DuPont Performance Polymers Crastin® HR5330HFS BK591 Polybutylene Terephthalate (PBT)  (Unverified Data**)

Category Polymer , Thermoplastic , Polyester, TP , Polybutylene Terephthalate (PBT) , Polybutylene Terephthalate (PBT), 30% Glass Fiber Filled
Manufacturer DuPont Performance Polymers
Trade Name Crastin®
Port Ningbo port,China
Trade Terms EXW, FOB, CFR, CIF
Payment Terms L/C, T/T, PayPal
Download PDF DuPont Performance Polymers Crastin® HR5330HFS BK591 Polybutylene Terephthalate (PBT)  (Unverified Data**).pdf
Price EMAIL US    sales@lookpolymers.com
Material Notes:
30% Glass Reinforced Hydrolysis Resistant Polybutylene Terephthalate Crastin HR5330HFS is a 30% glass fiber reinforced moderately toughened hydrolysis resistant polybutylene terephthalate for injection molding.Information provided by DuPont Performance Polymers
Physical Properties Metric English Comments
Density 1.50 g/cc
0.0542 lb/in³
ISO 1183
Water Absorption 0.35 %
<br>@Thickness 2.00 mm
 0.35 %
<br>@Thickness 0.0787 in
 Sim. to ISO 62
Moisture Absorption 0.150 %
<br>@Thickness 2.00 mm
 0.150 %
<br>@Thickness 0.0787 in
 Sim. to ISO 62
Viscosity 230000 cP
<br>@Temperature 250 °C
 230000 cP
<br>@Temperature 482 °F
 @ 1000 sec-1; ISO 11443
Linear Mold Shrinkage, Flow 0.0030 cm/cm
0.0030 in/in
ISO 294-4 2577
Linear Mold Shrinkage, Transverse 0.010 cm/cm
0.010 in/in
ISO 294-4 2577
Melt Flow 8.5 g/10 min
<br>@Load 2.16 kg,<br> Temperature 250 °C
 8.5 g/10 min
<br>@Load 4.76 lb,<br> Temperature 482 °F
 cm³/10min; ISO 1133
Mechanical Properties Metric English Comments
Tensile Strength at Break 120 MPa
17400 psi
ISO 527-1/-2
Tensile Stress 8.01 MPa
<br>@Strain 0.240 %,<br> Temperature 150 °C
 1160 psi
<br>@Strain 0.240 %,<br> Temperature 302 °F
 ISO 11403-1 -2
10.04 MPa
<br>@Strain 0.210 %,<br> Temperature 90.0 °C
 1456 psi
<br>@Strain 0.210 %,<br> Temperature 194 °F
 ISO 11403-1 -2
23.3 MPa
<br>@Strain 0.330 %,<br> Temperature 40.0 °C
 3380 psi
<br>@Strain 0.330 %,<br> Temperature 104 °F
 ISO 11403-1 -2
26.61 MPa
<br>@Strain 1.05 %,<br> Temperature 150 °C
 3859 psi
<br>@Strain 1.05 %,<br> Temperature 302 °F
 ISO 11403-1 -2
32.96 MPa
<br>@Strain 0.360 %,<br> Temperature 23.0 °C
 4780 psi
<br>@Strain 0.360 %,<br> Temperature 73.4 °F
 ISO 11403-1 -2
33.14 MPa
<br>@Strain 0.830 %,<br> Temperature 90.0 °C
 4807 psi
<br>@Strain 0.830 %,<br> Temperature 194 °F
 ISO 11403-1 -2
37.33 MPa
<br>@Strain 1.98 %,<br> Temperature 150 °C
 5414 psi
<br>@Strain 1.98 %,<br> Temperature 302 °F
 ISO 11403-1 -2
43.6 MPa
<br>@Strain 2.96 %,<br> Temperature 150 °C
 6320 psi
<br>@Strain 2.96 %,<br> Temperature 302 °F
 ISO 11403-1 -2
43.81 MPa
<br>@Strain 0.440 %,<br> Temperature 0.000 °C
 6354 psi
