SABIC Innovative Plastics LNP VERTON RVL28 PA 66

Category Polymer , Thermoplastic , Nylon , Nylon 66
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name LNP VERTON
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics LNP VERTON RVL28 PA 66.pdf
Price EMAIL US    sales@lookpolymers.com
Material Notes:
LNP* VERTON* RVL28 is a compound based on Nylon 66 resin containing 40% Long Glass Fiber, 10% PTFE. Added features of this material include: Easy Molding, Heat Stabilized, Wear Resistant, Structural.
Physical Properties Metric English Comments
Density 1.57 g/cc
0.0567 lb/in³
ISO 1183
1.58 g/cc
0.0571 lb/in³
ASTM D792
Moisture Absorption 0.500 %
0.500 %
50% RH, 24 hrs; ASTM D570
Linear Mold Shrinkage, Flow 0.0020 - 0.0040 cm/cm

@Time 86400 sec
 0.0020 - 0.0040 in/in

@Time 24.0 hour
 ASTM D955
0.0033 cm/cm

@Time 86400 sec
 0.0033 in/in

@Time 24.0 hour
 ISO 294
Linear Mold Shrinkage, Transverse 0.0077 cm/cm

@Time 86400 sec
 0.0077 in/in

@Time 24.0 hour
 ISO 294
0.0070 - 0.0090 cm/cm

@Time 86400 sec
 0.0070 - 0.0090 in/in

@Time 24.0 hour
 ASTM D955
Mechanical Properties Metric English Comments
Tensile Strength at Break 228 MPa
33100 psi
ISO 527
234 MPa
33900 psi
ASTM D638
Tensile Strength, Yield 228 MPa
33100 psi
ISO 527
234 MPa
33900 psi
ASTM D638
Elongation at Break 2.3 %
2.3 %
ASTM D638
2.4 %
2.4 %
ISO 527
Elongation at Yield 2.3 %
2.3 %
ASTM D638
2.4 %
2.4 %
ISO 527
Tensile Modulus 13.23 GPa
1919 ksi
1 mm/min; ISO 527
14.47 GPa
2099 ksi
50 mm/min; ASTM D638
Flexural Strength 337 MPa
48900 psi
ASTM D790
351 MPa
50900 psi
ISO 178
Flexural Modulus 12.41 GPa
1800 ksi
ASTM D790
13.0 GPa
1890 ksi
ISO 178
Izod Impact, Notched 2.56 J/cm
4.80 ft-lb/in
ASTM D256
Izod Impact, Unnotched 14.09 J/cm
26.40 ft-lb/in
ASTM D4812
Izod Impact, Notched (ISO) 23.0 kJ/m²
10.9 ft-lb/in²
80*10*4; ISO 180/1A
Izod Impact, Unnotched (ISO) 93.0 kJ/m²
44.3 ft-lb/in²
80*10*4; ISO 180/1U
Dart Drop, Total Energy 14.0 J
10.3 ft-lb
Instrumented Impact Energy @ peak; ASTM D3763
Impact Test 7.00 J
5.16 ft-lb
Multiaxial Impact; ISO 6603
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 48.6 µm/m-°C

@Temperature -40.0 - 40.0 °C
 27.0 µin/in-°F

@Temperature -40.0 - 104 °F
 ASTM E 831
49.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
 27.2 µin/in-°F

@Temperature -40.0 - 104 °F
 ISO 11359-2
CTE, linear, Transverse to Flow 21.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
 11.7 µin/in-°F

@Temperature -40.0 - 104 °F
 ISO 11359-2
21.6 µm/m-°C

@Temperature -40.0 - 40.0 °C
 12.0 µin/in-°F

@Temperature -40.0 - 104 °F
 ASTM E 831
Deflection Temperature at 0.46 MPa (66 psi) 255 °C
491 °F
Flatw 80*10*4 sp=64mm; ISO 75/Bf
256 °C

@Thickness 3.20 mm
 493 °F

@Thickness 0.126 in
 unannealed; ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 259 °C
498 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af
253 °C

@Thickness 3.20 mm
 487 °F

@Thickness 0.126 in
 unannealed; ASTM D648