306 | |
| 160 °C | 320 °F | Rate B/120; ISO 306 | |
| UL RTI, Electrical | 110 °C | 230 °F | UL 746B |
| UL RTI, Mechanical with Impact | 105 °C | 221 °F | UL 746B |
| UL RTI, Mechanical without Impact | 110 °C | 230 °F | UL 746B |
| Flammability, UL94 | V-1 @Thickness 1.50 mm |
V-1 @Thickness 0.0591 in |
UL 94 by SABIC-IP |
| V-0 @Thickness 2.00 mm |
V-0 @Thickness 0.0787 in |
UL 94 by SABIC-IP | |
| 5VB @Thickness 3.00 mm |
5VB @Thickness 0.118 in |
UL 94 by SABIC-IP | |
| 5VA @Thickness 3.00 mm |
5VA @Thickness 0.118 in |
UL 94 by SABIC-IP | |
| Glow Wire Test | 960 °C @Thickness 3.20 mm |
1760 °F @Thickness 0.126 in |
IEC 60695-2-12 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Surface Resistance | >= 4.00e+17 ohm | >= 4.00e+17 ohm | ASTM D257 |
| 4.00e+17 - 5.00e+17 ohm | 4.00e+17 - 5.00e+17 ohm | ROA; IEC 60093 | |
| Dielectric Constant | 3.1 @Frequency 1.00e+6 Hz |
3.1 @Frequency 1.00e+6 Hz |
IEC 60250 |
| 3.11 @Frequency 1.00e+6 Hz |
3.11 @Frequency 1.00e+6 Hz |
ASTM D150 | |
| Dielectric Strength | 16.0 kV/mm @Thickness 3.20 mm |
406 kV/in @Thickness 0.126 in |
in oil; IEC 60243-1 |
| Dissipation Factor | 0.0040 @Frequency 1.00e+6 Hz |
0.0040 @Frequency 1.00e+6 Hz |
ASTM D150 |
| 0.0040 @Frequency 1.00e+6 Hz |
0.0040 @Frequency 1.00e+6 Hz |
IEC 60250 | |
| Hot Wire Ignition, HWI | >= 120 sec | >= 120 sec | UL 746A |
| High Amp Arc Ignition, HAI | 0.00 - 15 arcs | 0.00 - 15 arcs | UL 746A |
| High Voltage Arc-Tracking Rate, HVTR | >= 150 mm/min | >= 5.91 in/min | UL 746A |
Users viewing this material also viewed the following:
- Multibase TPSiV® 4000-60A Thermoplastic Elastomer
- MV Labs Y400 YCl3·6H2O Yttrium chloride hexahydrate
- Total Finaclear® 521 Clear Impact Polystyrene (discontinued **)
- Lushan PR-2A Maleic Anhydride Grafted Polypropylene
- Loctite® 246 High Temperature/Medium Strength Threadlocker
- A. Schulman POLYPUR™ FPU 1515 Thermoplastic Polyurethane Compound
- C.O.I.M. PLAXTER® P 72 Polymeric Plasticizer
- ATI Wah Chang 425™ Titanium Alloy, Tubular Extruded, Mill Annealed
- Multibase Multibatch® MP 63001 Anti-split
- DuPont Performance Polymers Delrin® 100ST NC010 Acetal Homopolymer (Unverified Data**)
Copyright © lookpolymers.com All Rights Reserved