<br>@Strain 0.440 %,<br> Temperature 32.0 °F
 ISO 11403-1 -2
49.22 MPa
<br>@Strain 1.53 %,<br> Temperature 90.0 °C
 7139 psi
<br>@Strain 1.53 %,<br> Temperature 194 °F
 ISO 11403-1 -2
57.24 MPa
<br>@Strain 0.960 %,<br> Temperature 40.0 °C
 8302 psi
<br>@Strain 0.960 %,<br> Temperature 104 °F
 ISO 11403-1 -2
59.41 MPa
<br>@Strain 2.26 %,<br> Temperature 90.0 °C
 8617 psi
<br>@Strain 2.26 %,<br> Temperature 194 °F
 ISO 11403-1 -2
65.44 MPa
<br>@Strain 0.660 %,<br> Temperature -20.0 °C
 9491 psi
<br>@Strain 0.660 %,<br> Temperature -4.00 °F
 ISO 11403-1 -2
66.81 MPa
<br>@Strain 0.790 %,<br> Temperature 23.0 °C
 9690 psi
<br>@Strain 0.790 %,<br> Temperature 73.4 °F
 ISO 11403-1 -2
74.56 MPa
<br>@Strain 0.790 %,<br> Temperature 0.000 °C
 10810 psi
<br>@Strain 0.790 %,<br> Temperature 32.0 °F
 ISO 11403-1 -2
76.98 MPa
<br>@Strain 1.51 %,<br> Temperature 40.0 °C
 11170 psi
<br>@Strain 1.51 %,<br> Temperature 104 °F
 ISO 11403-1 -2
84.73 MPa
<br>@Strain 0.790 %,<br> Temperature -40.0 °C
 12290 psi
<br>@Strain 0.790 %,<br> Temperature -40.0 °F
 ISO 11403-1 -2
91.45 MPa
<br>@Strain 1.21 %,<br> Temperature 23.0 °C
 13260 psi
<br>@Strain 1.21 %,<br> Temperature 73.4 °F
 ISO 11403-1 -2
91.85 MPa
<br>@Strain 2.14 %,<br> Temperature 40.0 °C
 13320 psi
<br>@Strain 2.14 %,<br> Temperature 104 °F
 ISO 11403-1 -2
103.45 MPa
<br>@Strain 1.19 %,<br> Temperature 0.000 °C
 15004 psi
<br>@Strain 1.19 %,<br> Temperature 32.0 °F
 ISO 11403-1 -2
110.95 MPa
<br>@Strain 1.68 %,<br> Temperature 23.0 °C
 16092 psi
<br>@Strain 1.68 %,<br> Temperature 73.4 °F
 ISO 11403-1 -2
121.04 MPa
<br>@Strain 1.33 %,<br> Temperature -20.0 °C
 17555 psi
<br>@Strain 1.33 %,<br> Temperature -4.00 °F
 ISO 11403-1 -2
122.73 MPa
<br>@Strain 1.21 %,<br> Temperature -40.0 °C
 17801 psi
<br>@Strain 1.21 %,<br> Temperature -40.0 °F
 ISO 11403-1 -2
128.42 MPa
<br>@Strain 1.66 %,<br> Temperature 0.000 °C
 18626 psi
<br>@Strain 1.66 %,<br> Temperature 32.0 °F
 ISO 11403-1 -2
159.43 MPa
<br>@Strain 2.06 %,<br> Temperature -20.0 °C
 23123 psi
<br>@Strain 2.06 %,<br> Temperature -4.00 °F
 ISO 11403-1 -2
168.02 MPa
<br>@Strain 1.85 %,<br> Temperature -40.0 °C
 24369 psi
<br>@Strain 1.85 %,<br> Temperature -40.0 °F
 ISO 11403-1 -2
198.29 MPa
<br>@Strain 2.50 %,<br> Temperature -40.0 °C
 28760 psi
<br>@Strain 2.50 %,<br> Temperature -40.0 °F
 ISO 11403-1 -2
Elongation at Break 3.2 %
3.2 %
ISO 527-1/-2
Tensile Modulus 8.50 GPa
1230 ksi
ISO 527-1/-2
Flexural Strength 182 MPa
26400 psi
ISO 178
Secant Modulus 3.76 GPa
<br>@Strain 2.64 %,<br> Temperature 40.0 °C
 545 ksi
<br>@Strain 2.64 %,<br> Temperature 104 °F
 ISO 11403-1 -2
4.83 GPa
<br>@Strain 1.71 %,<br> Temperature 40.0 °C
 701 ksi
<br>@Strain 1.71 %,<br> Temperature 104 °F
