SABIC Innovative Plastics Lexan® LR180R PC (Europe-Africa-Middle East)

Category Polymer , Thermoplastic , Polycarbonate (PC)
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name Lexan®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics Lexan® LR180R PC (Europe-Africa-Middle East).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
LR180R is a medium viscosity,release containing multipurpose polycarbonate industrial gradeThis data was supplied by SABIC-IP for the Europe-Africa-Middle East region.
Physical Properties Metric English Comments
Density 1.20 g/cc
0.0434 lb/in³
ISO 1183
Moisture Absorption at Equilibrium 0.15 %
0.15 %
23°C / 50% RH; ISO 62
Water Absorption at Saturation 0.35 %

@Temperature 23.0 °C
 0.35 %

@Temperature 73.4 °F
 ISO 62
Melt Flow 12 g/10 min

@Load 1.20 kg,
Temperature 300 °C
 12 g/10 min

@Load 2.65 lb,
Temperature 572 °F
 [cm^3/10 min] Melt Volume Rate; ISO 1133
Mechanical Properties Metric English Comments
Tensile Strength at Break 65.0 MPa
9430 psi
50 mm/min; ISO 527
Tensile Strength, Yield 60.0 MPa
8700 psi
50 mm/min; ISO 527
Elongation at Break 100 %
100 %
50 mm/min; ISO 527
Elongation at Yield 6.0 %
6.0 %
50 mm/min; ISO 527
Tensile Modulus 2.30 GPa
334 ksi
1 mm/min; ISO 527
Flexural Yield Strength 90.0 MPa
13100 psi
2 mm/min; ISO 178
Flexural Modulus 2.25 GPa
326 ksi
2 mm/min; ISO 178
Izod Impact, Notched (ISO) 11.0 kJ/m²

@Temperature -30.0 °C
 5.23 ft-lb/in²

@Temperature -22.0 °F
 80*10*3; ISO 180/1A
65.0 kJ/m²

@Temperature 23.0 °C
 30.9 ft-lb/in²

@Temperature 73.4 °F
 80*10*3; ISO 180/1A
Izod Impact, Unnotched (ISO) NB

@Temperature 23.0 °C
 NB

@Temperature 73.4 °F
 80*10*3; ISO 180/1U
NB

@Temperature -30.0 °C
 NB

@Temperature -22.0 °F
 80*10*3; ISO 180/1U
Charpy Impact Unnotched NB

@Temperature 23.0 °C
 NB

@Temperature 73.4 °F
 Edgew 80*10*3 sp=62mm; ISO 179/1eU
NB

@Temperature -30.0 °C
 NB

@Temperature -22.0 °F
 Edgew 80*10*3 sp=62mm; ISO 179/1eU
Charpy Impact, Notched 1.20 J/cm²

@Temperature -30.0 °C
 5.71 ft-lb/in²

@Temperature -22.0 °F
 V-notch Edgew 80*10*3 sp=62mm; ISO 179/1eA
6.50 J/cm²

@Temperature 23.0 °C
 30.9 ft-lb/in²

@Temperature 73.4 °F
 V-notch Edgew 80*10*3 sp=62mm; ISO 179/1eA
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 70.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
 38.9 µin/in-°F

@Temperature -40.0 - 104 °F
 ISO 11359-2
CTE, linear, Transverse to Flow 70.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
 38.9 µin/in-°F

@Temperature -40.0 - 104 °F
 ISO 11359-2
Deflection Temperature at 1.8 MPa (264 psi) 124 °C
255 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af
Vicat Softening Point 141 °C
286 °F
Rate B/50; ISO 306
143 °C
289 °F
Rate B/120; ISO 306
Optical Properties Metric English Comments
Refractive Index 1.586
1.586
ASTM D 542
Haze <= 1.0 %

@Thickness 2.54 mm
 <= 1.0 %

@Thickness 0.100 in
 ASTM D 1003
Transmission, Visible 87 %

@Thickness 2.54 mm
 87 %

@Thickness 0.100 in
 ASTM D 1003