SABIC Innovative Plastics NORYL FE8000S PPE+PS (Europe-Africa-Middle East)

Category Polymer , Thermoplastic , Polyphenylene Ether/PPO , Polystyrene (PS)
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name Noryl
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics NORYL FE8000S PPE+PS (Europe-Africa-Middle East).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Noryl* FE8000S resin is an unfilled modified polyphenylene ether resin designed for fluid handling applications. This resin is suitable for multiple conversion routes and will be available in custom colors.
Physical Properties Metric English Comments
Specific Gravity 1.08 g/cc
1.08 g/cc
ASTM D792
Density 1.08 g/cc
0.0390 lb/in³
ISO 1183
Moisture Absorption 0.0600 %
0.0600 %
23°C / 50% RH; ISO 62
Water Absorption at Saturation 0.23 %
0.23 %
ISO 62
Linear Mold Shrinkage, Flow 0.0060 - 0.0080 cm/cm

@Thickness 3.20 mm
0.0060 - 0.0080 in/in

@Thickness 0.126 in
SABIC Method
Melt Flow 6.0 g/10 min

@Load 5.00 kg,
Temperature 300 °C
6.0 g/10 min

@Load 11.0 lb,
Temperature 572 °F
ASTM D1238
Melt Index of Compound 10 g/10 min

@Load 10.0 kg,
Temperature 300 °C
10 g/10 min

@Load 22.0 lb,
Temperature 572 °F
MVR [cm^3/10 min]; ISO 1133
Mechanical Properties Metric English Comments
Tensile Strength at Break 56.0 MPa
8120 psi
Type I, 50 mm/min; ASTM D638
56.0 MPa
8120 psi
50 mm/min; ISO 527
Tensile Strength, Yield 73.0 MPa
10600 psi
50 mm/min; ISO 527
75.0 MPa
10900 psi
Type I, 50 mm/min; ASTM D638
Elongation at Break 11 %
11 %
Type I, 50 mm/min; ASTM D638
11 %
11 %
50 mm/min; ISO 527
Elongation at Yield 6.0 %
6.0 %
Type I, 50 mm/min; ASTM D638
6.0 %
6.0 %
50 mm/min; ISO 527
Tensile Modulus 2.45 GPa
355 ksi
1 mm/min; ISO 527
2.50 GPa
363 ksi
5 mm/min; ASTM D638
Flexural Yield Strength 102 MPa
14800 psi
1.3 mm/min, 50 mm span; ASTM D790
107 MPa
15500 psi
2 mm/min; ISO 178
Flexural Modulus 2.56 GPa
371 ksi
2 mm/min; ISO 178
2.60 GPa
377 ksi
1.3 mm/min, 50 mm span; ASTM D790
Izod Impact, Notched 2.90 J/cm
5.43 ft-lb/in
ASTM D256
2.40 J/cm

@Temperature -30.0 °C
4.50 ft-lb/in

@Temperature -22.0 °F
ASTM D256
Izod Impact, Notched (ISO) 23.0 kJ/m²
10.9 ft-lb/in²
80*10*4; ISO 180/1A
13.0 kJ/m²

@Temperature -30.0 °C
6.19 ft-lb/in²

@Temperature -22.0 °F
80*10*4; ISO 180/1A
Charpy Impact, Notched 2.20 J/cm²
10.5 ft-lb/in²
Edgew 80*10*4 sp=62mm; ISO 179/1eA
1.30 J/cm²

@Temperature -30.0 °C
6.19 ft-lb/in²

@Temperature -22.0 °F
Edgew 80*10*4 sp=62mm; ISO 179/1eA
Dart Drop, Total Energy 50.0 J

@Temperature 23.0 °C
36.9 ft-lb

@Temperature 73.4 °F
ASTM D3763
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 87.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
48.3 µin/in-°F

@Temperature -40.0 - 104 °F
ASTM E 831
87.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
48.3 µin/in-°F

@Temperature -40.0 - 104 °F
ISO 11359-2
CTE, linear, Transverse to Flow 93.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
51.7 µin/in-°F

@Temperature -40.0 - 104 °F
ASTM E 831
93.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
51.7 µin/in-°F

@Temperature -40.0 - 104 °F
ISO 11359-2
Deflection Temperature at 0.46 MPa (66 psi) 165 °C
329 °F
Flatw 80*10*4 sp=64mm; ISO 75/Bf
163 °C

@Thickness 3.20 mm
325 °F

@Thickness 0.126 in
unannealed; ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 151 °C
304 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af
149 °C

@Thickness 3.20 mm
300 °F

@Thickness 0.126 in
unannealed; ASTM D648
Vicat Softening Point 167 °C
333 °F
Rate B/50; ASTM D1525
168 °C
334 °F
Rate B/50; ISO 306
172 °C
342 °F
Rate B/120; ISO 306