 ISO 11403-1 -2
5.91 GPa
<br>@Strain 2.05 %,<br> Temperature 23.0 °C
 857 ksi
<br>@Strain 2.05 %,<br> Temperature 73.4 °F
 ISO 11403-1 -2
5.9625 GPa
<br>@Strain 0.960 %,<br> Temperature 40.0 °C
 864.80 ksi
<br>@Strain 0.960 %,<br> Temperature 104 °F
 ISO 11403-1 -2
6.98 GPa
<br>@Strain 2.05 %,<br> Temperature 0.000 °C
 1010 ksi
<br>@Strain 2.05 %,<br> Temperature 32.0 °F
 ISO 11403-1 -2
7.06 GPa
<br>@Strain 0.330 %,<br> Temperature 40.0 °C
 1020 ksi
<br>@Strain 0.330 %,<br> Temperature 104 °F
 ISO 11403-1 -2
7.25 GPa
<br>@Strain 1.36 %,<br> Temperature 23.0 °C
 1050 ksi
<br>@Strain 1.36 %,<br> Temperature 73.4 °F
 ISO 11403-1 -2
7.33 GPa
<br>@Strain 2.30 %,<br> Temperature -20.0 °C
 1060 ksi
<br>@Strain 2.30 %,<br> Temperature -4.00 °F
 ISO 11403-1 -2
8.40 GPa
<br>@Strain 1.34 %,<br> Temperature 0.000 °C
 1220 ksi
<br>@Strain 1.34 %,<br> Temperature 32.0 °F
 ISO 11403-1 -2
8.46 GPa
<br>@Strain 0.790 %,<br> Temperature 23.0 °C
 1230 ksi
<br>@Strain 0.790 %,<br> Temperature 73.4 °F
 ISO 11403-1 -2
8.68 GPa
<br>@Strain 2.06 %,<br> Temperature -40.0 °C
 1260 ksi
<br>@Strain 2.06 %,<br> Temperature -40.0 °F
 ISO 11403-1 -2
9.10 GPa
<br>@Strain 1.33 %,<br> Temperature -20.0 °C
 1320 ksi
<br>@Strain 1.33 %,<br> Temperature -4.00 °F
 ISO 11403-1 -2
9.16 GPa
<br>@Strain 0.360 %,<br> Temperature 23.0 °C
 1330 ksi
<br>@Strain 0.360 %,<br> Temperature 73.4 °F
 ISO 11403-1 -2
9.44 GPa
<br>@Strain 0.790 %,<br> Temperature 0.000 °C
 1370 ksi
<br>@Strain 0.790 %,<br> Temperature 32.0 °F
 ISO 11403-1 -2
9.92 GPa
<br>@Strain 0.660 %,<br> Temperature -20.0 °C
 1440 ksi
<br>@Strain 0.660 %,<br> Temperature -4.00 °F
 ISO 11403-1 -2
9.96 GPa
<br>@Strain 0.440 %,<br> Temperature 0.000 °C
 1440 ksi
<br>@Strain 0.440 %,<br> Temperature 32.0 °F
 ISO 11403-1 -2
10.143 GPa
<br>@Strain 1.21 %,<br> Temperature -40.0 °C
 1471.1 ksi
<br>@Strain 1.21 %,<br> Temperature -40.0 °F
 ISO 11403-1 -2
10.7 GPa
<br>@Strain 0.790 %,<br> Temperature -40.0 °C
 1560 ksi
<br>@Strain 0.790 %,<br> Temperature -40.0 °F
 ISO 11403-1 -2
Charpy Impact Unnotched 6.50 J/cm²
30.9 ft-lb/in²
ISO 179/1eU
Charpy Impact, Notched 1.20 J/cm²
5.71 ft-lb/in²
ISO 179/1eA
0.950 J/cm²
<br>@Temperature -30.0 °C
 4.52 ft-lb/in²
<br>@Temperature -22.0 °F
 ISO 179/1eA
Thermal Properties Metric English Comments
Melting Point 225 °C
437 °F
10°C/min; ISO 11357-1/-3
Deflection Temperature at 1.8 MPa (264 psi) 207 °C
405 °F
ISO 75-1/-2
Electrical Properties Metric English Comments
Volume Resistivity >= 1.00e+15 ohm-cm
>= 1.00e+15 ohm-cm
IEC 60093
Surface Resistance >= 1.00e+15 ohm
>= 1.00e+15 ohm
IEC 60093
Dielectric Strength 34.0 kV/mm
864 kV/in
IEC 60243-1
Comparative Tracking Index 525 V
525 V
IEC 60112