- Polyram PlusTek RA320G5 Nylon 66 for Injection Molding, 25% Glass-Fiber Reinforced, Flame Retardant and High Stiffness
Polyram PlusTek RA320G5 Nylon 66 for Injection Molding, 25% Glass-Fiber Reinforced, Flame Retardant and High Stiffness
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, Glass Fiber Filled, Flame Retardant |
| Manufacturer | Polyram |
| Trade Name | PlusTek |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Polyram PlusTek RA320G5 Nylon 66 for Injection Molding, 25% Glass-Fiber Reinforced, Flame Retardant and High Stiffness.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
25% Glass-fiber reinforced, flame retardant and high stiffness Nylon 66 for injection molding applications.Information provided by Polyram.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.35 g/cc | 0.0488 lb/in³ | ISO 1183 |
| Moisture Absorption at Equilibrium | 1.5 % | 1.5 % | 50% RH; ISO 62 |
| Water Absorption at Saturation | 4.5 % | 4.5 % | ISO 62 |
| Linear Mold Shrinkage | 0.0020 - 0.0040 cm/cm | 0.0020 - 0.0040 in/in | ISO 2577 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 120 | 120 | |
| Tensile Strength, Yield | 130 MPa | 18900 psi | ISO 527 |
| Elongation at Break | 2.5 % | 2.5 % | ISO 527 |
| Flexural Strength | 180 MPa | 26100 psi | ISO 178 |
| Flexural Modulus | 6.00 GPa | 870 ksi | ISO 178 |
| Izod Impact, Notched (ISO) | 7.00 kJ/m² | 3.33 ft-lb/in² | ISO 180 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 256 °C | 493 °F | ISO 11357 |
| Deflection Temperature at 0.46 MPa (66 psi) | 240 °C | 464 °F | ISO 75 |
| Deflection Temperature at 1.8 MPa (264 psi) | 230 °C | 446 °F | ISO 75 |
| Flammability, UL94 | V-0 @Thickness 3.00 mm |
V-0 @Thickness 0.118 in |
|
| Glow Wire Test | 960 °C | 1760 °F | GWFI; IEC 60695 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+15 ohm-cm | 1.00e+15 ohm-cm | IEC 60093 |
| Surface Resistance | 1.00e+12 ohm | 1.00e+12 ohm | IEC 60093 |
| Dielectric Constant | 3.8 @Frequency 1.00e+6 Hz |
3.8 @Frequency 1.00e+6 Hz |
IEC 60250 |
Users viewing this material also viewed the following:
- Nylene® PA6 Homopolymer 201 Nylon 6; Low Viscosity Nucleated
- SABIC Innovative Plastics Lexan® CFR7431 PC COPOLYMER (Asia Pacific)
- Industrial Laminates/Norplex NP329 Cotton Fabric
- Kraton® G1654 E (SEBS) Linear Triblock Copolymer
- SABIC Innovative Plastics LNP LUBRICOMP ZI001XXX PPE+PS (Asia Pacific)
- Saint-Gobain CHR® M97 Polyester Film Backing Acrylic Adhesive Pressure Sensitive Tape
- Teknor Apex Monprene® MP-2111 L2 Thermoplastic Elastomer
- ExxonMobil LDPE LD 258 Low Density Polyethylene Resin (European Grade)
- BASF Ultradur B 2300 G6 HR BK15116 30% Glass Filled PBT
- Asahi Kasei Tenac® SH410 Homopolymer Acetal Resin
Copyright © lookpolymers.com All Rights Reserved