Solvay Specialty Polymers Amodel® A-4133 L Polyphthalamide (PPA), Dry (discontinued **)

Category	Polymer , Thermoplastic , Polyphthalamide (PPA) , Polyphthalamide (PPA), 30% Glass Fiber Reinforced
Manufacturer
Trade Name
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Solvay Specialty Polymers Amodel® A-4133 L Polyphthalamide (PPA), Dry (discontinued **).pdf
Price	EMAIL US sales@lookpolymers.com

Material Notes:

Amodel A-4133L polyphthalamide (PPA) is a 33% glass reinforced resin designed to offer high crystallinity when molded in water-cooled molds. Key properties include high heat resistance, reduced outgassing and high strength over broad temperature range. It also exhibits low moisture absorption, excellent chemical resistance and excellent electrical properties. Amodel A-4133 L resin can be used in a variety of automotive electrical and electronic applications. These include connectors, sockets, switches, sensors. It is also a good choice for under-hood enclosures that protect critical control systems such as anti-lock brakes, traction control, steering, electronic engine control, transmission and chassis control units. Its rapid crystallization rate and high flow can result in shorter cycles, thereby enhancing molding productivity and lowering costs. - Black: A-4133 L BK 324 - Natural: A-4133 L NTInjection Notes: Injection Rate: 3 to 4 in/sec Holding Pressure: 50% of injection pressure

Physical Properties	Metric	English	Comments
Specific Gravity	1.46 g/cc	1.46 g/cc	ASTM D792
Density	1.46 g/cc	0.0527 lb/in³	ISO 1183
Filler Content	33 %	33 %	Glass Fiber
Water Absorption	0.29 % @Time 86400 sec	0.29 % @Time 24.0 hour	ASTM D570
Linear Mold Shrinkage, Flow	0.0050 cm/cm	0.0050 in/in	ASTM D955
Linear Mold Shrinkage, Transverse	0.010 cm/cm	0.010 in/in	ASTM D955

Mechanical Properties	Metric	English	Comments
Tensile Strength at Break	80.7 MPa @Temperature 175 °C	11700 psi @Temperature 347 °F	ISO 527-2
	89.6 MPa @Temperature 150 °C	13000 psi @Temperature 302 °F	ISO 527-2
	134 MPa @Temperature 100 °C	19400 psi @Temperature 212 °F	ISO 527-2
	193 MPa @Temperature 23.0 °C	28000 psi @Temperature 73.4 °F	ISO 527-2
Tensile Strength	200 MPa	29000 psi	ASTM D638
Elongation at Break	2.5 %	2.5 %	ASTM D638
	1.9 % @Temperature 23.0 °C	1.9 % @Temperature 73.4 °F	ISO 527-2
	3.3 % @Temperature 100 °C	3.3 % @Temperature 212 °F	ISO 527-2
	3.3 % @Temperature 150 °C	3.3 % @Temperature 302 °F	ISO 527-2
	4.0 % @Temperature 175 °C	4.0 % @Temperature 347 °F	ISO 527-2
Tensile Modulus	11.7 GPa	1700 ksi	ASTM D638
	5.79 GPa @Temperature 175 °C	840 ksi @Temperature 347 °F	ISO 527-2
	6.41 GPa @Temperature 150 °C	930 ksi @Temperature 302 °F	ISO 527-2
	8.96 GPa @Temperature 100 °C	1300 ksi @Temperature 212 °F	ISO 527-2
	12.3 GPa @Temperature 23.0 °C	1780 ksi @Temperature 73.4 °F	ISO 527-2
Flexural Strength	290 MPa	42100 psi	ASTM D790
	114 MPa @Temperature 175 °C	16500 psi @Temperature 347 °F	ISO 178
	128 MPa @Temperature 150 °C	18600 psi @Temperature 302 °F	ISO 178
	187 MPa @Temperature 100 °C	27100 psi @Temperature 212 °F	ISO 178
	269 MPa @Temperature 23.0 °C	39000 psi @Temperature 73.4 °F	ISO 178
Flexural Modulus	12.3 GPa	1780 ksi	ASTM D790
	4.90 GPa @Temperature 175 °C	711 ksi @Temperature 347 °F	ISO 178
	5.17 GPa @Temperature 150 °C	750 ksi @Temperature 302 °F	ISO 178
	7.72 GPa @Temperature 100 °C	1120 ksi @Temperature 212 °F	ISO 178
	10.4 GPa @Temperature 23.0 °C	1510 ksi @Temperature 73.4 °F	ISO 178
Compressive Strength	162 MPa	23500 psi	ASTM D695
Poissons Ratio	0.41	0.41	ASTM E132
Shear Modulus	4.15 - 4.36 GPa	602 - 632 ksi	Calculated
Shear Strength	89.6 MPa	13000 psi	ASTM D732
Izod Impact, Notched	0.694 J/cm	1.30 ft-lb/in	ASTM D256
Izod Impact, Unnotched	4.80 J/cm	8.99 ft-lb/in	ASTM D256
Izod Impact, Notched (ISO)	8.20 kJ/m²	3.90 ft-lb/in²	ISO 180/1A
	54.6 kJ/m²	26.0 ft-lb/in²	ISO 180/1U
Charpy Impact Unnotched	8.60 J/cm²	40.9 ft-lb/in²	ISO 179/1eU
Charpy Impact, Notched	0.800 J/cm²	3.81 ft-lb/in²	ISO 179/1eA

