SABIC Innovative Plastics NORYL LEN2211 PPE+HIPS (Asia Pacific)
| Category | Polymer , Thermoplastic , Polyphenylene Ether/PPO , Polystyrene (PS) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | Noryl |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics NORYL LEN2211 PPE+HIPS (Asia Pacific).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
PPE / HIPS unfilled, FR for LED application
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.23 g/cc | 1.23 g/cc | ASTM D792 |
| Water Absorption | 0.070 % @Time 86400 sec |
0.070 % @Time 24.0 hour |
ASTM D570 |
| Linear Mold Shrinkage, Flow | 0.0050 - 0.0070 cm/cm @Thickness 3.20 mm |
0.0050 - 0.0070 in/in @Thickness 0.126 in |
SABIC Method |
| Melt Flow | 7.0 g/10 min @Load 10.0 kg, Temperature 250 °C |
7.0 g/10 min @Load 22.0 lb, Temperature 482 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 57.0 MPa | 8270 psi | SABIC - Japan Method |
| Elongation at Break | 35 % | 35 % | SABIC - Japan Method |
| Flexural Strength | 96.0 MPa | 13900 psi | ASTM D790 |
| Flexural Modulus | 2.84 GPa | 412 ksi | ASTM D790 |
| Izod Impact, Notched | 0.780 J/cm | 1.46 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 60.0 µm/m-°C @Temperature -30.0 - 30.0 °C |
33.3 µin/in-°F @Temperature -22.0 - 86.0 °F |
TMA |
| Deflection Temperature at 1.8 MPa (264 psi) | 120 °C @Thickness 6.40 mm |
248 °F @Thickness 0.252 in |
unannealed; ASTM D648 |
Users viewing this material also viewed the following:
- Resin Technology Group 24N Two component Polyurethane Adhesive
- ExxonMobil Santoprene® 111-55 Thermoplastic Elastomer (discontinued **)
- SABIC Innovative Plastics Lexan® SLX1432 PC Copolymer (Asia Pacific)
- Samyang Triel® 5301SP Thermoplastics Polyetherester Elastomer, Double Extrusion
- A. Schulman FORMION™ FI 120E Non-Reinforced, Extrusion Grade Zinc Ionomer
- ExxonMobil 32 Mobil EAL Arctic Series
- DSM Biomedical BioSpan® SPU Segmented Polyether Polyurethane (SPU)
- Latrobe Lescalloy® UT-18 VAC-ARC ; 1.25 in. round High Strength Alloy Steel
Copyright © lookpolymers.com All Rights Reserved