Ineos Styrenics Avantra® 525K High Impact Styrenic Polymer (NAFTA)
| Category | Polymer , Thermoplastic , Polystyrene (PS) , Polystyrene, Impact Modified |
| Manufacturer | Ineos Styrenics |
| Trade Name | Avantra® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Ineos Styrenics Avantra® 525K High Impact Styrenic Polymer (NAFTA).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Description: Specialty and super-high impact grades for a variety of applications such as refrigerator liners, consumer electronics housings, recreation equipment and sporting goods, toys, office products, cosmetics and personal care products, building and construction, housewares, and furniture and furnishings.Information provided by BASF.Ineos Styrenics purchased this product line from BASF in 2005.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.04 g/cc | 0.0376 lb/in³ | ASTM D792 |
| Moisture Absorption at Equilibrium | <= 0.10 % | <= 0.10 % | 23°C/50% RH |
| Water Absorption at Saturation | <= 0.10 % | <= 0.10 % | |
| Linear Mold Shrinkage | 0.0040 - 0.0070 cm/cm | 0.0040 - 0.0070 in/in | ASTM D955 |
| Melt Flow | 3.6 g/10 min @Load 5.00 kg, Temperature 200 °C |
3.6 g/10 min @Load 11.0 lb, Temperature 392 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell L | 55 | 55 | ASTM D785 |
| Tensile Strength at Break | 24.0 MPa | 3480 psi | ASTM D638 |
| Tensile Strength, Yield | 28.0 MPa | 4060 psi | ASTM D638 |
| Elongation at Break | 25 % | 25 % | ASTM D638 |
| Tensile Modulus | 2.206 GPa | 320.0 ksi | ASTM D638 |
| Flexural Modulus | 1.931 GPa | 280.1 ksi | ASTM D790-1 |
| Izod Impact, Notched | 0.587 J/cm | 1.10 ft-lb/in | ASTM D256-A |
| Gardner Impact | 5.65 J @Thickness 3.17 mm, Temperature 23.0 °C |
4.17 ft-lb @Thickness 0.125 in, Temperature 73.4 °F |
ASTM D3029 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 85.0 °C | 185 °F | ASTM D648 |
| Vicat Softening Point | 101 °C | 214 °F | ASTM D1525 |
| Flammability, UL94 | HB @Thickness 1.54 mm |
HB @Thickness 0.0606 in |
HB CSA 0.6, Natural |
| HB @Thickness 1.50 mm |
HB @Thickness 0.0591 in |
HB UL94, All Colors |
| Optical Properties | Metric | English | Comments |
|---|---|---|---|
| Gloss | 95 % | 95 % | 60°; ASTM D523 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 200 - 230 °C | 392 - 446 °F | Extrusion |
Users viewing this material also viewed the following:
- MV Labs EU1000 Eu2(SO4)3·8H2O Europium(III) sulfate octahydrate
- Polycasa Acryl® G 55 Acrylic, Injection Molding Grade
- PolyOne Edgetek® PK-20CF/000 Polyetheretherketone (PEEK), Carbon Fiber Reinforced (discontinued **)
- KB Alloys 50% Copper Aluminum Alloy
- Multibase Multi-Flex® A 3541 Clear TPE Thermoplastic Elastomer
- Universal Wire Works BAg-18 (AMS 4774) Silver Brazing Filler Metal
- Westlake Plastics Tempalux® Film Made from ULTEM® Polyetherimide Resin
- UBE 7034T Nylon 6/12 Monofilament (Drawing Ratio=6, Diameter 2 mm)
- DuPont Teijin Films Melinex® 377 Polyester Film, 92 Gauge
Copyright © lookpolymers.com All Rights Reserved