Thermal Properties	Metric	English	Comments
CTE, linear, Parallel to Flow	11.0 µm/m-°C @Temperature 100 - 200 °C	6.11 µin/in-°F @Temperature 212 - 392 °F	TMA; ASTM E831
	22.0 µm/m-°C @Temperature 0.000 - 100 °C	12.2 µin/in-°F @Temperature 32.0 - 212 °F	TMA; ASTM E831
CTE, linear, Transverse to Flow	77.0 µm/m-°C @Temperature 0.000 - 100 °C	42.8 µin/in-°F @Temperature 32.0 - 212 °F	TMA; ASTM E831
	140 µm/m-°C @Temperature 100 - 200 °C	77.8 µin/in-°F @Temperature 212 - 392 °F	TMA; ASTM E831
Melting Point	327 °C	621 °F
Deflection Temperature at 0.46 MPa (66 psi)	320 °C @Thickness 3.20 mm	608 °F @Thickness 0.126 in	Annealed; ASTM D648
Deflection Temperature at 1.8 MPa (264 psi)	310 °C	590 °F	Unannealed; ISO 75-2/A
	300 °C @Thickness 3.20 mm	572 °F @Thickness 0.126 in	Annealed; ASTM D648
Flammability, UL94	HB @Thickness 3.20 mm	HB @Thickness 0.126 in	UL 94

Processing Properties	Metric	English
Rear Barrel Temperature	318 - 324 °C	604 - 615 °F
Front Barrel Temperature	327 - 332 °C	621 - 630 °F
Melt Temperature	329 - 343 °C	624 - 649 °F
Mold Temperature	65.6 - 93.3 °C	150 - 200 °F
Drying Temperature	120 °C @Time 14400 sec	248 °F @Time 4.00 hour
Moisture Content	0.045 %	0.045 %

Descriptive Properties	Value	Comments
Additive	Lubricant
	Mold Release
Appearance	Black
	Natural Color
Availability	Africa & Middle East
	Asia Pacific
	Europe
	North America
	South America
Features	Fast Molding Cycle
	Good Chemical Resistance
	Good Creep Resistance
	Good Dimensional Stability
	Good Stiffness
	High Stiffness
	High Strength
	Hot Water Moldability
	Low Moisture Absorption
	Lubricated
Forms	Pellets
Processing Method	Water-Heated Mold Injection Molding
Uses	Automotive Applications
	Automotive Electronics
	Automotive Under the Hood
	General Purpose
	Housings
	Industrial Applications
	Industrial Parts
	Lawn and Garden Equipment
	Machine/Mechanical Parts
	Metal Replacement
	Power/Other Tools
	Valves/Valve Parts