3M Scotch-Weld™ TE031 Black Polyurethane Reactive Adhesive

Category	Polymer , Adhesive
Manufacturer	3M
Trade Name	Scotch-Weld™
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	3M Scotch-Weld™ TE031 Black Polyurethane Reactive Adhesive.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

3M™ Scotch-Weld™ Polyurethane Reactive Adhesives are a family of one-component, moisture curing, urethane adhesives. These adhesives are applied warm and bond a wide variety of substrates such as wood, fiber reinforced plastic (FRP) and many other plastics to themselves, to metal and glass. Extrudable grade adhesive with fast set time ideal for bonding a wide variety of plastics including polystyrene and polyacrylic.Information provided by 3M

Physical Properties	Metric	English	Comments
Density	>= 1.04 g/cc	>= 0.0376 lb/in³
Brookfield Viscosity	14000 cP	14000 cP	Thermosel using spindle #27

Mechanical Properties	Metric	English	Comments
Hardness, Shore D	48	48
Tensile Strength at Break	24.8 MPa	3600 psi	ASTM D638 Die C
Elongation at Break	750 %	750 %	ASTM D638 Die C
Tensile Modulus	0.0248 GPa	3.60 ksi	ASMT D638 Die C
Shear Strength	4.00 MPa @Temperature 23.0 °C	580 psi @Temperature 73.4 °F	Overlap, Polystyrene, Substrate Failure
	4.48 MPa @Temperature 82.0 °C	650 psi @Temperature 180 °F	Overlap, Maple
	5.45 MPa @Temperature 82.0 °C	790 psi @Temperature 180 °F	Overlap, FRP
	8.48 MPa @Temperature 23.0 °C	1230 psi @Temperature 73.4 °F	Overlap, Polyacrylic, Substrate Failure
	9.24 MPa @Temperature 23.0 °C	1340 psi @Temperature 73.4 °F	Overlap, ABS, Substrate Failure
	10.3 MPa @Temperature 23.0 °C	1500 psi @Temperature 73.4 °F	Overlap, Maple
	10.8 MPa @Temperature 23.0 °C	1570 psi @Temperature 73.4 °F	Overlap, Polycarbonate
	12.9 MPa @Temperature 23.0 °C	1870 psi @Temperature 73.4 °F	Overlap, PVC, Substrate Failure
	18.6 MPa @Temperature 23.0 °C	2700 psi @Temperature 73.4 °F	Overlap, FRP
Peel Strength	0.175 kN/m	1.00 pli	180°, Aluminum
	0.526 kN/m	3.00 pli	180°, Glass
	9.99 kN/m	57.0 pli	180°, Polyacrylic
	11.9 kN/m	68.0 pli	180°, Polystyrene
	12.3 kN/m	70.0 pli	180°, ABS
	13.7 kN/m	78.0 pli	180°, FRP, Cotton duck failed during testing
	14.7 kN/m	84.0 pli	180°, PVC, Cotton duck failed during testing
	16.7 kN/m	95.0 pli	180°, Polycarbonate, Cotton duck failed during testing

Thermal Properties	Metric	English	Comments
Maximum Service Temperature, Air	121 °C	250 °F

Processing Properties	Metric	English	Comments
Cure Time	0.500 min	0.00833 hour	Set Time

Descriptive Properties	Value	Comments
Appearance	Black