SABIC Innovative Plastics LNP LUBRICOMP EX03647H PEI
| Category | Polymer , Thermoplastic , Polyetherimide (PEI) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP LUBRICOMP |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP LUBRICOMP EX03647H PEI.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP LUBRICOMP* EX03647H is a compound based on Polyetherimide resin containing Proprietary Fillers. Added features of this material include: Healthcare, Wear Resistant.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.40 g/cc | 1.40 g/cc | ASTM D792 |
| Density | 1.39 g/cc | 0.0502 lb/in³ | ASTM D792 |
| Moisture Absorption | 0.170 % | 0.170 % | 50% RH, 24 hrs; ASTM D570 |
| 0.250 % | 0.250 % | 23°C / 50% RH; ISO 62 | |
| Linear Mold Shrinkage, Flow | 0.0010 - 0.0030 cm/cm @Time 86400 sec |
0.0010 - 0.0030 in/in @Time 24.0 hour |
ASTM D955 |
| Linear Mold Shrinkage, Transverse | 0.0030 - 0.0050 cm/cm @Time 86400 sec |
0.0030 - 0.0050 in/in @Time 24.0 hour |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 200 MPa | 29000 psi | 5 mm/min; ISO 527 |
| 208 MPa | 30200 psi | Type I, 5 mm/min; ASTM D638 | |
| Elongation at Break | 1.4 % | 1.4 % | 5 mm/min; ISO 527 |
| 1.5 % | 1.5 % | Type I, 5 mm/min; ASTM D638 | |
| Tensile Modulus | 18.3 GPa | 2650 ksi | 1 mm/min; ISO 527 |
| 19.14 GPa | 2776 ksi | 5 mm/min; ASTM D638 | |
| Flexural Strength | 284 MPa | 41200 psi | ISO 178 |
| 301 MPa | 43700 psi | 1.3 mm/min, 50 mm span; ASTM D790 | |
| Flexural Modulus | 16.94 GPa | 2457 ksi | 2 mm/min; ISO 178 |
| 17.5 GPa | 2540 ksi | 1.3 mm/min, 50 mm span; ASTM D790 | |
| Izod Impact, Notched | 0.490 J/cm | 0.918 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 3.93 J/cm | 7.36 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 6.00 kJ/m² | 2.86 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 29.0 kJ/m² | 13.8 ft-lb/in² | 80*10*4; ISO 180/1U |
| Dart Drop, Total Energy | 8.00 J @Temperature 23.0 °C |
5.90 ft-lb @Temperature 73.4 °F |
ASTM D3763 |
| Impact Test | 2.00 J | 1.48 ft-lb | Multiaxial Impact; ISO 6603 |
| Coefficient of Friction, Dynamic | 0.31 | 0.31 | ASTM D3702 Modified |
| Coefficient of Friction, Static | 0.29 | 0.29 | ASTM D3702 Modified |
| K (wear) Factor | 26.2 x 10-8 mm³/N-M | 13.0 x 10-10 in³-min/ft-lb-hr | Washer; ASTM D3702 Modified |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 8.00 µm/m-°C @Temperature -30.0 - 30.0 °C |
4.44 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D696 |
| CTE, linear, Transverse to Flow | 29.0 µm/m-°C @Temperature -30.0 - 30.0 °C |
16.1 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D696 |
| Deflection Temperature at 0.46 MPa (66 psi) | 213 °C | 415 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| 213 °C @Thickness 3.20 mm |
415 °F @Thickness 0.126 in |
unannealed; ASTM D648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 209 °C | 408 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 209 °C @Thickness 3.20 mm |
408 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
Users viewing this material also viewed the following:
- ExxonMobil Exceed™ 1023DA Tough Premium Film Resin (discontinued **)
- Karina KAPU 8035/1-Y Ivory PVC Compound
- SABIC Innovative Plastics LNP LUBRICOMP Lexan_WR5210R PC (Europe-Africa-Middle East)
- A. Schulman POLYBATCH™ White LL8000 AP Concentrate Based In LLDPE
- Elektro-Isola G-Etronax B Phenolic, Glass Fabric Reinforcement, Dark Brown, Tubes
- COI Ceramics Nicalon™ CG SiCO Ceramic Fiber
- C.O.I.M. LARIPUR® LPR6325 Special Adipate Ester Polyurethane
- Toyobo T-751 Nylon, Painting Grade
Copyright © lookpolymers.com All Rights Reserved