- SABIC Innovative Plastics LNP Thermocomp YF004 Polyester Elastomer
SABIC Innovative Plastics LNP Thermocomp YF004 Polyester Elastomer
| Category | Polymer , Thermoplastic , Polyester, TP |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP THERMOCOMP |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP Thermocomp YF004 Polyester Elastomer.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP THERMOCOMP* YF004 is a compound based on Polyester Elastomer resin containing Glass Fiber.This data was supplied by SABIC-IP for the Americas region.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.35 g/cc | 1.35 g/cc | ASTM D 792 |
| Density | 1.35 g/cc | 0.0488 lb/in³ | ASTM D 792 |
| Moisture Absorption at Equilibrium | 0.71 % | 0.71 % | 23°C / 50% RH; ISO 62 |
| 0.71 % @Time 86400 sec |
0.71 % @Time 24.0 hour |
50% RH; ASTM D 570 | |
| Linear Mold Shrinkage, Flow | 0.0020 - 0.0040 cm/cm @Time 86400 sec |
0.0020 - 0.0040 in/in @Time 24.0 hour |
ASTM D 955 |
| Linear Mold Shrinkage, Transverse | 0.0060 - 0.0080 cm/cm @Time 86400 sec |
0.0060 - 0.0080 in/in @Time 24.0 hour |
ASTM D 955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 47.0 MPa | 6820 psi | Type I, 5 mm/min; ASTM D 638 |
| 48.0 MPa | 6960 psi | 5 mm/min; ISO 527 | |
| Elongation at Break | 11.9 % | 11.9 % | Type I, 5 mm/min; ASTM D 638 |
| 12.7 % | 12.7 % | 5 mm/min; ISO 527 | |
| Tensile Modulus | 2.16 GPa | 313 ksi | 1 mm/min; ISO 527 |
| 2.64 GPa | 383 ksi | 50 mm/min; ASTM D 638 | |
| Flexural Strength | 25.0 MPa | 3630 psi | ISO 178 |
| 55.0 MPa | 7980 psi | 1.3 mm/min, 50 mm span; ASTM D 790 | |
| Flexural Modulus | 0.310 GPa | 45.0 ksi | 2 mm/min; ISO 178 |
| 1.92 GPa | 278 ksi | 1.3 mm/min, 50 mm span; ASTM D 790 | |
| Izod Impact, Notched | 4.01 J/cm @Temperature 23.0 °C |
7.51 ft-lb/in @Temperature 73.4 °F |
ASTM D 256 |
| Izod Impact, Unnotched | NB @Temperature 23.0 °C |
NB @Temperature 73.4 °F |
ASTM D 4812 |
| Izod Impact, Notched (ISO) | 37.0 kJ/m² @Temperature 23.0 °C |
17.6 ft-lb/in² @Temperature 73.4 °F |
80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | NB @Temperature 23.0 °C |
NB @Temperature 73.4 °F |
80*10*4; ISO 180/1U |
| Impact Test | 10.0 J | 7.38 ft-lb | Multiaxial Impact; ISO 6603 |
| 14.0 J @Temperature 23.0 °C |
10.3 ft-lb @Temperature 73.4 °F |
Instrumented Impact Total Energy; ASTM D 3763 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 121 µm/m-°C @Temperature -30.0 - 30.0 °C |
67.2 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D 696 |
| CTE, linear, Transverse to Flow | 32.0 µm/m-°C @Temperature -30.0 - 30.0 °C |
17.8 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D 696 |
| Deflection Temperature at 0.46 MPa (66 psi) | 184 °C | 363 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| 186 °C @Thickness 3.20 mm |
367 °F @Thickness 0.126 in |
unannealed; ASTM D 648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 129 °C | 264 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 151 °C @Thickness 3.20 mm |
304 °F @Thickness 0.126 in |
unannealed; ASTM D 648 |
Users viewing this material also viewed the following:
- Polimeri Europa Clearflex® MQ F0 Very Low Density Polyethylene
- Network Polymers Softflex® 1104
- SABIC Innovative Plastics Lexan® LUX7430C PC COPOLYMER (Asia Pacific)
- Ineos N02G-00 Polypropylene Impact Copolymer
- Lord Adhesives 406 Flexible, High Impact and Peel Resistance, Medium Working Time Acrylic Adhesive
- Teknor Apex Monprene® MP 2313 Thermoplastic Elastomer
- Chosun Refractories AM10S Alumina Magnesia Carbon Bricks for Ladle Wall And Bottom
- Advanced Polymer Alloys DuraGrip™ DGR 6030 NC/BK Thermoplastic Elastomer (TPE)
- ALM D80-ST Nylon 11 SLS Prototyping Polymer
Copyright © lookpolymers.com All Rights Reserved