LG Chemical LUMIPLAS LD590T Light diffusion ABS
| Category | Polymer , Thermoplastic , ABS Polymer |
| Manufacturer | LG Chemical |
| Trade Name | LUMIPLAS |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | LG Chemical LUMIPLAS LD590T Light diffusion ABS.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Description: Extrusion, Light diffusion, High ImpactApplication: (LED) Lamp Cover, Signboard Lighting Decoration of Electronic DeviceCAS No. 9010-94-0Information provided by LG Chemical
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.12 g/cc | 1.12 g/cc | ASTM D792 |
| Maximum Moisture Content | 0.010 | 0.010 | Injection Molding |
| Linear Mold Shrinkage, Flow | 0.0040 - 0.0070 cm/cm @Thickness 3.20 mm |
0.0040 - 0.0070 in/in @Thickness 0.126 in |
ASTM D955 |
| Melt Flow | 8.0 g/10 min @Load 10.0 kg, Temperature 220 °C |
8.0 g/10 min @Load 22.0 lb, Temperature 428 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 108 | 108 | ASTM D785 |
| Tensile Strength, Yield | 49.0 MPa @Thickness 3.20 mm |
7110 psi @Thickness 0.126 in |
50mm/min; ASTM D638 |
| Elongation at Break | 30 % @Thickness 3.20 mm |
30 % @Thickness 0.126 in |
50mm/min; ASTM D638 |
| Flexural Yield Strength | 78.5 MPa @Thickness 3.20 mm |
11400 psi @Thickness 0.126 in |
15mm/min; ASTM D790 |
| Flexural Modulus | 2.45 GPa @Thickness 3.20 mm |
356 ksi @Thickness 0.126 in |
15mm/min; ASTM D790 |
| Izod Impact, Notched | 0.981 J/cm @Thickness 6.40 mm, Temperature 23.0 °C |
1.84 ft-lb/in @Thickness 0.252 in, Temperature 73.4 °F |
ASTM D256 |
| 1.08 J/cm @Thickness 3.20 mm, Temperature 23.0 °C |
2.02 ft-lb/in @Thickness 0.126 in, Temperature 73.4 °F |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 8.40 µm/m-°C | 4.67 µin/in-°F | ASTM D696 |
| Deflection Temperature at 1.8 MPa (264 psi) | 81.0 °C @Thickness 6.40 mm |
178 °F @Thickness 0.252 in |
Unannealed; ASTM D648 |
| UL RTI, Electrical | 50.0 °C | 122 °F | |
| UL RTI, Mechanical with Impact | 50.0 °C | 122 °F | |
| UL RTI, Mechanical without Impact | 50.0 °C | 122 °F |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 190 - 210 °C | 374 - 410 °F | Injection Molding |
| Middle Barrel Temperature | 200 - 220 °C | 392 - 428 °F | Injection Molding |
| Front Barrel Temperature | 220 - 250 °C | 428 - 482 °F | Injection Molding |
| Nozzle Temperature | 230 - 250 °C | 446 - 482 °F | Injection Molding |
| Melt Temperature | 230 - 250 °C | 446 - 482 °F | Injection Molding |
| Mold Temperature | 40.0 - 60.0 °C | 104 - 140 °F | Injection Molding |
| Drying Temperature | 70.0 - 80.0 °C | 158 - 176 °F | Injection Molding |
| Dry Time | 3.00 - 4.00 hour | 3.00 - 4.00 hour | Injection Molding |
| Back Pressure | 0.981 - 1.96 MPa | 142 - 284 psi | Injection Molding |
| Screw Speed | 30 - 60 rpm | 30 - 60 rpm | Injection Molding |
Users viewing this material also viewed the following:
- Mytex Polymers 1391 Polypropylene, Non-filled, Compounded
- SABIC Innovative Plastics Lexan® IR2240 PC (Europe-Africa-Middle East)
- Eastman 9921P PET Film (discontinued **)
- Nabaltec APYRAL® 8 Al(OH)3
- Ineos H12E-00 Polypropylene Homopolymer, Antistatic
- SABIC Innovative Plastics LNP Lubricomp KX99792 Acetal Copolymer
- Teknor Apex Monprene® MP-1277B Thermoplastic Elastomer
- Dow LDPE 135A Low Density Polyethylene, Blown Film Grade
- Eastman Tenite Propionate 358A4000008 Clear, Trsp Cellulose Acetate Propionate
Copyright © lookpolymers.com All Rights Reserved