Solvay Specialty Polymers Amodel® A-1933 HSL Polyphthalamide (PPA)  (Unverified Data**)

Category Polymer , Thermoplastic , Polyphthalamide (PPA) , Polyphthalamide (PPA), 30% Glass Fiber Reinforced
Manufacturer
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Solvay Specialty Polymers Amodel® A-1933 HSL Polyphthalamide (PPA)  (Unverified Data**).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Amodel A-1933 HSL is a 33% glass reinforced grade of polyphthalamide (PPA) resin. This grade was developed specifically for improved performance in a 50/50 ethylene glycol and water environment. This material was tested using the aggressive automotive coolant system, ethylene glycol with organic acid stabilizer, at 130°C (266°F). It exceeds the performance required by the automotive industry for polymeric materials exposed to high-temperature antifreeze solutions. Potential applications include a variety of automotive components such as thermostat housings, heater core endcaps, heater hose connectors, and water inlets, outlets, and valves. - Black: A-1933 HSL BK 328Information provided by Solvay Specialty Polymers.
Physical Properties Metric English Comments
Density 1.49 g/cc
0.0538 lb/in³
ISO 1183/A
Filler Content 33 %
33 %
Glass Fiber Reinforcement
Linear Mold Shrinkage, Flow 0.0020 cm/cm
0.0020 in/in
Type D2; ASTM D955
0.020 cm/cm
0.020 in/in
ISO 294-4
Linear Mold Shrinkage, Transverse 0.010 cm/cm
0.010 in/in
Type D2; ASTM D955
0.010 cm/cm
0.010 in/in
ISO 294-4
Mechanical Properties Metric English Comments
Tensile Strength, Yield 195 MPa
28300 psi
ISO 527-2
Elongation at Break 1.8 %
1.8 %
ISO 527-2
Tensile Modulus 11.5 GPa
1670 ksi
ISO 527-2
Flexural Strength 280 MPa
40600 psi
ISO 178
Flexural Modulus 10.3 GPa
1490 ksi
ISO 178
Izod Impact, Notched (ISO) 8.10 kJ/m²
3.85 ft-lb/in²
ISO 180/1A
Charpy Impact, Notched 0.820 J/cm²
3.90 ft-lb/in²
ISO 179/1eA
Thermal Properties Metric English Comments
Melting Point 323 °C
613 °F
ISO 11357-3
Deflection Temperature at 1.8 MPa (264 psi) 295 °C
563 °F
Unannealed; ISO 75-2/A
Processing Properties Metric English Comments
Rear Barrel Temperature 313 - 330 °C
595 - 626 °F
Front Barrel Temperature 326 - 339 °C
619 - 642 °F
Melt Temperature 331 - 352 °C
628 - 666 °F
Mold Temperature 150 °C
302 °F
Drying Temperature 120 °C
248 °F
Dry Time 4.00 hour
4.00 hour
Moisture Content 0.045 %
0.045 %
Descriptive Properties Value Comments
Additive Heat Stabilizer
Lubricant
Mold Release
Appearance Black
Automotive Specifications ASTM D6779 PA131G35
CHRYSLER MS-DB478 CPN4771 Color: BK-328 Black
ISO 1874-PA6T/6I, MH, 11-120, GF33 Color: BK-328, NT-07 Black & Natural
Availability Africa & Middle East
Asia Pacific
Europe
North America
South America
Features Antifreeze Resistant
Glycol Resistant
Good Chemical Resistance
Good Creep Resistance
Good Dimensional Stability
Good Stiffness
High Heat Resistance
High Strength
Lubricated
Forms Pellets
Generic PPA
Processing Method Injection Molding
Retention of Flexural Modulus (%) 76
130°C, 1000 hr, in Glycol
Retention of Flexural Strength (%) 71
130°C, 1000 hr, in Glycol
Retention of Tensile Modulus (%) 75
130°C, 1000 hr, in Glycol
Retention of Tensile Strength (%) 69
130°C, 1000 hr, in Glycol
RoHS Compliance RoHS Compliant
Uses Automotive Applications
Automotive Under the Hood
Housings
Valves/Valve Parts