SABIC Innovative Plastics Lexan® HF1140 PC (Europe-Africa-Middle East)

Category Polymer , Thermoplastic , Polycarbonate (PC)
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name Lexan®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics Lexan® HF1140 PC (Europe-Africa-Middle East).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Ideal for disposables/short life cycles. Good clarity, heat resistance, property retention and dimensional stability. FDA food contact compliant in limited colors.Effective January 15th, 2007 this grade will no longer be supported with biocompatibility information and should not be used for medical applications which require biocompatibility. Alternative grade HP1NREU.
Physical Properties Metric English Comments
Specific Gravity 1.20 g/cc
1.20 g/cc
ASTM D792
Density 1.20 g/cc
0.0434 lb/in³
ISO 1183
Moisture Absorption 0.150 %
0.150 %
23°C / 50% RH; ISO 62
Water Absorption at Saturation 0.35 %
0.35 %
ISO 62
Linear Mold Shrinkage, Flow 0.0050 - 0.0070 cm/cm
0.0050 - 0.0070 in/in
on Tensile Bar; SABIC Method
Melt Index of Compound 26 g/10 min

@Load 1.20 kg,
Temperature 300 °C
26 g/10 min

@Load 2.65 lb,
Temperature 572 °F
MVR [cm^3/10 min]; ISO 1133
Mechanical Properties Metric English Comments
Hardness, H358/30 95.0 MPa
13800 psi
ISO 2039-1
Tensile Strength at Break 50.0 MPa
7250 psi
50 mm/min; ISO 527
Tensile Strength, Yield 63.0 MPa
9140 psi
50 mm/min; ISO 527
Elongation at Break 70 %
70 %
50 mm/min; ISO 527
Elongation at Yield 6.0 %
6.0 %
50 mm/min; ISO 527
Tensile Modulus 2.35 GPa
341 ksi
1 mm/min; ISO 527
Flexural Yield Strength 90.0 MPa
13100 psi
2 mm/min; ISO 178
Flexural Modulus 2.30 GPa
334 ksi
2 mm/min; ISO 178
Izod Impact, Notched 6.40 J/cm
12.0 ft-lb/in
ASTM D256
Izod Impact, Notched (ISO) 60.0 kJ/m²
28.6 ft-lb/in²
80*10*3; ISO 180/1A
11.0 kJ/m²

@Temperature -30.0 °C
5.23 ft-lb/in²

@Temperature -22.0 °F
80*10*3; ISO 180/1A
Izod Impact, Unnotched (ISO) NB
NB
80*10*3; ISO 180/1U
NB

@Temperature -30.0 °C
NB

@Temperature -22.0 °F
80*10*3; ISO 180/1U
Charpy Impact Unnotched NB
NB
Edgew 80*10*3 sp=62mm; ISO 179/1eU
NB

@Temperature -30.0 °C
NB

@Temperature -22.0 °F
Edgew 80*10*3 sp=62mm; ISO 179/1eU
Charpy Impact, Notched 6.00 J/cm²
28.6 ft-lb/in²
Edgew 80*10*3 sp=62mm; ISO 179/1eA
1.20 J/cm²

@Temperature -30.0 °C
5.71 ft-lb/in²

@Temperature -22.0 °F
Edgew 80*10*3 sp=62mm; ISO 179/1eA
Tensile Impact Strength 378 kJ/m²
180 ft-lb/in²
Type S; ASTM D1822
Taber Abrasion, mg/1000 Cycles 10
10
CS-17, 1 kg; SABIC Method
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 70.0 µm/m-°C

@Temperature 23.0 - 80.0 °C
38.9 µin/in-°F

@Temperature 73.4 - 176 °F
ISO 11359-2
Thermal Conductivity 0.200 W/m-K
1.39 BTU-in/hr-ft²-°F
ISO 8302
Deflection Temperature at 0.46 MPa (66 psi) 133 °C
271 °F
Edgew 120*10*4 sp=100mm; ISO 75/Be
Deflection Temperature at 1.8 MPa (264 psi) 121 °C
250 °F
Edgew 120*10*4 sp=100mm; ISO 75/Ae
Vicat Softening Point 139 °C
282 °F
Rate B/50; ISO 306
140 °C
284 °F
Rate B/120; ISO 306
Oxygen Index 25 %
25 %
ISO 4589
Glow Wire Test 850 °C

@Thickness 1.00 mm
1560 °F

@Thickness 0.0394 in
IEC 60695-2-12
Electrical Properties Metric English Comments
Volume Resistivity >= 1.00e+15 ohm-cm
>= 1.00e+15 ohm-cm
IEC 60093
Surface Resistance >= 1.00e+15 ohm
>= 1.00e+15 ohm
ROA; IEC 60093
Dielectric Constant 2.7

@Frequency 50.0 - 60.0 Hz
2.7

@Frequency 50.0 - 60.0 Hz
IEC 60250
2.7

@Frequency 1.00e+6 Hz
2.7

@Frequency 1.00e+6 Hz
IEC 60250
Dielectric Strength 17.0 kV/mm

@Thickness 3.20 mm
432 kV/in

@Thickness 0.126 in
in oil; IEC 60243-1
Dissipation Factor 0.0010

@Frequency 50.0 - 60.0 Hz
0.0010

@Frequency 50.0 - 60.0 Hz
IEC 60250
0.010

@Frequency 1.00e+6 Hz
0.010

@Frequency 1.00e+6 Hz
IEC 60250
Descriptive Properties Value Comments
Ball Pressure Test, 125°C +/- 2°C PASSES
IEC 60695-10-2