SABIC Innovative Plastics NORYL GTX GTX810 PPE+PS+PA
| Category | Polymer , Thermoplastic , Nylon , Polyphenylene Ether/PPO , Polystyrene (PS) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | NORYL GTX |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics NORYL GTX GTX810 PPE+PS+PA.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
10% Glass Reinforced PPE+PA Alloy.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.16 g/cc | 1.16 g/cc | ASTM D792 |
| Density | 1.162 g/cc | 0.04198 lb/in³ | ASTM D792 |
| Moisture Absorption | 0.500 % | 0.500 % | 50% RH, 24 hrs; ASTM D570 |
| Moisture Absorption at Equilibrium | 1.0 % | 1.0 % | 50% RH; ASTM D570 |
| Linear Mold Shrinkage, Flow | 0.0060 - 0.0080 cm/cm @Thickness 3.20 mm |
0.0060 - 0.0080 in/in @Thickness 0.126 in |
SABIC Method |
| Linear Mold Shrinkage, Transverse | 0.0065 - 0.0085 cm/cm @Thickness 3.20 mm |
0.0065 - 0.0085 in/in @Thickness 0.126 in |
SABIC Method |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 119 | 119 | ASTM D785 |
| Tensile Strength at Break | 88.0 MPa | 12800 psi | Nominal Stress, brk, Type I, 5 mm/min; ASTM D638 |
| Tensile Strength, Yield | 89.0 MPa | 12900 psi | Nominal Stress, yld, Type I, 5 mm/min; ASTM D638 |
| Elongation at Break | 10 % | 10 % | Nominal Strain, 5 mm/min; ASTM D638 |
| Flexural Yield Strength | 155 MPa | 22500 psi | 2.6 mm/min, 100 mm span; ASTM D790 |
| Flexural Modulus | 3.96 GPa | 574 ksi | 2.6 mm/min, 100 mm span; ASTM D790 |
| Izod Impact, Notched | 0.800 J/cm | 1.50 ft-lb/in | ASTM D256 |
| 0.530 J/cm @Temperature -30.0 °C |
0.993 ft-lb/in @Temperature -22.0 °F |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 39.6 - 50.4 µm/m-°C @Temperature -20.0 - 150 °C |
22.0 - 28.0 µin/in-°F @Temperature -4.00 - 302 °F |
ASTM E 831 |
| Deflection Temperature at 0.46 MPa (66 psi) | 245 °C @Thickness 6.40 mm |
473 °F @Thickness 0.252 in |
unannealed; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 210 °C @Thickness 6.40 mm |
410 °F @Thickness 0.252 in |
unannealed; ASTM D648 |
| Vicat Softening Point | 240 °C | 464 °F | Rate B/50; ASTM D1525 |
| UL RTI, Electrical | 50.0 °C | 122 °F | UL 746B |
| UL RTI, Mechanical with Impact | 50.0 °C | 122 °F | UL 746B |
| UL RTI, Mechanical without Impact | 50.0 °C | 122 °F | UL 746B |
| Flammability, UL94 | HB @Thickness 1.47 mm |
HB @Thickness 0.0579 in |
UL 94 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Arc Resistance | 60 - 120 sec | 60 - 120 sec | Tungsten; ASTM D495 |
| Comparative Tracking Index | 175 - 250 V | 175 - 250 V | UL 746A |
| Hot Wire Ignition, HWI | >= 120 sec | >= 120 sec | UL 746A |
| High Amp Arc Ignition, HAI | >= 120 arcs | >= 120 arcs | UL 746A |
| High Voltage Arc-Tracking Rate, HVTR | 80.0 - 150 mm/min | 3.15 - 5.91 in/min | UL 746A |
Users viewing this material also viewed the following:
- Nye Lubricants 200A (SO) Synthetic Oil
- Parker Chomerics CHO-FOIL CCD Shielding Tape
- Polymer Resources PC-HM-FR1 Polycarbonate, 10% Glass Reinforced, Flame Retardant
- Polyram Bondyram® TL1308 Maleic Anhydride Modified Polypropylene
- Polyram PlusTek RB301G6 Nylon 6 for Injection Molding, 30% Glass-fiber Reinforced, Industrial Grade
- Total PPC 3060 MW5 Polypropylene, Heterophasic Copolymer, Automotive
- ChevronTexaco TDH® Oil
- Applied Composites 185 Polyester SMC
- ATI Wah Chang 425™ Titanium Alloy, Cold Rolled Sheet
- Axiall 4900 Flexible PVC
Copyright © lookpolymers.com All Rights Reserved